Pre-coating with aluminized non-woven fabric or aluminized card paper base material

A technology of non-woven fabrics and pre-coated films, applied in the direction of heat-activated films/sheets, film/sheet release coatings, film/sheet-shaped adhesives, etc. Good and other problems, to achieve the effect of improving firmness and toughness, wide applicability, and good transparency

Active Publication Date: 2018-12-28
张家港保税区康得菲尔实业有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For aluminized non-woven fabrics and aluminized cardboard products, the product structure at home and abroad is basically similar. Ordinary products have the aluminized layer directly exposed to the air, while high-end products use methods such as spraying transparent ink or resin to protect the aluminum layer, resulting in Aluminum brightness and cause discoloration and graying of the aluminized surface
However, the transparency of aluminum-plated non-woven fabrics or cardboard products produced by covering methods such as net roll coating with resin is definitely not good; and the thickness of ink or resin coating can achieve the accuracy of micron level, and the thickness less than The level of 400 angstroms; in addition, the spray resin needs to be diluted with a solvent, and it is extremely difficult to avoid chemical reactions during the drying process; therefore, the performance and parameter indicators of various parts on the surface of the product material cannot be guaranteed.
[0003] The above problem is a common problem in the printing and packaging industry, and it is also a technical difficulty that seriously affects product quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pre-coating with aluminized non-woven fabric or aluminized card paper base material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of pre-coating film with aluminized non-woven fabric base material, comprises aluminized non-woven fabric base material, is arranged on the surface of aluminized non-woven fabric base material successively from bottom to top and is used for preventing its blackening transparent Coating B2 and transparent coating A1, the hot-melt adhesive layer 7 arranged under the aluminized non-woven fabric substrate, and the hot-melt adhesive layer 7 and the aluminized non-woven fabric substrate arranged between and used to strengthen the two layers The primer layer 6 of cohesive force between; The thickness of transparent coating A1 and transparent coating B2 is less than 400 angstroms; The aluminized non-woven fabric base material comprises non-woven fabric 5, is arranged on the aluminized layer 3 above non-woven fabric 5, and The reinforced aluminized layer 4 arranged between the aluminized layer 3 and the non-woven fabric 5 is used to increase the firmness and toughness of t...

Embodiment 2

[0054] A precoated film with an aluminized non-woven fabric substrate, including an aluminized cardboard substrate, and a transparent coating B2 that is sequentially arranged on the upper surface of the aluminized cardboard substrate from bottom to top and used to prevent it from turning black Transparent coating A1, the hot-melt adhesive layer 7 arranged below the aluminum-plated cardboard substrate, and the adhesive layer between the hot-melt adhesive layer 7 and the aluminum-coated cardboard substrate and used to enhance the bonding force between the two layers Base coat 6; the thickness of transparent coating A1 and transparent coating B2 is less than 400 angstroms; aluminum plated cardboard base material comprises cardboard 5, is arranged on the aluminum coating layer 3 above the cardboard 5, and is arranged on the aluminum coating layer 3 and the cardboard The reinforced aluminized layer 4 between the papers 5 is used to increase the firmness and toughness of the aluminiz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pre-coating with an aluminized non-woven fabric or an aluminized card paper base material. The pre-coating sequentially comprises a transparent coating A, a transparent coating B, an aluminum coating, an enhanced aluminum coating, a non-woven fabric or card paper, a base coat and a hot melt adhesive layer from top to bottom, wherein the thickness of the transparent coating A and the transparent coating B is less than 400 angstroms; the refractive index of the transparent coating A to visible light is less than that of the transparent coating B. According to the pre-coating disclosed by the invention, the enhanced aluminum coating is coated on the surface of the non-woven fabric or card paper, so that the firmness and toughness of the aluminum coating are improved;due to evaporation of two transparent coatings having different physical properties, the problems that color change occurs and the aluminum coating darkens because the non-woven fabric or card paperis printed or coated after surface aluminizing are solved.

Description

technical field [0001] The invention belongs to the technical field of packaging and printing. More specifically, it relates to a precoated film having an aluminized non-woven fabric or an aluminized cardboard substrate. Background technique [0002] For aluminized non-woven fabrics and aluminized cardboard products, the product structure at home and abroad is basically similar. Ordinary products have the aluminized layer directly exposed to the air, while high-end products use methods such as spraying transparent ink or resin to protect the aluminum layer, resulting in Aluminum brightness and cause discoloration and graying of the aluminized surface. However, the transparency of aluminum-coated non-woven fabrics or cardboard products produced by covering methods such as net roll coating with resin is definitely not good; and the thickness of ink or resin coating can achieve a micron-level accuracy, which cannot achieve a thickness less than The level of 400 angstroms; in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/35C09J7/21C09J7/50
CPCC09J7/21C09J7/35C09J7/50C09J2479/023C09J2475/00C09J2467/003C09J2423/163C09J2423/04C09J2400/283C09J2400/263C09J2301/122C09J2301/304Y02W30/80
Inventor 许文虓李建云柯万春
Owner 张家港保税区康得菲尔实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products