Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Bamboo wood fiber negative ion decorative line batten

A decorative line board, bamboo wood fiber technology, applied in the field of decorative materials, can solve the problems of poor interface compatibility, poor wear resistance, poor environmental performance, etc., to achieve good impact resistance, long service life, and reduce harmful substances The effect of the release

Active Publication Date: 2019-03-15
雄县国建塑胶制品有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention proposes a bamboo and wood fiber negative ion decorative line board, which solves the problems of poor strength, toughness, thermal stability, wear resistance, etc. and poor environmental performance caused by the poor interface compatibility of wood-plastic composite materials in the prior art. technical issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo wood fiber negative ion decorative line batten
  • Bamboo wood fiber negative ion decorative line batten
  • Bamboo wood fiber negative ion decorative line batten

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of bamboo wood fiber negative ion decorative line board is made up of the following components by weight:

[0032] 60 parts of polyvinyl chloride resin, 40 parts of calcium carbonate, 30 parts of bamboo fiber wood powder, 10 parts of HL-100, 3 parts of foaming agent, 5 parts of calcium zinc stabilizer, 3 parts of calcium stearate, 2 parts of stearic acid , 0.5 parts of paraffin wax, 0.5 parts of oxidized polyethylene wax, 2 parts of modifier, 1 part of tetraphenylethylene, 1 part of polyvinylpyrrolidone, 1 part of polydimethylsiloxane, 1 part of polyethylene oxide, octaphenyl octane 5 parts of silsesquioxane, 3 parts of propylene glycol, 1 part of polyethylene glycol, 1 part of tourmaline ore powder, wherein the particle size of bamboo fiber wood powder is 100-200 mesh, and the modifier is ACR and CPE quality A mixture with a ratio of 1:1.

[0033] Its preparation method comprises the following steps:

[0034] S1, according to the formula of above-mentioned a k...

Embodiment 2

[0040] A kind of bamboo wood fiber negative ion decorative line board is made up of the following components by weight:

[0041] 65 parts of polyvinyl chloride resin, 45 parts of calcium carbonate, 35 parts of bamboo fiber wood powder, 13 parts of HL-100, 4 parts of foaming agent, 8 parts of calcium zinc stabilizer, 4 parts of calcium stearate, 3 parts of stearic acid , 0.7 parts of paraffin, 0.8 parts of oxidized polyethylene wax, 3 parts of modifiers, 2 parts of tetraphenylethylene, 1.5 parts of polyvinylpyrrolidone, 1.5 parts of polydimethylsiloxane, 1.5 parts of polyethylene oxide, octaphenyl octane 7 parts of silsesquioxane, 4 parts of propylene glycol, 2 parts of polyethylene glycol, 2.5 parts of tourmaline ore powder, wherein the particle size of bamboo fiber wood powder is 100-200 mesh, and the modifier is ACR and CPE quality A mixture with a ratio of 1:1.

[0042] Its preparation method is with embodiment 1.

Embodiment 3

[0044] A kind of bamboo wood fiber negative ion decorative line board is made up of the following components by weight:

[0045] 70 parts of polyvinyl chloride resin, 50 parts of calcium carbonate, 40 parts of bamboo fiber wood powder, 15 parts of HL-100, 5 parts of foaming agent, 10 parts of calcium zinc stabilizer, 5 parts of calcium stearate, 4 parts of stearic acid , 1 part of paraffin wax, 1 part of oxidized polyethylene wax, 4 parts of modifier, 3 parts of tetraphenylethylene, 2 parts of polyvinylpyrrolidone, 2 parts of polydimethylsiloxane, 2 parts of polyethylene oxide, octaphenyl octasil 10 parts of sesquioxane, 5 parts of propylene glycol, 3 parts of polyethylene glycol, 4 parts of tourmaline ore powder, wherein the particle size of bamboo fiber wood powder is 100-200 mesh, and the modifier is the mass ratio of ACR and CPE for a 1:1 mixture.

[0046] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of decorative materials, and proposes a bamboo wood fiber negative ion decorative line batten, comprising the following components in parts by weight: 60-70 parts of polyvinyl chloride resin, 40-50 parts of calcium carbonate, 30-40 parts of bamboo fiber wood powder, 10-15 parts of a regulator, 3-5 parts of a foaming agent, 5-10 parts of a calcium-zinc stabilizer, 3-5 parts of calcium stearate, 2-4 parts of stearic acid, 0.5-1 part of paraffin, 0.5-1 part of oxidized polyethylene wax, 2-4 parts of a modifier, 1-3 parts of a fluorescent toner, 1-2 parts of polyvinyl pyrrolidone, 1-2 parts of polydimethylsiloxane, 1-2 parts of polyoxyethylene, 5-10 parts of octaphenylsilsesquioxane, 3-5 parts of propylene glycol, 1-3 parts of polyethylene glycol, and 1-4 parts of tourmaline ore powder. The bamboo wood fiber negative ion decorative line batten solves the technical problems of poor properties of strength, toughness, thermal stability abrasion resistance and the like caused by poor interfacial compatibility of the wood-plastic composite material in the prior art, and poor environment-friendliness.

Description

technical field [0001] The invention belongs to the technical field of decorative materials and relates to a bamboo wood fiber anion decorative line board. Background technique [0002] With the improvement of people's living standards, people pay more and more attention to the quality of life. At the same time, people have higher and higher requirements for the decoration quality of the living environment. Whether the decoration materials are environmentally friendly or not affects the health of users. At the same time, with the pace of life Accelerating, when using decorative materials, whether harmful gases, harmful ions or harmful radiation will be produced has become a concern of consumers. Therefore, environmental protection, pollution-free and easy installation have become the research direction of new environmentally friendly materials. [0003] Wood-plastic composite material is a new type of decorative material. It is made of polyvinyl chloride resin and wood powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L91/06C08L83/04C08L39/06C08L71/02C08K13/02C08K5/053C08K5/098C08K5/09C08J9/04
CPCC08J9/0023C08J9/0061C08J9/0066C08J9/0085C08J9/0095C08J9/04C08J2327/06C08J2439/06C08J2471/02C08J2483/04C08J2491/06C08J2497/02
Inventor 国建
Owner 雄县国建塑胶制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com