Polyvinyl chloride calcium-plastic flooring material and preparation method thereof

A technology of polyvinyl chloride and floor materials, applied in the field of floor materials, can solve problems such as poor texture and poor anti-skid performance

Inactive Publication Date: 2019-01-18
王家盛
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a polyvinyl chloride calcium-plastic floor material and its preparation method, which can solve the problems of poor texture and poor anti-skid performance of existing calcium-plastic floor materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] A polyvinyl chloride calcium plastic flooring material, made of the following components in parts by weight: 30 parts of polyvinyl chloride resin powder, 30 parts of polyvinyl chloride recycled resin powder, 30 parts of neodymium oxide, 30 parts of calcium carbonate, 100 parts 20 parts of bauxite, 8 parts of sodium methyl silicate, 3 parts of phytosterol, 3 parts of calcium stearate, and 2 parts of lauric acid diethanolamide.

[0014] The preparation method of this polyvinyl chloride calcium plastic floor material comprises the following steps:

[0015] (1) Ingredients: According to the ratio of raw materials, polyvinyl chloride resin powder, polyvinyl chloride recycled resin powder, neodymium oxide, calcium carbonate, 100 mesh alumina, sodium methyl silicate, phytosterol, calcium stearate, laurel Acid diethanolamide is added into a mixer and mixed at a speed of 1200 rpm for 20 minutes at a temperature of 100°C to obtain a mixture for later use;

[0016] (2) Granulatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyvinyl chloride calcium-plastic flooring material and a preparation method thereof. The flooring material is prepared from raw materials in parts by weight as follows: 30 parts of polyvinyl chloride resin powder, 30-50 parts of polyvinyl chloride reclaimed resin powder, 30-45 parts of neodymium oxide, 30-40 parts of calcium carbonate, 20-40 parts of 100-mesh alumina, 8-12 parts of sodium methyl silicate, 3-5 parts of phytosterol, 3-5 parts of calcium stearate and 2 parts of lauroyl diethanolamide. The invention also provides the polyvinyl chloride calcium-plastic flooring material and the preparation method thereof. Through combination of the formula and the preparation method, the problems of poor texture and bad anti-skid performance of existing calcium-plastic flooring materials are solved.

Description

technical field [0001] The invention belongs to the technical field of floor materials, and in particular relates to a polyvinyl chloride calcium-plastic floor material and a preparation method thereof. Background technique [0002] Calcium-plastic materials are a type of composite material that is made of inorganic calcium salt as the main raw material and mixed with synthetic resins such as polyolefins. It has chemical stability, high and low temperature resistance, good heat insulation, water resistance, good flame retardancy, slow burning speed, less smoke, and is not easy to cause fire and public nuisance. Widely used as building materials, home improvement materials, furniture and daily necessities materials, etc., the existing calcium-plastic floor materials have the above-mentioned advantages, but also have the problems of poor texture and poor anti-skid performance. Contents of the invention [0003] The technical problem to be solved by the present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/22C08K3/26C08K5/098B29C48/92
CPCC08L27/06C08K2003/221C08K2003/2227C08K2003/265C08L2205/025C08L2207/20C08K13/02C08K3/22C08K3/26C08K5/098
Inventor 王家盛
Owner 王家盛