A method for making block seamless floor tiles

A technology of seamless paving and production methods, applied in the processing of building materials, construction, building construction, etc., can solve the problems of limited use range, many construction personnel, low efficiency, etc., and achieve strong integrity and high flexural strength High and applicable effect

Active Publication Date: 2021-03-16
宿州典跃新型建筑材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many on-site construction personnel, many procedures, and low efficiency. The scope of use is greatly restricted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for making blocky seamless floor tiles, comprising the following steps:

[0030] (1) Production of block paving floor tiles:

[0031] ①Weigh each raw material according to the following weight percentage: 20% of quartz stone with a particle size of 3-5mm, 26% of quartz stone with a particle size of 1-3mm, 26.5% of quartz stone with a particle size of 0.05-1mm, 18% of 525 white cement %, water-based bisphenol A epoxy resin emulsion and amine water-based epoxy curing agent 8.2%, water reducer 0.05%, dispersant 0.05%, defoamer 0.05%, pigment 1.15%.

[0032] The solid content of the water-based bisphenol A epoxy resin emulsion is 82.5%; the ratio of the water-based bisphenol A epoxy resin emulsion to the amine water-based epoxy curing agent is 1:1.3.

[0033] ② Mix the raw materials to prepare the mixture, which specifically includes the following steps:

[0034] A. Mix sandstone with different particle sizes (quartz stone with a particle size of 3-5mm, quartz st...

Embodiment 2

[0043] A method for making blocky seamless floor tiles, comprising the following steps:

[0044] (1) Production of block paving floor tiles:

[0045] ①Weigh each raw material according to the following weight percentages: 20% of marble with a particle size of 3-5mm, 26% of marble with a particle size of 1-3mm, 26.5% of marble with a particle size of 0.05-1mm, 18% of 525 white cement, water-based Bisphenol A type epoxy resin emulsion and amine water-based epoxy curing agent 8.2%, water reducer 0.05%, dispersant 0.05%, defoamer 0.05%, pigment 1.15%.

[0046] The solid content of the water-based bisphenol A epoxy resin emulsion is 78%; the ratio of the water-based bisphenol A epoxy resin emulsion to the amine water-based epoxy curing agent is 1:1.3.

[0047] 2. each raw material is mixed to prepare compound, and concrete method is with embodiment 1.

[0048] ③Fill the mixture into the mold, then place it in a press for pressurization, demould, and make a blocky floor tile embry...

Embodiment 3

[0054] A method for making blocky seamless floor tiles, comprising the following steps:

[0055] (1) Production of block paving floor tiles:

[0056]①Weigh each raw material according to the following weight percentages: 20% of granite with a particle size of 3-5mm, 25% of granite with a particle size of 1-3mm, 26% of granite with a particle size of 0.05-1mm, 18% of 525 white cement, water-based Bisphenol A type epoxy resin emulsion and amine water-based epoxy curing agent 10%, water reducer 0.1%, dispersant 0.1%, defoamer 0.1%, pigment 0.7%.

[0057] The solid content of the water-based bisphenol A epoxy resin emulsion is 80%; the ratio of the water-based bisphenol A epoxy resin emulsion to the amine water-based epoxy curing agent is 1:1.3.

[0058] 2. each raw material is mixed to prepare compound, and concrete method is with embodiment 1.

[0059] ③Fill the mixture into the mould, then put it in the press for pressure treatment, demould, and make a blocky floor tile embry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method for bulk seamless paved floor tiles. The manufacturing method comprises the following steps: (1) manufacturing bulk paved floor tiles: weighing raw materials: dinas, 525 white cement, a water-borne epoxy resin emulsion, a water-borne epoxy curing agent, a water reducer, a dispersant, a defoamer and pigments; uniformly mixing the raw materials to obtaina mixed material, filling a mold with the mixed material, pressuring the mold and demolding the mold; processing the edges of floor tile blanks with a tooth-shaped processing tool, wherein aggregatesare exposed out of the edges to form tooth-shaped edges to obtain the bulk paved floor tiles; and (2) paving the seamless paved floor tiles: paving the floor tiles; filling the seams after maintenance, wherein the seam filling material is as same as the mixed material in the step (1); compacting the floor tiles after filling the seams; and curing, grinding and polishing the floor tiles. By combining the advantages of bulk paving and field paving, the prepared seamless paved floor tiles are high in integrity, efficient, environment-friendly, seamless and arbitrary in color. Cement is modifiedby the water-borne epoxy resin, so that the performance of the paved floor tiles is better.

Description

technical field [0001] The invention relates to the technical field of floor tiles, in particular to a method for manufacturing block-shaped seamless floor tiles. Background technique [0002] The ground decoration materials are usually block paving and on-site paving. Block paving is efficient, environmentally friendly and widely applicable. However, the gaps caused by block paving affect the designer's overall design concept, and it is easy to hide dirt, and the color is also restricted. Although the on-site paving ground can be seamless, it can well express the designer's design concept, and the color can also be played arbitrarily. However, there are many on-site construction personnel, many procedures, and low efficiency, which greatly limits the scope of use. Contents of the invention [0003] The purpose of the present invention is to provide a method for making block seamless paving floor tiles, which combines the advantages of block paving and on-site paving to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04E04G21/00
CPCC04B28/04C04B2201/50C04B2201/52E04G21/00C04B14/06C04B24/281C04B24/121C04B2103/302C04B2103/408C04B2103/50C04B2103/54C04B14/285C04B14/048
Inventor 郭君建汝宗林
Owner 宿州典跃新型建筑材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com