Hydrophilic MQ silicon resin and synthesizing method thereof

A technology of MQ silicone resin and synthesis method, which is applied in the field of organic synthesis, can solve problems such as easy gel generation, difficult control of structure and M/Q value, wide molar mass distribution, etc., and achieve the effect of improving the defoaming effect

Inactive Publication Date: 2019-05-21
湖北新四海化工股份有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The synthesis of MQ silicone resin mainly adopts water glass method and silicate method at present; It is wide and easy to produce gel; compared with the sodium silicate method, the hydrolysis reaction activity of the silicate method is lower and the reaction is milder, so it is beneficial to the control of the reaction and the yield is higher. It is the current MQ silicone resin The main method of synthesis
However, the current literature reports and large-scale production are basically hydrophobic MQ silicone resins, and the literature on water-based or hydrophilic MQ silicone resins is still rare.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophilic MQ silicon resin and synthesizing method thereof
  • Hydrophilic MQ silicon resin and synthesizing method thereof
  • Hydrophilic MQ silicon resin and synthesizing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] S1: To prepare modified alkoxysilane, add 0.55mol of unsaturated polyether and chloroplatinic acid catalyst into a flask, mix well, and heat up to 90°C for reaction. Slowly add 0.5 mol of trimethoxysilane into the flask dropwise, then keep the temperature for 2 hours, and remove the low boilers under reduced pressure to obtain modified alkoxysilane, that is, polyether modified trimethoxysilane.

[0031] In this embodiment, the unsaturated polyether structural formula is C 3 h 5 O-(C 2 h 4O ) m -(C 3 h 6 O) n -CH 3 , where m=0, n=2. The preparation method of the chloroplatinic acid catalyst is as follows: 1 weight part of chloroplatinic acid is dissolved in 10 weight parts of isopropanol to obtain the chloroplatinic acid catalyst. The dosage of chloroplatinic acid catalyst in this embodiment is 5 ppm of the total molar amount of trimethoxysilane and unsaturated polyether.

[0032] S2: Add the modified alkoxysilane obtained in step S1, 200 mL of isopropanol, 2.0...

Embodiment 2

[0035] S1: To prepare modified alkoxysilane, add 4 mol of unsaturated polyether and chloroplatinic acid catalyst into a flask, mix well, and heat up to 100°C for reaction. Slowly add 1 mol of trimethoxysilane into the flask dropwise, then keep the temperature for 1 hour, and remove the low boilers under reduced pressure to obtain modified alkoxysilane, that is, polyether modified trimethoxysilane.

[0036] In this embodiment, the unsaturated polyether structural formula is C 3 h 5 O-(C 2 h 4O ) m -(C 3 h 6 O) n -CH 3 , where m=8, n=5. The preparation method of the chloroplatinic acid catalyst is as follows: 1 weight part of chloroplatinic acid is dissolved in 30 weight parts of ethanol to obtain the chloroplatinic acid catalyst. The dosage of chloroplatinic acid catalyst in this embodiment is 20 ppm of the total molar amount of trimethoxysilane and unsaturated polyether.

[0037] S2: Add the modified alkoxysilane obtained in step S1, 200 mL of ethanol, 4 mol of tetra...

Embodiment 3

[0040] S1: To prepare modified alkoxysilane, add 2 mol of unsaturated polyether and chloroplatinic acid catalyst into a flask, mix well, and heat up to 60°C for reaction. Then slowly drop 2 mol of trimethoxysilane into the flask, and then keep the temperature for 3 hours, and remove the low boilers under reduced pressure to obtain modified alkoxysilane, that is, polyether modified trimethoxysilane.

[0041] In this embodiment, the unsaturated polyether structural formula is C 3 h 5 O-(C 2 h 4O ) m -(C 3 h6 O) n -CH 3 , where m=20, n=0. The preparation method of the chloroplatinic acid catalyst is as follows: 1 weight part of chloroplatinic acid is dissolved in 50 weight parts of tetramethyltetravinyl cyclotetrasiloxane to obtain the chloroplatinic acid catalyst. The dosage of the chloroplatinic acid catalyst in this embodiment is 50 ppm of the total molar amount of trimethoxysilane and unsaturated polyether.

[0042] S2: 400 mL of the mixture of modified alkoxysilane,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of organic synthesis, in particular to a hydrophilic MQ silicon resin and a synthesizing method thereof. The hydrophilic MQ silicon resin can be greatly applied to the fields such as the fields of surfactants, defoaming, and water-based coatings. The hydrophilic MQ silicon resin mainly comprises the following raw materials: 4-24 parts of tetraethoxysilane, 1-4 parts of unsaturated polyether or methyl acrylate, 1-7 parts of hexamethyldisiloxane, 1-4 parts of trimethoxy silane, and 1-2 parts of an acid catalyst, and further comprises a chloroplatinicacid catalyst.

Description

technical field [0001] The invention belongs to the technical field of organic synthesis, in particular to a hydrophilic MQ silicone resin and a synthesis method thereof. Background technique [0002] MQ silicone resin is an organopolysiloxane product with a special structure composed of tetrafunctional siloxane polycondensation chains (i.e. Q groups) and monofunctional siloxane chains (i.e. M groups). Excellent heat resistance, low temperature resistance, film-forming properties, flexibility, water resistance and adhesive properties, mainly used as fillers for silicone pressure-sensitive adhesives, tackifiers and reinforcing fillers for addition-type liquid silicone rubber, and Used in tackifiers, surface treatment agents, release agents, defoamers, anti-sticking agents, brighteners and other additives. The synthesis of MQ silicone resin mainly adopts water glass method and silicate method at present; It is wide and easy to produce gel; compared with the sodium silicate m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/46C08G77/18C08G65/336
Inventor 邵玲龚家全杨帆杨开柱
Owner 湖北新四海化工股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com