PA66 composite material and preparation method thereof

A technology of PA66 and composite materials, applied in the field of polymer materials, can solve the problems of insufficient rigidity or toughness of PA66, and achieve the effects of avoiding agglomeration or delamination, great promotion value, and improving rigidity and toughness

Inactive Publication Date: 2019-01-04
ANHUI JIANGHUAI AUTOMOBILE GRP CORP LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a PA66 composite material and its preparation method to solve the problem that the rigidity or toughness of the existing PA66 cannot meet some specific requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PA66 composite material and preparation method thereof
  • PA66 composite material and preparation method thereof
  • PA66 composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] The preparation method of any one of the above-mentioned PA66 composite materials, comprising the following steps:

[0048] (1) Weigh 80-100 parts of PA66, 40-50 parts of functionally modified masterbatch, 0.1-0.5 parts of antioxidant, mix and stir evenly to obtain a mixture;

[0049] (2) Extrude and granulate the mixture obtained in step (1) to obtain PA66 composite material.

[0050] The step (2) is specifically: putting the mixture obtained in the step (1) into the hopper of a twin-screw extruder to extrude and granulate to obtain a PA66 composite material, wherein the twin-screw extruder includes Six temperature zones are arranged in sequence, the temperature of the first zone is 200-220°C, the temperature of the second zone is 260-280°C, the temperature of the third zone is 260-280°C, the temperature of the fourth zone is 260-280°C, the temperature of the fifth zone is 260-280°C, The temperature in the six zones is 260-280°C, the head temperature is 260-280°C, and...

Embodiment 1

[0052] (1) Weigh 80 parts of PA66, 40 parts of functionally modified masterbatch, 0.1 part of Irganox168, mix and stir evenly to obtain a mixture;

[0053] (2) Extrude and granulate the mixture obtained in step (1) to obtain PA66 composite material P1.

[0054] Among them, the temperature and screw speed of each zone of the twin-screw extruder are respectively: the temperature of the first zone is 200°C, the temperature of the second zone is 260°C, the temperature of the third zone is 260°C, the temperature of the fourth zone is 260°C, the temperature of the fifth zone is 260°C, the temperature of the sixth zone is 260°C, The head temperature is 260°C; the screw speed is 200r / min.

Embodiment 2

[0056](1) Weigh 100 parts of PA66, 50 parts of functionally modified masterbatch, 0.1 part of Irganox168, 0.2 part of Irganox1330, 0.2 part of Irganox1010, mix and stir evenly to obtain a mixture;

[0057] (2) Extrude and granulate the mixture obtained in step (1) to obtain PA66 composite material P2.

[0058] Among them, the temperature and screw speed of each zone of the twin-screw extruder are respectively: the temperature of the first zone is 220°C, the temperature of the second zone is 280°C, the temperature of the third zone is 280°C, the temperature of the fourth zone is 280°C, the temperature of the fifth zone is 280°C, and the temperature of the sixth zone is 280°C. The head temperature is 280°C; the screw speed is 280r / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a PA66 composite material and a preparation method thereof. The PA66 composite material is prepared from the following components in parts by weight: 80-100 parts of PA66, 40-50 parts of functional modified masterbatches and 0.1-0.5 part of an antioxidant. The functional modified masterbatches is prepared from the following componnets in parts by weight: 20-40 parts of MBS, 20-30 parts of wollastonite, 40-60 parts of talcum powder, 1-3 parts of oleamide and 1-3 parts of isopropyl tris(dioctyl phosphate acyl oxide) titanate. By the technical scheme, compared with a packing used directly, the functional modified masterbatches optimizes a production environment, improves the production efficiency, and has quite high promotion value.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, in particular to a PA66 composite material and a preparation method thereof. Background technique [0002] Polyamide 66 (PA66), as a common thermoplastic, is widely used. In practical applications, it is often necessary to modify PA66 to improve the rigidity or toughness of PA66 to meet the needs of different application fields. [0003] This technical solution innovatively uses functionally modified masterbatches to improve PA66 composite materials, which solves the problem of incompatibility between rigidity and toughness, and at the same time improves the rigidity and toughness of PA66 composite materials. This method has not been reported so far, which greatly expands It has widened the application range of PA66 composite material and has very practical significance. Contents of the invention [0004] The purpose of the present invention is to provide a PA66 composite material a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L51/04C08K3/34C08K5/20C08K7/10C08J3/22
CPCC08L77/06C08J3/226C08J2351/04C08J2377/06C08K2201/003C08L51/04C08K3/34C08K5/20C08K7/10
Inventor 刘凯黄家奇孙启林
Owner ANHUI JIANGHUAI AUTOMOBILE GRP CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com