Concrete containing natural zeolite powder and preparation method thereof

A technology of zeolite powder and concrete, which is applied in the field of concrete containing natural zeolite powder and its preparation, can solve the problems that restrict the normal production of concrete, achieve good pumpability, improve work performance, and increase cohesion

Inactive Publication Date: 2019-03-08
广西建宏水泥制品有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the vigorous development of the construction market, the supply of waste slag admixtures such as fly ash, mineral powder, and silica fume is in short supply, and even there is no supply of goods, which greatly restricts the normal production of concrete.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A concrete containing natural zeolite powder, comprising the following components in mass fraction:

[0032] 54 parts of light sand;

[0033] 30 parts of light aggregate;

[0034] 38 parts of cement;

[0035] 9 parts of zeolite powder;

[0036] 0.5 parts of water reducing agent;

[0037] 18 parts of water.

[0038] Further, the light sand is waste glass slag, and the particle size of the light sand is 16-20 mesh.

[0039] Further, the lightweight aggregate is one or more of pumice, volcanic slag, fly ash ceramsite and expanded slag beads, and the particle size of the lightweight aggregate is 40 mesh to 60 mesh.

[0040] Further, the particle size of the zeolite powder is 200-250 mesh.

[0041] Further, the water reducer is a polycarboxylate water reducer.

[0042] A preparation method for concrete containing natural zeolite powder, comprising the following steps:

[0043] S1 Add light sand, light aggregate, cement and zeolite powder into the mixer, start the mix...

Embodiment 2

[0050] A concrete containing natural zeolite powder, comprising the following components in mass fraction:

[0051] 81 parts of light sand;

[0052] 56 parts of light aggregate;

[0053] 60 parts of cement;

[0054] 14 parts of zeolite powder;

[0055] 2 parts of water reducing agent;

[0056] 28 parts of water.

[0057] Further, the light sand is waste glass slag, and the particle size of the light sand is 16-20 mesh.

[0058] Further, the lightweight aggregate is one or more of pumice, volcanic slag, fly ash ceramsite and expanded slag beads, and the particle size of the lightweight aggregate is 40 mesh to 60 mesh.

[0059] Further, the particle size of the zeolite powder is 200-250 mesh.

[0060] Further, the water reducer is a naphthalene-based water reducer.

[0061] A preparation method for concrete containing natural zeolite powder, comprising the following steps:

[0062] S1 Add light sand, light aggregate, cement and zeolite powder into the mixer, start the mi...

Embodiment 3

[0069] A concrete containing natural zeolite powder, comprising the following components in mass fraction:

[0070] 70 parts of light sand;

[0071] 42 parts of light aggregate;

[0072] 49 parts of cement;

[0073] 12 parts of zeolite powder;

[0074] 1.2 parts of water reducing agent;

[0075] 23 parts of water.

[0076] Further, the light sand is waste glass slag, and the particle size of the light sand is 16-20 mesh.

[0077] Further, the lightweight aggregate is one or more of pumice, volcanic slag, fly ash ceramsite and expanded slag beads, and the particle size of the lightweight aggregate is 40 mesh to 60 mesh.

[0078] Further, the particle size of the zeolite powder is 200-250 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of concrete preparation, in particular to concrete containing natural zeolite powder. The concrete is prepared from the following components in parts by mass: 54-81 parts of lightweight sand, 30-56 parts of lightweight aggregates, 38-60 parts of cement, 9-14 parts of zeolite powder, 0.5-2 parts of a water reducer, and 18-28 parts of water. A preparationmethod comprises the following steps: S1, adding lightweight sand, lightweight aggregates, cement and zeolite powder into a stirrer, starting the stirrer to obtain a material mixture; and S2, addingwater and water reducer into the material mixture, continuously stirring for a certain period of time to obtain the concrete containing the natural zeolite powder. The concrete provided by the invention can effectively improve water-retaining property of the concrete, improves viscosity of the concrete, reduces gradual loss of the concrete, and meanwhile guarantees good pumpability performance ofthe concrete, boosts production efficiency, and also effectively relieves dead load, and guarantees structure safety.

Description

technical field [0001] The invention relates to the technical field of concrete preparation, in particular to a concrete containing natural zeolite powder and a preparation method thereof. Background technique [0002] Lightweight aggregate concrete has strict requirements on raw materials, mix ratio and mixing process, and it is difficult to guarantee the stability of its working performance. Severe separation of bones, excessive loss over time, etc. Adding appropriate amount of zeolite powder under the same mix ratio, and properly changing the mixing process of concrete can effectively improve the working performance of concrete and meet various technical requirements. With the vigorous development of the construction market, the supply of waste slag admixtures such as fly ash, mineral powder, and silica fume is in short supply, and there is even no supply of goods, which greatly restricts the normal production of concrete. [0003] Therefore, we propose a concrete conta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B18/16C04B14/02C04B14/14C04B18/08C04B18/141C04B14/047C04B2103/302
Inventor 单加健
Owner 广西建宏水泥制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com