Lubricating agent for processing hemp roving and preparation method thereof

A lubricant and roving technology, applied in the field of hemp textile, can solve the problems of weak strength, reduce textile efficiency, affect the dyeing of spun yarn, etc., achieve the effect of reducing the strong CV value, good softness and smoothness, and improving winding efficiency

Active Publication Date: 2019-02-12
青岛奥洛思新材料有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor cohesion and weak strength of the hemp fiber, in the spinning process, it is easy to cause uneven force in the drafting area of ​​the spinning frame, and the spun yarn is not fluffy after spinning, and the texture is relatively hard, which reduces the winding efficiency and affects the subsequent spun yarn dyeing. The end-break rate in the weaving process is reduced and the textile efficiency is reduced. Therefore, increasing the research on lubricants for processing flax or hemp roving will help to improve textile efficiency and promote the development of the hemp spinning industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A lubricant for processing hemp roving and a preparation method thereof, comprising the following steps:

[0061] (1) Weighing: Inspect various raw materials according to requirements, weigh various raw materials according to the formula ratio, and reserve them for later use;

[0062] (2), heating and stirring: add deionized water into the reaction kettle equipped with a stirring device, adjust the temperature of the reaction kettle to 45-50 °C, after the temperature is stable, add D48 with a weight percentage of 15%-20% Add methylcyclotetrasiloxane into the reaction kettle, turn on the stirring device, the stirring device rotates at 100-200rpm, raise the temperature of the reaction kettle to 95°C; the stirring time is 30-50min;

[0063] (3), heating and stirring: continue to control the temperature of the reactor at 95°C for 1 hour, then add 6-9% silicon wax, continue to rise to 110°C, pour in nitrogen for 50 minutes, and then increase the weight percentage to 2%. -3% p...

Embodiment 2

[0068] A lubricant for processing hemp roving and a preparation method thereof, comprising the following steps:

[0069] (1) Weighing: Inspect various raw materials according to requirements, weigh various raw materials according to the formula ratio, and reserve them for later use;

[0070] (2), heating and stirring: add deionized water into the reaction kettle equipped with a stirring device, adjust the temperature of the reaction kettle to 47 ° C, after the temperature is stable, add 18% by weight of D4 octamethylcyclotetrasilicon Add oxane into the reaction kettle, turn on the stirring device, the stirring device rotates at 150rpm, raise the temperature of the reaction kettle to 95°C; the stirring time is 40min;

[0071] (3), heating and stirring: continue to control the temperature of the reactor at 95°C for 1 hour, then add 8% silicon wax, continue to rise to 110°C, pour into nitrogen and keep warm for 50 minutes, and then add 2.5% by weight of poly Add oxyethylene ethe...

Embodiment 3

[0076] A lubricant for processing hemp roving and a preparation method thereof, comprising the following steps:

[0077] (1) Weighing: Inspect various raw materials according to requirements, weigh various raw materials according to the formula ratio, and reserve them for later use;

[0078] (2), heating and stirring: add deionized water into the reaction kettle equipped with a stirring device, adjust the temperature of the reaction kettle to 50 ° C, after the temperature is stable, add 20% by weight of D4 octamethylcyclotetrasilicon Add oxane into the reaction kettle, turn on the stirring device, the stirring device rotates at 200rpm, raise the temperature of the reaction kettle to 95°C; the stirring time is 50min;

[0079] (3), heating and stirring: continue to control the temperature of the reactor at 95°C for 1 hour, then add 9% silicon wax, continue to rise to 110°C, pour into nitrogen and keep warm for 50 minutes, and then add 3% polystyrene wax to Add oxyethylene ether...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of hemp textiles, in particular to a lubricating agent for processing hemp roving and a preparation method thereof. The lubricating agent is prepared fromthe following components by weight percent: 3 to 6 percent of tetra-ester quaternary ammonium salt, 2 to 3 percent of polyoxyethylene ether, 6 to 9 percent of silicon wax, 3 to 5 percent of silane coupling agent KN-550, 2 to 3 percent of catalyst T-50, 15 to 20 percent of D4 octamethylcyclotetrasiloxane, 0.5 to 1.5 percent of glacial acetic acid, and the balance of deionized water. According to the preparation method of the lubricating agent, a finished product is obtained in the steps of measuring the components according to the formula ratio, stirring in different stages, heating, and commissioning. The minimal strength of the roving can be improved, the mightiness CV value can be reduced, the force of a spinning frame traction area is more uniform, the spun yarn is loose and soft, the spooling efficiency can be improved, the subsequent spun yarn dyeing is not influenced, the end broken rate in the weaving process can be reduced, and the waving efficiency can be effectively improved.

Description

technical field [0001] The invention relates to the technical field of hemp spinning, in particular to a lubricant for treating hemp roving and a preparation method thereof. Background technique [0002] China is a big country of hemp textiles. The Yangtze River Delta and Pearl River Delta regions have become the world's most important flax production centers. Linen cloth is a fabric made of flax fiber. Various spinning processes into yarn. Hemp fibers for spinning include bast fibers and leaf fibers. Bast fibers include ramie, jute, kenaf, velvet, flax, hemp, etc. Leaf fiber has sisal, abaca and so on. Hemp fibers are rich in resources and have the characteristics of long fibers, small elongation, and fast moisture absorption and release. The spun yarns can be made into various hemp fabrics, hoses, conveyor belts, and various sewing hemp threads, etc., for clothing, decoration, It is widely used in industrial and agricultural production and national defense construction...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/46D06M15/53D06M13/513D06M13/188D06M101/06
CPCD06M13/188D06M13/46D06M13/513D06M15/53D06M16/00D06M2101/06D06M2200/25D06M2200/40D06M2200/50
Inventor 尤士华张铭
Owner 青岛奥洛思新材料有限公司