Polypropylene composite material and preparation method thereof, sheet or irregular section prepared thereby and application thereof
A composite material, polypropylene technology, applied in the field of polymer composite materials, can solve the problems of not being able to produce parts containing skin texture, low shrinkage rate, sensitive skin allergies, etc., to reduce mold expansion rate and gloss. , The effect of low shrinkage rate and low mold release expansion rate
Active Publication Date: 2018-11-02
GUANGDONG KINGFA TECH CO LTD
View PDF5 Cites 3 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The material can be used to produce structural parts due to its high strength and low shrinkage, but the glass fiber reinforced material uses the retained length of the glass fiber to play a reinforcing role. Because of the anisotropy of the glass fiber, it cannot be used to
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-9 and comparative example 1-4
[0056] Weigh the components according to the parts by weight shown in Table 1, first mix the polypropylene, skin texture replicating agent, and size regulator in a high mixer for 3 minutes, then add antioxidant and lubricant, and mix for 2 minutes again, the speed The premix is obtained at 2000 rpm; the premix is melted and extruded by a twin-screw extruder, and the temperature of each zone of the screw is maintained at 190-230°C, extruded and granulated to obtain a polypropylene composite material, which is prepared according to the standard The test specimens were tested, and their mechanical properties were determined, and the specific values are listed in Table 3.
[0057] Table 1 Composition and properties of polypropylene composites in Examples and Comparative Examples
[0058]
[0059] Continuation of Table 1:
[0060]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more Abstract
The invention discloses a polypropylene composite material and a preparation method thereof, a sheet or an irregular section prepared thereby and application thereof. The composite material comprises50-80 parts of polypropylene, 5-20 parts of a skin texture copying agent, and 10-30 parts of a size stabilizing agent; the width of half peak of a crystallization peak of the polypropylene is 3-7 DEGC; the peak temperature of the crystallization peak of the polypropylene is 113-120 DEG C; the peak temperature of the crystallization peak of the skin and texture copying agent is 90-100 DEG C. According to the polypropylene composite material, the mold releasing expansion rate and the glossiness of the composite material are reduced, and meanwhile, the material is high in shrinkage rate; the material is low in mold releasing expansion rate, so that injection molding defects such as bright shadow, waveform and white spots in skin and texture copying can be effectively avoided; material support is supplied to nice skin and texture design; the structural design can integrate more aesthetic effects.
Description
technical field [0001] The invention belongs to the technical field of polymer composite materials, and in particular relates to a polypropylene composite material and a preparation method thereof, a sheet or profiled material prepared therefrom and an application thereof. technical background [0002] For automotive interior materials, with the improvement of people's comfort and aesthetic requirements, injection-molded plastic parts are required to have various shades and thicknesses of skin texture, which affects the shrinkage rate, gloss and scratch resistance of the material. Scrubbing puts forward higher requirements. At present, automotive interior materials are mainly PP toughened and filled. The shrinkage of these materials is affected by the type and quantity of matrix resin, toughener and filler, but the overall shrinkage of these materials is above 0.9%. Die expansion ratios are above 1.5. For parts with deep skin texture and fine skin texture, this kind of shr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more IPC IPC(8): C08L23/12C08L23/14C08L23/08C08L23/06C08K3/26C08K5/134C08K5/526
CPCC08L23/12C08L23/14C08L2205/02C08L2205/03C08L2207/10C08L23/0815C08L23/06C08K3/26C08K5/1345C08K5/526
Inventor 汪海胡志华周日敏李诚陈振树刘思杨
Owner GUANGDONG KINGFA TECH CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap