A kind of preparation method of macroporous strongly acidic styrene ion exchange resin

A technology of strong acid styrene and ion exchange resin, applied in the direction of ion exchange, cation exchange, organic cation exchanger, etc., can solve the problems of environmental protection, poor resin quality, cumbersome resin production process, etc., and achieve strong anti-pollution performance, Reduce production cost, unbreakable effect

Active Publication Date: 2019-07-19
扬州金珠树脂有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention is to prepare a macroporous strongly acidic styrene-based cation exchange resin aimed at the defects of poor resin quality, cumbersome resin production process and non-environmental protection produced by the current raw materials;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of macroporous strongly acidic styrene ion exchange resin
  • A kind of preparation method of macroporous strongly acidic styrene ion exchange resin
  • A kind of preparation method of macroporous strongly acidic styrene ion exchange resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Macroporous strongly acidic styrene-based cation exchange resin, the synthesis steps are as follows (the following proportions are calculated based on 1 ton of finished resin):

[0030] (1) Preparation of water phase material: 550Kg of demineralized water is added to the reactor, then 25Kg of industrial salt is added, until it is completely dissolved, 15Kg of polyvinyl alcohol aqueous solution of methylene blue 1g and 1788 (4%) aqueous solution is added, fully stirred Mix and heat up to 58°C for later use;

[0031] (2) Prepare the organic phase: take 200Kg of styrene and add it to the batching kettle, add 10Kg of polystyrene resin, stir for 3 hours, wait for it to fully dissolve, then add 20Kg of solid paraffin, heat up to 60°C and stir for 20min, after it is fully dissolved, pump Add divinylbenzene 30Kg, and add initiator benzoyl peroxide 2.5Kg, stir 5min, obtain organic phase, standby;

[0032] (3) Polymerization operation: Put the prepared organic phase into the wat...

Embodiment 2

[0036] Macroporous strongly acidic styrene-based cation exchange resin, the synthesis steps are as follows (the following proportions are calculated based on 1 ton of finished resin):

[0037] (1) Preparation of water phase material: 580Kg of demineralized water is added to the reactor, then 28Kg of industrial salt is added, and it is completely dissolved, then 16Kg of polyvinyl alcohol aqueous solution of methylene blue 1g and 1788 (4%) aqueous solution is added, fully stirred Mix and heat up to 58°C for later use;

[0038] (2) Prepare the organic phase: take 195Kg of styrene and add it to the batching kettle, add 15Kg of polystyrene resin, stir for 3 hours, wait for it to fully dissolve, then add 20Kg of solid paraffin, heat up to 60°C and stir for 20min, after it is fully dissolved, pump Add divinylbenzene 35Kg, and add initiator benzoyl peroxide 2Kg, stir 5min, obtain organic phase, standby;

[0039](3) Polymerization operation: put the prepared organic phase into the wat...

Embodiment 3

[0043] Macroporous strongly acidic styrene-based cation exchange resin, the synthesis steps are as follows (the following proportions are calculated based on 1 ton of finished resin):

[0044] (1) Preparation of water phase material: 600Kg of demineralized water is added to the reactor, then 30Kg of industrial salt is added, until it is completely dissolved, 18Kg of polyvinyl alcohol aqueous solution of methylene blue 1g and 1788 (4%) aqueous solution is added, fully stirred Mix and heat up to 58°C for later use;

[0045] (2) Prepare the organic phase: Take 190Kg of styrene and add it to the batching kettle, add 20Kg of polystyrene resin, stir for 3 hours, wait for it to fully dissolve, then add 30Kg of solid paraffin, heat up to 60°C and stir for 20min, after it is fully dissolved, pump Add divinylbenzene 40Kg, and add initiator benzoyl peroxide 3Kg, stir 5min, obtain organic phase, standby;

[0046] (3) Polymerization operation: Put the prepared organic phase into the water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of ion exchange resin, and relates to a preparation method of macropore strong acid type styrene series ion exchange resin. The preparation method of the macropore strong acid type styrene series ion exchange resin comprises the following steps: (1) preparation of a water phase: mixing softened water, industrial salt, methylene blue and a polyvinyl alcohol aqueous solution, stirring and heating for subsequent use; (2) preparation of an organic phase: after mixing styrene and the polystyrene resin, stirring, adding solid paraffin, heating and reacting, stirring and dissolving, sucking divinylbenzene, adding an initiator, and stirring to obtain the organic phase; (3) mixing the organic phase and the water phase at a mass ratio of 0.428-0.445: 1; carrying out heating reaction, and filtering out liquid; adding methylbenzene for washing; after the methylbenzene is filtered thoroughly, adding water, carrying out heating reaction, washing and carrying out hot-air drying; and adding sulfuric acid, carrying out heating reaction, cooling, and adding water for diluting to obtain the final product. The prepared resin is simple in process, is environmentally friendly and pollution-free, and is widely used for water treatment, the organic impurity removal rate reaches 99% or above, and the application prospect is wide.

Description

technical field [0001] The invention belongs to the technical field of ion exchange resins, and in particular relates to a preparation method of macroporous strongly acidic styrene-based ion exchange resins. Background technique [0002] There are a wide variety of ion exchange resin products. According to the nature of the active groups it carries, it can be divided into strong acid cations, weak acid cations, strong base anions, weak base anions, chelating, amphoteric and redox resins; according to different functions and principles of action, it can be divided into water treatment Resins, adsorption resins and resin catalysts, among which water treatment resins have the most output; according to different pore types, they can be divided into gel type and macroporous type; [0003] Among them, strong-acid cation exchange resins have been widely used as catalysts in organic reactions such as esterification, hydrolysis, condensation, hydration, alkylation, and acylation in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F212/36C08J9/26B01J39/19B01J39/05
CPCB01J39/05B01J39/19C08F212/08C08J9/26C08J2201/046C08J2325/08C08F212/36
Inventor 阮圣如陈必玉张雪峰吉霞卢浩李玉琴
Owner 扬州金珠树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products