Manufacturing method of abrasion-resistant and anti-fracture trolley grate bar

A production method and anti-fracture technology are applied in the field of grate bars for sintering machine trolleys, which can solve the problems of short service life, easy damage and failure of grate bars, etc., and achieve the effects of preventing fracture, reducing sintering cost, and improving production efficiency.

Inactive Publication Date: 2019-05-24
广西威华新材料科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a method for making a wear-resistant and anti-fracture trolley grate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of abrasion-resistant and anti-fracture trolley grate bar
  • Manufacturing method of abrasion-resistant and anti-fracture trolley grate bar
  • Manufacturing method of abrasion-resistant and anti-fracture trolley grate bar

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] The trolley grate bars produced in Example 1 and Example 2 are as follows Figure 1-Figure 3 As shown, it includes the grate bar body. The working surface 1 of the grate bar body is composed of an upper layer and a lower layer. The upper layer is high chromium wear-resistant white cast iron 1-1, and the lower layer is low alloy cast steel 1-2. Left and right supporting legs 3 and 4 are provided on both sides of the lower end of the working surface 1 of the grate body. The bottoms of the left supporting foot 3 and the right supporting foot 4 are bent outwards. The upper two sides of the working surface 1 of the grate body are respectively A left limit block 5 and a right limit block 6 are sleeved, and the upper middle section of the working surface 1 of the grate bar body is provided with two limit nails 2 at the same height as the limit block.

[0025] The trolley grate made by this production method has been inspected in Liuzhou Iron and Steel (Group) Co., Ltd. sintering ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of an abrasion-resistant and anti-fracture trolley grate bar, and belongs to the technical field of furnace grate bars for sintering machine trolleys. The manufacturing method of the abrasion-resistant and anti-fracture trolley grate bar comprises the steps that low alloy cast steel and high chromium abrasion-resistant white mouth cast iron are separately poured into two electric furnaces to be smelted to control the temperature and time of the two electric furnaces, after smelted, low alloy cast molten steel is firstly poured into a casting mold,when the low alloy cast molten steel naturally cools to the critical temperature, namely, when the low alloy cast molten steel reaches a solid phase line, and then the high chromium abrasion-resistant white mouth casting molten iron is cast; and the weight ratio of the low alloy cast molten steel and the high chromium abrasion-resistant white mouth casting molten iron is controlled, and after thelow alloy cast molten steel and the high chromium abrasion-resistant white mouth casting molten iron cast, and then tempering, normalizing heat treatment are carried out. Compared with the prior art,the trolley grate bar prepared by the manufacturing method of the abrasion-resistant and anti-fracture trolley grate bar is tested in a 2#360m<2> sintering machine of a sintering plant for more thantwo years, the service life of the trolley grate bar is more than 4 times of the service life of an original monometallic high chromium cast iron alloy, no phenomenon of excessive burning loss and fracture collapse and scattered of the grate bar exists in more than two years of use, the sintering cost is greatly reduced, and the production efficiency is improved.

Description

technical field [0001] The invention relates to the technical field of grate bars for sintering machine trolleys, in particular to a method for manufacturing grate bars for wear-resistant and fracture-resistant trolleys. Background technique [0002] In the smelting and sintering industry, the grate bar is the key component of the sintering machine trolley. The maximum temperature reaches over 900°C during operation, and it is rapidly cooled on the sintering return lane. It is subjected to high temperature oxidation and gas corrosion during work, and the surface oxidizes and falls off. , the gap between the grate bars becomes larger, and when the gap between the grate bars exceeds 8mm, the grate bars will fail. The initial stage of oxidation is accompanied by the growth process, the gap between the grate bars becomes smaller, and the ventilation is poor, which also leads to the failure of the grate bars. Especially when the sintering machine is sintered without bottom mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D19/16C21D1/28C21D5/04
Inventor 陈文桂李红勇保五生
Owner 广西威华新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap