Coating material including fired object of soft porous ancient marine humus
A technology of coating materials and porosity, applied in the direction of metal material coating process, coating, thin material treatment, etc., can solve undocumented problems, improve yield, improve safety and usefulness, and improve fuel efficiency Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0068] 1. Fabrication of coating materials and disks coated therewith
[0069] Mironekuton (manufactured by Iwase Cosfa Co., Ltd.), which is a soft porous ancient marine humus, was directly calcined in a powder state at about 800° C. to produce a calcined powder (particle size of 10 μm or less). Mix 8 g in 16 L of paint containing PTFE (852N-201 (manufactured by Du Pont-Mitsui Fluorochemicals Co. Ltd.) or EK-3700C21R (manufactured by Daikin Industries, Ltd.) with a solid content (PTFE) of about 50 parts by mass) The aforementioned calcined powder (about 0.1% by mass relative to the aforementioned solid content) was used to produce a coating material (containing about 0.05% by mass of the aforementioned calcined powder).
[0070] The above-mentioned coating material was uniformly applied to the surface of a stainless steel plate having a length of 5 cm and a width of 10 cm to a thickness of about 20 μm, and dried. The produced and coated disk was used in the following experime...
Embodiment 2
[0084] 1. Manufacture of cartridges for improving oil quality with sintered bodies
[0085] Mironekuton (manufactured by Iwase Cosfa Co., Ltd.), which is a soft porous ancient marine humus, was molded into a spherical shape with a diameter of 15 mm, and fired at about 800° C. to produce a spherical sintered body. Two of these sintered bodies were housed in a cylinder (25×25×60 mm, made of stainless steel, with holes), and used in the following experiments as a cylinder for improving oil quality.
[0086] 2. About trans fatty acids
[0087] The above-mentioned cartridge for improving oil quality was immersed in 1 L of edible oil, and the trans fatty acid content was measured by the same method as in Example 1. When the oil quality improving cartridge provided with the sintered body of the present invention was used for the treatment, as shown in Table 2 below, no trans fatty acid was detected.
[0088] [Table 2]
[0089] Table 2: Trans Fatty Acid Content in Edible Oils
[0...
Embodiment 3
[0101] 1. Production of sintered body for putting into tank
[0102] Mironekuton (manufactured by Iwase Cosfa Co., Ltd.), which is a soft porous ancient marine humus, was molded into a spherical shape with a diameter of 15 mm or 5 mm, and fired at about 800° C. to produce a spherical sintered body.
[0103] 2. About the highest output, maximum torque and fuel efficiency
[0104] One of the above-mentioned sintered bodies (5 mm in diameter) was put into an engine oil tank (E) containing engine oil or a transmission (T) containing transmission oil. Table 3 below shows the measurement results of the maximum output, maximum torque, and fuel efficiency before and after the installation.
[0105] [table 3]
[0106] Table 3: Maximum output, maximum torque and fuel efficiency
[0107]
[0108] When the sintered body of soft porous ancient marine humus of the present invention is put into an engine or a gearbox, the engine speed at which the maximum output is exerted becomes low,...