A high-strength face-centered cubic medium-entropy alloy and its preparation method

A technology of face-centered cubic and entropy alloys, applied in the field of high-strength face-centered cubic entropy alloys and their preparation

Active Publication Date: 2020-03-31
SOUTHEAST UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with high-entropy alloys, medium-entropy alloys are more valuable for production and use. At present, the research on medium-entropy alloys is still in its infancy, and there are few reports on medium-entropy alloys.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength face-centered cubic medium-entropy alloy and its preparation method
  • A high-strength face-centered cubic medium-entropy alloy and its preparation method
  • A high-strength face-centered cubic medium-entropy alloy and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A high-strength face-centered cubic structure medium-entropy alloy, the alloy composition: Co: 30%, Ni: 30%, Cu: 40%, and the preparation method includes the following steps:

[0043] Weigh 5.62 g of Co ingot, 6.29 g of Ni ingot, and 8.08 g of Cu ingot, and put the granular / lumpy raw materials Co, Cu and Ni with a purity of more than 99.99% into proportions.

[0044] 2) Put the ingredients into the vacuum melting furnace and vacuumize to 1×10 -3 Pa, then fill with argon until the pressure in the furnace reaches 0.05MPa, the melting current: 200A, flip and repeat the melting more than 5 times.

[0045] 3) Suction casting the ingot into shape, after cooling, take out the cast rod, put it into the muffle furnace for homogenization annealing treatment, heat up to 1000°C at a rate of 5°C / min, then open the furnace door and quickly put the cast rod Put it into the furnace, wait for the furnace temperature to return to 1000℃, and hold for 1h.

[0046] 3. Put the medium entropy alloy r...

Embodiment 2

[0048] A high-strength face-centered cubic structure medium-entropy alloy, the alloy composition: Co: 32%, Ni: 32%, Cu: 36%, and the preparation method includes the following steps:

[0049] Weigh 5.99 g of Co ingots, 6.72 g of Ni ingots, and 7.27 g of Cu ingots, and add granular / lumpy raw materials Co, Cu, and Ni with a purity of greater than 99.99% into proportions.

[0050] 2) Put the ingredients into the vacuum melting furnace and vacuumize to 1×10 -3 Pa, then fill with argon until the pressure in the furnace reaches 0.05MPa, the melting current: 200A, flip and repeat the melting more than 5 times.

[0051] 3) Suction casting the ingot into shape, after cooling, take out the cast rod, put it into the muffle furnace for homogenization annealing treatment, heat up to 1000°C at a rate of 5°C / min, then open the furnace door and quickly put the cast rod Put it into the furnace, wait for the furnace temperature to return to 1000℃, and hold for 1h.

[0052] 3. Put the medium entropy allo...

Embodiment 3

[0054] A high-strength face-centered cubic structure medium-entropy alloy, the alloy composition: Co: 33.3%, Cu: 33.3%, Ni: 33.3%, and the preparation method includes the following steps:

[0055] Weigh 6.5 g of Co ingots, 7.01 g of Cu ingots, and 6.47 g of Ni ingots, and put the granular / lumpy raw materials Co, Cu, and Ni with a purity greater than 99.99% into proportions.

[0056] 2) Put the ingredients into the vacuum melting furnace and vacuumize to 1×10 -3 Pa, then fill with argon until the pressure in the furnace reaches 0.05MPa, the melting current: 200A, flip and repeat the melting more than 5 times.

[0057] 3) Suction casting the ingot into shape, after cooling, take out the cast rod, put it into the muffle furnace for homogenization annealing treatment, heat up to 1000°C at a rate of 5°C / min, then open the furnace door and quickly put the cast rod Put it into the furnace, wait for the furnace temperature to return to 1000℃, and hold for 1h.

[0058] 3. Put the medium entrop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compression ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength face-centered cubic structure medium-entropy alloy and a preparation method thereof. The CoNiCu medium-entropy alloy comprises Co, Ni and Cu elements; a resultof respective comparison of different medium-entropy alloys in electron concentration and mixing enthalpy according to the Gibbs free energy and the phase formation law of the alloy shows that the CoNiCu medium-entropy alloy has the tendency to form a single-phase FCC structure, a CoNiCu medium-entropy alloy model is constructed based on the tendency, and the alloy is predicted to be a ductile material by a first-principles technique. The preparation method of the alloy comprises the following steps: batching, vacuum melting, suction casting, homogenization annealing and solid solution treatment. Co, Cr, and Cu with a purity of 99% or more are selected and are proportioned according to an equimolar ratio or an approximately equimolar ratio, the proportioned raw materials are placed in a vacuum smelting furnace and are multiply smelted, suction casting molding is carried out after the components are uniform, and the obtained casting undergoes homogenization annealing and solid solutiontreatment to obtain the CoNiCu medium-entropy alloy having a single face-centered cubic structure and having a room temperature compressive strength of above 1600 MPa and a compression ratio of above20%.

Description

Technical field [0001] The invention relates to the technical field of new materials, in particular to a high-strength face-centered cubic structure medium-entropy alloy and a preparation method thereof. Background technique [0002] According to the mixing entropy, the existing alloys can be divided into three categories. The first category is a low-entropy alloy with one or two elements as the main constituent elements, namely traditional alloys (ΔS mix <1R); The second type is a medium entropy alloy with two to four main elements (1R≤S mix ≤1.5R); the third category is high-entropy alloys (S mix ≥1.5R). [0003] The outstanding performance of high-entropy alloys makes it one of the most researched metal materials. The high entropy effect of high-entropy alloys promotes the formation of single-phase solid solutions. At the same time, due to the significant solid solution strengthening effect, the strength and plasticity of the solid solution phase are increased. It is generall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C30/02C22C1/02B22D18/06C22F1/02
CPCB22D18/06C22C1/02C22C30/02C22F1/02
Inventor 储成林安旭龙戴挺
Owner SOUTHEAST UNIV