Composite material for high-performance foot pads, and preparation method thereof

A composite material, high-performance technology, applied in the field of material manufacturing, can solve the problems of wear resistance, corrosion resistance, pollution resistance, environmental protection performance is not perfect and so on

Inactive Publication Date: 2019-04-02
HIGHER TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the disadvantages of wear resistance, corrosion resistance, pollution resistance, and environmental protection in the prior art, and provides a composite material for high-performance foot pads and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A composite material for high-performance foot pads. The raw materials include the following components in parts by weight: PVC resin SG-550-60 parts, DOP 50-60 kg, stearic acid 0.5-1 part, toner 2-5 parts 30-40 parts of filler, 7-12 parts of oxidized polyethylene wax, 2-6 parts of antimony trioxide, 10-18 parts of plasticizer, 1-3 parts of low-temperature resistance modifier, JUST-5100 surface resistance 15-20 parts of dirt agent. In the present embodiment, the raw materials include the following components in parts by weight: 550 parts of PVC resin SG-50 kg, 0.5 parts of stearic acid, 2 parts of toner, 30 parts of filler, 7 parts of oxidized polyethylene wax, 2 parts of antimony trioxide, 10 parts of plasticizer, 1 part of low temperature resistance modifier, 15 parts of JUST-5100 surface antifouling agent.

[0024] The filler includes heavy calcium carbonate and talcum powder, the weight ratio of heavy calcium carbonate and talcum powder is 3:1-1:1, and the particle...

Embodiment 2

[0029] A composite material for high-performance foot pads. The raw materials include the following components in parts by weight: PVC resin SG-550-60 parts, DOP 50-60 kg, stearic acid 0.5-1 part, toner 2-5 parts 30-40 parts of filler, 7-12 parts of oxidized polyethylene wax, 2-6 parts of antimony trioxide, 10-18 parts of plasticizer, 1-3 parts of low-temperature resistance modifier, JUST-5100 surface resistance 15-20 parts of dirt agent. In the present embodiment, the raw materials include the following components in parts by weight: 55 parts of PVC resin SG-55 kg, 0.7 parts of stearic acid, 3.5 parts of toner, 35 parts of filler, 10 parts of oxidized polyethylene wax, 4 parts of antimony trioxide, 14 parts of plasticizer, 2 parts of low temperature resistance modifier, 17 parts of JUST-5100 surface antifouling agent.

[0030] The filler includes heavy calcium carbonate and talcum powder, the weight ratio of heavy calcium carbonate and talcum powder is 3:1-1:1, and the parti...

Embodiment 3

[0035] A composite material for high-performance foot pads. The raw materials include the following components in parts by weight: PVC resin SG-550-60 parts, DOP 50-60 kg, stearic acid 0.5-1 part, toner 2-5 parts 30-40 parts of filler, 7-12 parts of oxidized polyethylene wax, 2-6 parts of antimony trioxide, 10-18 parts of plasticizer, 1-3 parts of low-temperature resistance modifier, JUST-5100 surface resistance 15-20 parts of dirt agent. In the present embodiment, in parts by weight, the raw materials include the following components: 60 parts of PVC resin SG-560 kg, 1 part of stearic acid, 2 to 5 parts of toner, 40 parts of filler, 12 parts of oxidized polyethylene wax 6 parts, 6 parts of antimony trioxide, 10-18 parts of plasticizer, 3 parts of low temperature resistance modifier, 20 parts of JUST-5100 surface antifouling agent.

[0036] The filler includes heavy calcium carbonate and talcum powder, the weight ratio of heavy calcium carbonate and talcum powder is 3:1-1:1, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Elastic modulusaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of material manufacturing, and discloses a composite material for high-performance foot pads, and a preparation method thereof, wherein the raw materials comprise, by weight, 50-60 parts of a PVC resin SG-5, 50-60 parts of DOP, 0.5-1 part of stearic acid, 2-5 parts of toner, 30-40 parts of a filler, 7-12 parts of oxidized polyethylene wax, 2-6 parts of diantimonytrioxide, 10-18 parts of a plasticizer, 1-3 parts of a low-temperature-resistant modifier, and 15-20 parts of a JUST-5100 surface antifouling agent. The preparation method comprises: adding the raw materials into a twin-screw extruder, extruding, and granulating to prepare the composite material. According to the present invention, the added PVC raw material and the main auxiliary materials are treated by the technical means so as to meet the environmental protection standards, and the foot pad made by the process technology has advantages of wear resistance, corrosion resistance, fouling resistance, environmental protection and the like.

Description

technical field [0001] The invention relates to the field of material manufacturing, in particular to a composite material for high-performance foot pads and a preparation method thereof. Background technique [0002] Functional and environmentally friendly floor mats are a research and development trend following the traditional floor mats to meet the needs of market development. The floor mats made of water-collecting, corrosion-resistant, and stain-resistant materials start with the raw materials and the appearance of the product, giving the floor mats new functions. Domestically, there have been many achievements in the research and development of polyvinyl chloride-based materials, mainly including anti-ultraviolet, anti-corrosion, anti-pollution and so on. Anti-corrosion and stain-resistant floor mats are one of the core technical indicators of automobile floor mats, and are also one of the focuses of great attention from countries, industries and consumers in the wor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/30C08K13/02C08K5/09C08K3/22C08K5/12
CPCC08L27/06C08L23/30C08K13/02C08K5/09C08K3/2279C08K5/12
Inventor 许斌
Owner HIGHER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com