Pediatric wound face anti-infective dressing
A wound surface and anti-infection technology, applied in the field of medical supplies, can solve the problems of inability to provide a safe and sterile body surface contact environment during the wound recovery process, lack of anti-infection and antibacterial, increase children's pain, etc., and achieve preparation costs Inexpensive, significant anti-infection effect, low-equipment-dependent effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] An anti-infection dressing for pediatric wounds, prepared by the following preparation method:
[0031] Ⅰ Polyprezinc modified hyaluronic acid: Add 1kg polyprezinc, 3kg hyaluronic acid, 0.3kg of 2-ethoxy-1-ethoxycarbonyl-1,2-dihydroquinoline into 15kg of tetrahydrofuran, and then add Stir and react at 50°C for 20 hours, then remove the solvent by rotary evaporation, wash with ethanol for 3 times, remove the ethanol by rotary evaporation, and finally place it in a vacuum drying oven at 80°C to dry to constant weight to obtain polypurizin modified hyaluronic acid;
[0032] II Preparation of chitosan modified by quaternary ammonium salt 15: Add 3kg of chitosan and 151kg of quaternary ammonium salt to 10kg of dimethyl sulfoxide, stir and react at 60°C, then precipitate in water, and wash the product 4 times with ethanol , and then dried in a vacuum oven at 75°C to constant weight;
[0033] Ⅲ Functionalized quaternary ammonium salt 15 modified chitosan: Add 1 kg of quaterna...
Embodiment 2
[0039] An anti-infection dressing for pediatric wounds, prepared by the following preparation method:
[0040] ⅠPolyprezinc modified hyaluronic acid: Add 1kg polyprezinc, 3.5kg hyaluronic acid, 0.35kg of 2-ethoxy-1-ethoxycarbonyl-1,2-dihydroquinoline to 17kg of acetone, and then Stir the reaction at 52°C for 21 hours, then remove the solvent by rotary evaporation, wash with ethanol for 4 times, remove the ethanol by rotary evaporation, and finally place it in a vacuum drying oven at 83°C to dry to constant weight to obtain polypurizin modified hyaluronic acid;
[0041] Ⅱ Preparation of chitosan modified by quaternary ammonium salt 15: Add 3.5kg of chitosan and 151kg of quaternary ammonium salt to 11.5kg of N,N-dimethylformamide, stir and react at 65°C, and then precipitate in water , and the product was washed with ethanol for 5 times, and then dried in a vacuum oven at 77°C to constant weight;
[0042] Ⅲ functionalized quaternary ammonium salt 15 modified chitosan: add 1 kg ...
Embodiment 3
[0048] An anti-infection dressing for pediatric wounds, prepared by the following preparation method:
[0049] Ⅰ Polyprezinc modified hyaluronic acid: Add 1kg polyprezinc, 4kg hyaluronic acid, 0.4kg of 2-ethoxy-1-ethoxycarbonyl-1,2-dihydroquinoline to 17kg of acetonitrile, and then add Stir and react at 55°C for 22 hours, then remove the solvent by rotary evaporation, wash with ethanol for 4 times, remove the ethanol by rotary evaporation, and finally place it in a vacuum drying oven at 85°C to dry to constant weight to obtain polypurizin modified hyaluronic acid;
[0050] II Preparation of chitosan modified by quaternary ammonium salt 15: Add 4kg of chitosan and 151kg of quaternary ammonium salt to 12.5kg of N-methylpyrrolidone, stir and react at 70°C, then precipitate in water, and wash the product with ethanol 5 times, and then dried in a vacuum oven at 79°C to constant weight;
[0051] Ⅲ Functionalized quaternary ammonium salt 15 modified chitosan: add 1 kg of quaternary ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com