Electric leakage resistant PP material

A technology of resistance to electric leakage and raw materials, applied in the field of PP materials, can solve the problems of high production cost of PBT materials, low resistance to electric leakage and tracking index, affecting market competitiveness, etc., and achieve the effect of strong safety performance, high cost performance and cost reduction.

Inactive Publication Date: 2018-11-13
东莞市百思特塑胶有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tracking index (PTI) value of ordinary flame-retardant PBT is low, while the glow wire ignition temperature is generally 650°C-750°C. The material is used in electronic and ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The anti-leakage PP material provided by the present invention, the anti-leakage PP material is prepared from the following raw material components by weight percentage: PP resin 85%; phosphorus phenol flame retardant 3%; brominated flame retardant 5%; powder filler 2%; toughening agent 4.5%; lubricant 0.5%. During preparation, each component is mixed in a high-speed mixer for 1 to 2 minutes and then put into a twin-screw extruder for molecular decomposition, recombination and granulation to obtain leakage-resistant PP material.

[0017] The present invention adopts PP resin as a carrier, and the scientific name of PP resin is polypropylene, which is a kind of thermoplastic resin prepared by polymerizing propylene. According to the position of the methyl group, it is divided into three types: isotactic polypropylene, atactic polypropylene and syndiotactic polypropylene, and the cost is relatively low. The preferred model of the present invention is 4520 PP resin, impor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of novel materials and particularly relates to an electric leakage resistant PP material. The electric leakage resistant PP material is prepared from the following raw material components in percentage by weight: 60-90% of PP resin, 1-5% of a phosphorus phenol flame retardant, 4-8% of a bromine flame retardant, 1-3% of a powder filler, 2-7% of a flexibilizer and 0.2-1% of a lubricating agent. The preparation method comprises the following steps: adopting the principle condensed phase flame retardance and auxiliary interrupted heat exchange, strictlycontrolling the component of metal components in the materials, taking the PP resin as a carrier, performing molecular decomposition and recombination by a twin-screw extruder, granulating, performing physical test and environmental inspection, and finally obtaining the high-PTI (Proof Tracking Index) low-cost PP material. The product is stable in quality and excellent in safety performance, thePTI value reaches 600V, the cost is greatly reduced relative to PBT (Poly Butylenes Terephthalate), the cost performance is high, and the requirements of the electronics and electric appliance industries on the product safety are met.

Description

technical field [0001] The invention relates to the technical field of new materials, especially PP materials. Background technique [0002] In various electronic and electrical products such as computers, automotive connectors, cooling fans, AC / DC plugs, and transformer frames, modified PBT materials are usually used to make shells. PBT (abbreviation for polybutylene terephthalate), was first developed by German scientist P. Schlack in 1942. Afterwards, the American Celanese company (now Ticona) carried out industrial development and listed it under the trade name of Celanex. In 1970, 30% glass fiber reinforced plastics were put on the market. With the wide application of PBT materials, the performance requirements of PBT materials have also increased, such as flame retardancy, and sufficient tensile strength, bending strength, Impact strength, etc., so it is necessary to add auxiliary materials such as flame retardants and glass fibers during production to modify PBT. Wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/08C08L61/06C08L25/06C08K13/02C08K3/22C08K3/34C08K5/20C08K5/03
CPCC08L23/12C08K2003/2241C08L2201/08C08L2203/20C08L2205/03C08L2205/06C08L2201/02C08L2312/00C08L23/0815C08L61/06C08L25/06C08K13/02C08K3/22C08K3/34C08K5/20C08K3/2279C08K5/03
Inventor 许志鹏
Owner 东莞市百思特塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products