Zinc-based coated steel sheet, manufacturing method thereof, thermoforming method and component

A coated steel sheet and thermoforming technology, applied in the field of coated steel sheet, can solve the problems of easy evaporation, erosion of liquid phase metal coating on steel sheet, influence on process, etc.

Inactive Publication Date: 2019-01-01
ANGANG STEEL CO LTD
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to protect the steel plate, the commonly used method is to coat the surface of the steel plate with a layer of protective metal coating. The commonly used ones are galvanized and aluminum-plated, but there are some problems. Galvanizing is prone to corrosion of the steel plate by the liquid metal coating, and Easy to evaporate; aluminum plating will form a layer of hard iron-aluminum compound on the surface of the steel plate, which will affect the subsequent process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc-based coated steel sheet, manufacturing method thereof, thermoforming method and component
  • Zinc-based coated steel sheet, manufacturing method thereof, thermoforming method and component
  • Zinc-based coated steel sheet, manufacturing method thereof, thermoforming method and component

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] Describe below in conjunction with specific embodiment:

[0029] The embodiment sees attached table 1, 2, 3.

[0030] The strength of the steel plate is greater than 1500MPa, and the elongation is greater than 5%. The coating is completely transformed into an iron alloy layer, without coating evaporation, liquid phase erosion, and hard Fe-Al intermetallic compounds. The structure of the component is martensite + ferrite + retained austenite.

[0031] Attached table 1: the chemical element composition of embodiment coating

[0032]

[0033]

[0034] Attached Table 2: Chemical Composition of Example Steels

[0035]

[0036]

[0037] Attached table 3: Process parameters and properties of the steel in the example

[0038]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a zinc-based coated steel sheet, a manufacturing method thereof, a thermoforming method and a component. After hot press forming, the strength of the steel sheet is greater than 1500 MPa, and the elongation is greater than 5%. A coating is completely transformed into a ferroalloy layer, no evaporation of the coating is generated, no liquid-phase erosion phenomenon is generated, and no hard Fe-Al intermetallic compound is generated. The structure of the component is martensite, ferrite, and retained austenite.

Description

technical field [0001] The invention relates to a coated steel sheet, in particular to a zinc-based coated steel sheet, a manufacturing method, a thermoforming method and components thereof. Background technique [0002] For a long time, steel has been the basis of the automobile industry. Although the amount of aluminum alloy, magnesium alloy, plastic and composite materials in automobile manufacturing has been increasing, high-strength steel has high potential for weight reduction, high impact absorption energy, and high fatigue. The advantages of strength, high formability and low planar anisotropy have become the main lightweight materials for the automotive industry. The automobile industry in the 21st century to reduce fuel consumption and reduce CO 2 And exhaust emissions have become the main needs of the society. In order to adapt to this development trend, the steel industry has developed many types of high-strength steel plates such as DP, TRIP, CP, and QP steel t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C18/02C22C18/04C22C18/00C22C38/02C22C38/04C22C38/06C22C38/60C22C38/14C22C38/12C22C38/16C22C38/34C22C38/38C22C38/32C22C38/28C22C38/22C22C38/20C22C38/26C22C38/58C22C38/54C22C38/50C22C38/44C22C38/42C22C38/48C23C2/06C21D8/02
CPCC21D8/0226C21D2211/001C21D2211/005C21D2211/008C22C18/00C22C18/02C22C18/04C22C38/002C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C22C38/16C22C38/20C22C38/22C22C38/26C22C38/28C22C38/32C22C38/34C22C38/38C22C38/42C22C38/44C22C38/48C22C38/50C22C38/54C22C38/58C22C38/60C23C2/06
Inventor 吕家舜杨洪刚周芳王永明徐承明李锋刘仁东
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com