Water-based PET under-coating paint and preparation method thereof
A water-based and coating technology, applied in the direction of polyester coatings, coatings, primers, etc., can solve the problems of increasing process steps and inconvenient operation, and achieve the effects of improving production efficiency, high production efficiency, and short baking time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0044] The present invention also provides a kind of preparation method for preparing above-mentioned water-based PET primer, comprising the following steps:
[0045] S1. Dissolve the components with poor compatibility with the water-based polyester resin in the co-solvent, add deionized water, control the dispersion speed to 350-450r / min and stir evenly to obtain a dispersion system;
[0046] S2. Control the dispersion speed to 350-750r / min, add the water-based polyester resin and other components into the dispersion system under stirring, and stir evenly to obtain the water-based PET primer.
[0047] Preferably, in step S2, when the water-based polyester resin is a solid resin, the solid resin is dissolved into a resin solution with a content of 33% in hot water at 85°C before use, and then mixed in step S2, in order to accelerate the water-based To dissolve the polyester resin in hot water, a pH regulator can be added to the hot water, and the pH regulator is ammonia water....
Embodiment 1
[0049] A kind of water-based PET primer, is characterized in that, is made up of following component by weight:
[0050] 40 parts of water-based polyester resin;
[0051] 3 parts of co-solvent;
[0052] 5 parts of deionized water;
[0053] 0.1 part of defoamer;
[0054] 2 parts curing agent;
[0055] Catalyst 0.1 part;
[0056] Wetting agent 0.1 part;
[0057] Anti-sticking agent 0.1 part.
[0058] Preferably, the water-based polyester resin is a water-based saturated polyester resin, the number-average molecular weight Mn of the water-based saturated polyester resin is 10000, and the glass transition temperature Tg is 20°C.
[0059] Preferably, the co-solvent is at least one of alkyl alcohol, alcohol ether, ketone or alcohol ether acetate.
[0060] Preferably, the defoamer is at least one of mineral oil defoamer, polyether defoamer, organosiloxane defoamer or polyether modified organosiloxane defoamer.
[0061] Preferably, the catalyst is at least one of a strong acid...
Embodiment 2
[0070] A kind of water-based PET primer, is characterized in that, is made up of following component by weight:
[0071] 75 parts of water-based polyester resin;
[0072] 15 parts of co-solvent;
[0073] 57 parts of deionized water;
[0074] 0.5 part of defoamer;
[0075] 10 parts of curing agent;
[0076] 2 parts catalyst;
[0077] 1 part of wetting agent;
[0078] 1 part anti-sticking agent.
[0079] Preferably, the water-based polyester resin is a water-based saturated polyester resin, the number-average molecular weight Mn of the water-based saturated polyester resin is 18000, and the glass transition temperature Tg is 70°C.
[0080] Preferably, the co-solvent is at least one of alkyl alcohol, alcohol ether, ketone or alcohol ether acetate.
[0081] Preferably, the defoamer is at least one of mineral oil defoamer, polyether defoamer, organosiloxane defoamer or polyether modified organosiloxane defoamer.
[0082] Preferably, the catalyst is at least one of a strong ac...
PUM
Property | Measurement | Unit |
---|---|---|
Glass transition temperature | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap