Application of polyamide 5X as reinforced thermoplastic compound apparent mass modifier
A thermoplastic composition, a technology for enhancing thermoplastic, which is applied in the field of polyamide 5X as an apparent quality improver for reinforced thermoplastic compositions, can solve problems such as poor apparent quality, and achieve good dimensional stability, appearance requirements and dimensional stability requirements High, improve the effect of surface quality problems
Active Publication Date: 2019-02-05
BENSONG ENG PLASTICS HANGZHOU
View PDF11 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0007] The purpose of the present invention is to provide a kind of apparent quality improver for the reinforced thermoplastic composition that is used to improve the defect of poor apparent quality of traditional reinforced polyamide composite product, promptly provide polyamide 5X as reinforced thermoplastic composition apparent quality improver The use of and the thermoplastic composition containing the polyamide 5X resin of said use
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0029] For further explanation, the present invention provides the following examples so that those skilled in the art can clearly understand the gist of the present invention. However, it should be noted that the following embodiments are not limitations to the technical solution of the present invention. Those skilled in the art may make a series of deformations and modifications to the technical solution provided by the present invention in combination with existing knowledge while analyzing and understanding the various embodiments. Equivalent replacement, the new technical solution obtained by the deformation and equivalent replacement is also included in the present invention.
[0030]Since the embodiments of the present invention cannot be exhaustive, some preferred technical features and preferred technical solutions can be reasonably replaced or combined with each other, and the resulting new technical solutions are also included in the present invention.
[0031] Bec...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention belongs to the field of polymer composites, provides application of polyamide 5X resin as reinforced thermoplastic compound apparent mass modifier, and also provides a thermoplastic compound. The polyamide 5X as reinforced thermoplastic compound apparent mass modifier has the beneficial effects that novel bio-based resin-polyamide 5X resin is added into a conventional reinforced thermoplastic compound system to achieve a purpose of obviously eliminating the surface quality problem of a conventional reinforced thermoplastic compound product, and in addition, an improvement effectand the filling amount of enhanced filler in a certain range are in a direct proportion; meanwhile, a product warping problem is obviously eliminated, and product dimension stability is better. The polyamide 5X as reinforced thermoplastic compound apparent mass modifier can be widely applied to fields with high requirements on mechanical strength, appearance requirements and dimension stability; the application range of the reinforced thermoplastic compound is widened, and the application range of the polyamide 5X resin is also widened.
Description
technical field [0001] The invention belongs to the field of polymer composite materials, and specifically relates to the use of polyamide 5X as an agent for improving the apparent quality of reinforced thermoplastic compositions. Background technique [0002] Polyamide resin has excellent mechanical properties, thermal properties, and chemical resistance, so it is widely used as parts in the fields of automobiles, electrical equipment, mechanical parts, transportation equipment, textiles, papermaking machinery, and communication supplies. Reinforced polyamide composite materials, especially high-strength polyamide composite materials, have successfully replaced metal materials and are used in the production of auto parts. While achieving the purpose of lightening the car and achieving fuel-saving and high-speed purposes, it can still ensure the strength, stiffness, and Requirements such as wear resistance, heat resistance and corrosion resistance have become an important sy...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L77/02C08K7/14C08K5/20
CPCC08L77/06C08L2205/025C08L2205/03C08L77/02C08K7/14C08K5/20
Inventor 于同周昌伟叶巍陈剑锐
Owner BENSONG ENG PLASTICS HANGZHOU