Conductive laminated structure and preparation method thereof, and display panel and display device

A laminated structure and cover plate technology, applied to the conductive layer on the insulating carrier, cable/conductor manufacturing, circuit, etc., can solve the problems of poor adhesion of nanometer metal wires, and achieve the effect of improving electrical conductivity and enhancing adhesion

Active Publication Date: 2018-12-07
GUANGZHOU GOVISIONOX TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adhesion of nanowires is currently poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive laminated structure and preparation method thereof, and display panel and display device
  • Conductive laminated structure and preparation method thereof, and display panel and display device
  • Conductive laminated structure and preparation method thereof, and display panel and display device

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] further, such as Figure 4 As shown, the embodiment of the present invention also proposes a method for preparing a conductive laminated structure, including the following steps:

[0047] Step S11, providing a substrate; and

[0048] Step S12 , forming a metal nano wire layer on the substrate, the metal nano wire layer doped with an optically transparent resin that does not contain a photoinitiator.

[0049] By adopting the above method, not only the adhesive force of the nanometer metal wire layer can be improved, the phenomenon of peeling can be prevented, but also the anti-ultraviolet ability of the nanometer metal wire layer can be improved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a conductive laminated structure and a preparation method thereof, a display panel and a display device. The conductive laminate structure and the preparation method thereof comprises a substrate; and a nano metal line layer on the substrate, the nano metal line layer doped with an optically transparent resin without a photoinitiator. As a result, the adhesion of the nano metal wire layer can be improved, the peeling phenomenon can be prevented, and the ultraviolet resistance of the nano metal wire layer can be improved.

Description

technical field [0001] The invention relates to nanometer metal wire materials and the application field thereof, in particular to a conductive laminated structure and a preparation method thereof, a display panel and a display device. Background technique [0002] Transparent conductors are widely used in fields such as touch panels, liquid crystal displays, thin film photo voltaic cells, and organic light emitting diode devices. growing year by year. [0003] Currently, indium tin oxide (ITO) is the main transparent conductive material, which has excellent light transmittance and conductivity. However, this kind of transparent conductive material is usually deposited by sputtering process, the preparation temperature is high, and it contains rare metals, which makes the price expensive. This kind of film is easy to break when it is bent, so it is not suitable for the preparation of flexible devices. As a result, there are many limitations in the performance and yield of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)