Highly oriented cellulose airgel and its preparation method

A technology of cellulose aerogel and cellulose hydrogel, which is applied in the field of highly oriented cellulose aerogel and its preparation, can solve the problems of inability to prepare cellulose aerogel, and achieves easy large-scale industrial production , Wide application prospects, low cost effect

Active Publication Date: 2021-11-23
WUYI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The first object of the present invention is to provide a preparation method of highly oriented cellulose airgel, which has the advantages of simple operation and low cost, and the highly oriented cellulose aerogel prepared according to this method solves the problem of traditional preparation. The technical problem that the method cannot prepare highly oriented nanofiber structure and transparent cellulose airgel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly oriented cellulose airgel and its preparation method
  • Highly oriented cellulose airgel and its preparation method
  • Highly oriented cellulose airgel and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] According to a first aspect of the present invention, the present invention provides a method for preparing a highly oriented cellulose airgel, comprising the following steps:

[0032] (a) adding a chemical crosslinking agent to the cellulose solution for chemical crosslinking to obtain a chemically crosslinked cellulose hydrogel;

[0033] (b) performing pre-stretching and alcohol solution replacement on the chemically cross-linked cellulose hydrogel, and drying to obtain a highly oriented cellulose airgel material.

[0034] The preparation method of the highly oriented cellulose airgel provided by the present invention is simple in operation, low in cost, and easy for large-scale industrial production. Alcohol coagulation bath is used to freeze the orientation, and at the same time, the hydrogel is replaced with alcohol gel, and the orientation of the hydrogel is fixed. Carried out together with solvent replacement, the replacement time and the amount of alcohol are gr...

Embodiment 1

[0090] This embodiment provides a highly oriented cellulose airgel, the preparation method of which comprises the following steps:

[0091] (a) Control the experimental temperature to be lower than the cellulose gelation temperature, add epichlorohydrin to the cellulose solution with a mass fraction of 4wt%, wherein the mass ratio of epichlorohydrin to cellulose is 3.55:4, and stir rapidly 3h, centrifugal defoaming, standing at 0°C for 6h to obtain chemically cross-linked cellulose hydrogel;

[0092] (b) Pre-stretching the chemically cross-linked cellulose hydrogel obtained in step (a), wherein the deformation of the pre-stretching is 200%, and then placing the cellulose hydrogel in a 95% mass fraction In the ethanol solution, the ethanol solution was replaced every 3 hours at -5°C. After three replacements, the above-mentioned alcohol gel was placed in a supercritical dryer for supercritical drying to obtain a highly oriented cellulose airgel material.

Embodiment 2

[0094] This example provides a highly oriented cellulose airgel. The difference between the preparation method of this example and Example 1 is that the pre-stretching deformation is 5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides a highly oriented cellulose airgel and a preparation method thereof, and relates to the field of polymer functional materials. The preparation method of the highly oriented cellulose aerogel comprises the following steps: (a) adding Chemical cross-linking agent, chemical cross-linking, to obtain chemical cross-linked cellulose hydrogel; (b) pre-stretching and alcohol solution replacement of chemical cross-linked cellulose hydrogel, drying, to obtain highly oriented cellulose airgel The material solves the technical problem that the traditional preparation method cannot prepare highly oriented nanofiber structure and transparent cellulose airgel. The preparation method of the highly oriented cellulose airgel provided by the invention uses an alcohol coagulation bath to freeze the orientation, and at the same time The replacement of hydrogel with alcohol gel greatly reduces the replacement time and alcohol consumption, and improves the preparation efficiency of airgel.

Description

technical field [0001] The invention relates to the field of polymer functional materials, in particular to a highly oriented cellulose airgel and a preparation method thereof. Background technique [0002] At present, there are two main methods for the preparation of cellulose aerogels: the first is to prepare high-strength cellulose hydrogels based on chemical and physical double cross-linking strategies, and finally obtained by supercritical drying; the second is to use cellulose nanofibers. Solutions were prepared by freeze-drying. In addition, there are some functional cellulose aerogels (superhydrophobicity, oil absorption, magnetic + oil absorption, dye adsorption, heat insulation, antibacterial, etc.), which are prepared by modifying cellulose aerogels. However, the structure of each of the above-mentioned cellulose aerogels is uniform and isotropic, and none of the preparation methods can prepare transparent cellulose aerogel materials with a highly oriented nanofi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08J3/24C08J3/00C08L1/02
CPCC08J3/00C08J3/24C08J9/28C08J2301/02
Inventor 叶冬冬
Owner WUYI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com