A kind of slate ceramic tile with diamond luster effect and preparation method thereof

A technology for ceramic tiles and diamonds, applied in the field of ceramic tiles, can solve problems such as affecting the decorative effect of the surface pattern of ceramic tiles, and achieve the effect of enhancing decoration and obvious effect.

Active Publication Date: 2022-07-12
DONGGUAN CITY WONDERFUL CERAMICS IND PARK +3
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) If the mica sheet is used to produce luster, its flash point itself has a darker black color, which will affect the decorative effect of the surface pattern of the ceramic tile for light-colored or bright-colored products;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of slate ceramic tile with diamond luster effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] like figure 1 As shown, a slate ceramic tile with diamond luster effect includes a green tile 1, a bottom glaze layer 2, a pattern layer 3, a transparent glaze layer 4 and a diamond glitter dry grain glaze layer 5 sequentially compounded from bottom to top.

[0034] A kind of preparation method of the slate ceramic tile with diamond luster effect as mentioned above, comprises the steps:

[0035] (1) pressing the billet into a green brick 1, and drying it in a roller kiln;

[0036] (2) apply primer glaze on the surface of described embryo brick 1;

[0037] (3) printing a slate-like pattern on the surface of the base glaze by 3D printing to form a pattern layer 3;

[0038] (4) applying transparent glaze on the surface of the pattern layer 3;

[0039] (5) applying diamond flash dry grain glaze on the surface of the transparent glaze, the diamond dry grain glaze includes the following raw materials by weight: 65 parts of methyl water, 15 parts of dry grains and 12 parts of...

Embodiment 2

[0050] like figure 1 As shown, a slate ceramic tile with diamond luster effect includes a green tile 1, a bottom glaze layer 2, a pattern layer 3, a transparent glaze layer 4 and a diamond glitter dry grain glaze layer 5 sequentially compounded from bottom to top.

[0051] A kind of preparation method of the slate ceramic tile with diamond luster effect as above, comprises the steps:

[0052] (1) pressing the billet into a green brick 1, and drying it in a roller kiln;

[0053] (2) apply primer glaze on the surface of described embryo brick 1;

[0054] (3) printing a slate-like pattern on the surface of the base glaze by 3D printing to form a pattern layer 3;

[0055] (4) applying transparent glaze on the surface of the pattern layer 3;

[0056] (5) apply diamond flash dry grain glaze on the surface of the transparent glaze, and the diamond dry grain glaze includes the following raw materials in parts by weight: 60 parts of methyl water, 10 parts of dry grains and 8 parts o...

Embodiment 3

[0065] like figure 1 As shown, a slate ceramic tile with diamond luster effect includes a green tile 1, a bottom glaze layer 2, a pattern layer 3, a transparent glaze layer 4 and a diamond glitter dry grain glaze layer 5 sequentially compounded from bottom to top.

[0066] A kind of preparation method of the slate ceramic tile with diamond luster effect as above, comprises the steps:

[0067] (1) pressing the billet into a green brick 1, and drying it in a roller kiln;

[0068] (2) apply primer glaze on the surface of described embryo brick 1;

[0069] (3) printing a slate-like pattern on the surface of the base glaze by 3D printing to form a pattern layer 3;

[0070] (4) applying transparent glaze on the surface of the pattern layer 3;

[0071] (5) applying diamond flash dry grain glaze on the surface of the transparent glaze, the diamond dry grain glaze comprises the following raw materials in parts by weight: 70 parts of methyl water, 20 parts of dry grains and 15 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramic tiles, in particular to a slate ceramic tile with diamond luster effect and a preparation method thereof. 3) Printing slate-like patterns (4) Applying transparent glaze; (5) Applying diamond flash dry grain glaze; (6) Firing the green brick to obtain the slate ceramic tile with diamond luster effect. In the present invention, after applying primer glaze on the blank surfaces of various properties, combined with the later slate-like pattern, transparent glaze and dry-grain glaze with strong glitter effect, the plate with diamond glitter particles and cleavage luster is manufactured. Rock ceramic tiles. When viewed from the side under natural light, you can see that there are obvious fine granular glittering particles on the surface of the ceramic tile, similar to the sparkling reflection effect of many very small diamonds; and under the spotlight, this diamond-like reflection light effect is more Obviously, the decorative properties of ceramic tile products are enhanced.

Description

technical field [0001] The invention relates to the technical field of ceramic tiles, in particular to a slate ceramic tile with diamond luster effect and a preparation method thereof. Background technique [0002] In the manufacture of architectural ceramics, the glossiness of various wall and floor tiles has different manifestations, such as matt, matt, satin, high gloss, bright and other glossy effects. Generally, the product's gloss effect is expressed by the overall gloss of the glaze itself. Conventional glazed tile products are mostly matte and glossy surfaces. Polished tiles and fully polished glazed products can achieve high gloss after polishing. It is not the gloss effect reflected by the glaze itself, the gloss of the entire layout tends to be consistent, there will not be much change, and the visual gloss will not have obvious contrast. In addition, a small number of antique ceramic tiles use the flash point process of mica flakes or glossy glaze, and there wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C03C8/16C03C8/14C03C8/20C03C8/04C03C8/02
CPCY02P40/60
Inventor 曹端旭欧志勇盛正强李艳君刘燕燕黄道聪
Owner DONGGUAN CITY WONDERFUL CERAMICS IND PARK