Non-aqueous electrolyte of lithium ion battery and lithium ion battery
A lithium-ion battery, non-aqueous electrolyte technology, applied in the direction of secondary batteries, circuits, electrical components, etc., can solve the problems of high temperature cycle and insufficient storage performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0058] This embodiment is used to illustrate the lithium-ion battery non-aqueous electrolyte, lithium-ion battery and preparation method thereof disclosed in the present invention, comprising the following steps:
[0059] Preparation of non-aqueous electrolyte: Mix ethylene carbonate (EC), diethyl carbonate (DEC) and ethyl methyl carbonate (EMC) in a mass ratio of EC:DEC:EMC=1:1:1, then add Lithium hexafluorophosphate (LiPF 6 ) to a molar concentration of 1 mol / L, and based on the total weight of the non-aqueous electrolytic solution as 100%, add components containing mass percentages shown in Table 1.
[0060] Preparation of the positive plate: mix the positive active material lithium nickel cobalt manganese oxide LiNi according to the mass ratio of 93:4:3 0.5 co 0.2 mn 0.3 o 2 , conductive carbon black Super-P and binder polyvinylidene fluoride (PVDF), and then the mixture was dispersed in N-methyl-2-pyrrolidone (NMP) to obtain positive electrode slurry. The slurry is e...
Embodiment 2~22
[0066] Embodiments 2 to 22 are used to illustrate the lithium ion battery non-aqueous electrolyte, lithium ion battery and preparation method thereof disclosed in the present invention, including most of the operating steps in Example 1, the difference being:
[0067] In the preparation step of described non-aqueous electrolytic solution:
[0068] Based on the total mass of the non-aqueous electrolyte as 100%, the non-aqueous electrolyte is added with the components shown in the mass percentages of Examples 2 to 22 in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com