High-temperature art porcelain pink glaze and preparation method and sintering technology thereof

A peach-colored and artistic technique, applied in the field of high-temperature art porcelain peach-colored glaze and its preparation, to achieve the effect of stabilizing the glaze color and enamel

Active Publication Date: 2019-01-04
PINGDINGSHAN UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the influence of factors such as production cost and technology, the ceramic glazes used for large-scale glaze murals and display art are mostly medium and low temperature glazes. Although they have certain environmental tolerance, they are also limited by the natural environment and use time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature art porcelain pink glaze and preparation method and sintering technology thereof
  • High-temperature art porcelain pink glaze and preparation method and sintering technology thereof
  • High-temperature art porcelain pink glaze and preparation method and sintering technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A pink glaze for high-temperature art porcelain, the pink glaze is made of the following raw materials by weight percentage: base glaze 88%, color base 12%; the base glaze is made of the following raw materials by weight percentage: feldspar 35% , 40% of quartz, 10% of clay, and 15% of zinc oxide; the color base is made of the following raw materials in weight percentage: 8% of manganese carbonate, 80% of aluminum hydroxide, 7% of ammonium nitrate, and phosphoric acid with a mass concentration of 50%. 5%.

[0023] The preparation method of the high-temperature artistic porcelain pink glaze includes the following steps: 1) mixing the raw materials of the base glaze in proportion, putting them into a glaze mill, grinding at 45r / min for 18 hours, and filtering through a 120-mesh sieve to obtain the base glaze; 2) Put the raw materials of the color base into the glaze mill in proportion and grind for 1 hour at 450r / min, and filter through a 120-mesh sieve to obtain the colo...

Embodiment 2

[0026] A pink glaze for high-temperature art porcelain, the pink glaze is made of the following raw materials by weight percentage: base glaze 88%, color base 12%; the base glaze is made of the following raw materials by weight percentage: feldspar 50% , 30% of quartz, 10% of clay, and 10% of zinc oxide; the color base is made of the following raw materials in weight percentage: 10% of manganese carbonate, 74% of aluminum hydroxide, 8% of ammonium nitrate, and phosphoric acid with a mass concentration of 50%. 8%.

[0027] The preparation method of the high-temperature artistic porcelain pink glaze includes the following steps: 1) mixing the raw materials of the base glaze in proportion, putting them into a glaze mill, grinding at 45r / min for 22 hours, and filtering through a 140-mesh sieve to obtain the base glaze; 2) Put the raw materials of the color base into the glaze mill in proportion and grind them for 2 hours at 450r / min, and filter through a 140-mesh sieve to obtain t...

Embodiment 3

[0030] A pink glaze for high-temperature art porcelain, the pink glaze is made of the following raw materials by weight percentage: base glaze 88%, color base 12%; the base glaze is made of the following raw materials by weight percentage: feldspar 35% , 30% of quartz, 25% of clay, and 10% of zinc oxide; the color base is made of the following raw materials in weight percentage: 10% of manganese carbonate, 78% of aluminum hydroxide, 5% of ammonium nitrate, and phosphoric acid with a mass concentration of 50%. 7%.

[0031] The preparation method of the described high-temperature artistic porcelain pink glaze is the same as in Example 1.

[0032] The firing process of the described high-temperature artistic porcelain pink glaze is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides high-temperature art porcelain pink glaze. The pink glaze is prepared from, by weight, 88% of base glaze and 12% of color base; the base glaze is prepared from, by weight, 35-50% of feldspar, 30-40% of quartz, 10-25% of clay and 10-15% of zinc oxide. The color base is prepared from, by weight, 8-10% of manganese carbonate, 74-80% of aluminum hydroxide, 5-8% of ammonium nitrate and 5-8% of phosphoric acid with the mass concentration of 50%. The color and texture of the sintered glaze are more stable, the glaze can withstand any natural environments and can be permanentlypreserved; and the high-temperature art porcelain pink glaze is mainly suitable for providing pink required by high-temperature porcelain plate glaze painting, and the flat sintering technology is adopted at the time of sintering.

Description

technical field [0001] The invention belongs to the technical field of high-temperature art porcelain glazes, and in particular relates to a high-temperature art porcelain pink glaze, a preparation method and a firing process thereof. Background technique [0002] High-temperature art porcelain means that in the field of art porcelain production, the melting temperature of the glaze is around 1300°C, and the kiln atmosphere is oxidized or reduced, and a unique glaze color appears after firing. [0003] Ceramic decorative materials are the main material for indoor and outdoor decoration. Although the relatively rich ceramic decorative materials in the market have characteristics that other decorative materials such as wear resistance, corrosion resistance, and weathering resistance cannot replace. However, due to the influence of factors such as production cost and technology, most of the ceramic glazes used for large-scale glaze murals and display art are medium and low tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 孙晓岗刘晓明杨兴化孔相卿
Owner PINGDINGSHAN UNIVERSITY