A glass fiber net reinforced bamboo fiber molded slide plate and its preparation method

A technology of glass fiber mesh and glass fiber yarn, which is applied in the field of glass fiber mesh reinforced bamboo fiber molded skateboard and its preparation, and can solve the problems of poor bonding performance of glass fiber mesh reinforced skateboard, poor interlayer bonding performance, and uneven appearance of the skateboard, etc. , to achieve the effect of simple and convenient blank assembly, good gluing performance and short hot pressing forming time

Active Publication Date: 2020-12-08
INT CENT FOR BAMBOO & RATTAN
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the uneven appearance of the skateboard and the diversification of the appearance design, the processing technology is complicated, and most of the bamboo skateboards are assembled in the same direction along the grain, the structure is simple, the mechanical properties in the length direction are good, and the longitudinal bending strength is 80MPa~ 95MPa, the mechanical properties in the width direction are poor, the transverse bending strength is 20MPa~40MPa, the bonding performance of the glass fiber mesh reinforced slide plate is poor, and the interlayer bonding performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The glass fiber mesh reinforced bamboo fiber molded skateboard of this embodiment is made of bamboo veneer and prepreg arranged between two layers of bamboo veneer, and the prepreg is made of preform impregnated with adhesive and then covered with ring. It is made of epoxy resin film; the preform is obtained by interlacing and stacking three layers of glass fiber mesh and two layers of bamboo fiber.

[0026] The present embodiment provides the method for preparing above-mentioned glass fiber net reinforced bamboo fiber molded slide plate, comprises the following steps:

[0027] Step 1, preparation of bamboo fiber: the bamboo material is sequentially cut, knotted, split, rolled and broken up to obtain bamboo fiber; the length of the bamboo fiber is 5cm to 15cm;

[0028] Step 2, preparation of bamboo veneer: splicing bamboo strips flat to obtain bamboo veneer; the thickness of the bamboo veneer is 1cm; the width of the bamboo veneer is 30cm;

[0029] Step 3. Preparation ...

Embodiment 2

[0038] The glass fiber mesh reinforced bamboo fiber molded skateboard of this embodiment is made of bamboo veneer and prepreg arranged between two layers of bamboo veneer, and the prepreg is made of preform impregnated with adhesive and then covered with ring. It is made of epoxy resin film; the preform is obtained by interlacing and stacking three layers of glass fiber mesh and two layers of bamboo fiber.

[0039] The present embodiment provides the method for preparing above-mentioned glass fiber net reinforced bamboo fiber molded slide plate, comprises the following steps:

[0040] Step 1, preparation of bamboo fiber: the bamboo material is sequentially cut, knotted, split, rolled and broken up to obtain bamboo fiber; the length of the bamboo fiber is 5cm to 15cm;

[0041] Step 2, preparation of bamboo veneer: splicing bamboo strips flat to obtain bamboo veneer; the thickness of the bamboo veneer is 1.5cm; the width of the bamboo veneer is 30cm;

[0042] Step 3. Preparatio...

Embodiment 3

[0048] The glass fiber mesh reinforced bamboo fiber molded skateboard of this embodiment is made of bamboo veneer and prepreg arranged between two layers of bamboo veneer, and the prepreg is made of preform impregnated with adhesive and then covered with ring. It is made of epoxy resin film; the preform is obtained by stacking 4 layers of glass fiber mesh and 3 layers of bamboo fiber interlaced layer by layer.

[0049] The present embodiment provides the method for preparing above-mentioned glass fiber net reinforced bamboo fiber molded slide plate, comprises the following steps:

[0050] Step 1, preparation of bamboo fiber: the bamboo material is sequentially cut, knotted, split, rolled and broken up to obtain bamboo fiber; the length of the bamboo fiber is 5cm to 15cm;

[0051] Step 2, preparation of bamboo veneer: splicing bamboo strips flat to obtain bamboo veneer; the thickness of the bamboo veneer is 1.5cm; the width of the bamboo veneer is 30cm;

[0052] Step 3. Prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a glass fiber web reinforced bamboo fiber mould pressing sliding plate, which is made of bamboo veneers and prepreg arranged between the two layers of bamboo veneers, and the invention also provides a preparation method, which comprises the following steps of: sorting bamboo fibers, sequentially and crossly paving a glass fiber net and the bamboo fibers from bottom to top toobtain a preformed body, impregnating an adhesive, covering the surface of the preformed body with an epoxy resin adhesive film to obtain the prepreg, assembling the bamboo veneers and the prepreg and carrying out hot pressing molding to obtain the sliding plate. According to the invention, the assembly is simple and convenient; in the hot pressing molding process, after the epoxy resin adhesivefilm on the surface layer of the prepreg is heated, the epoxy resin adhesive can be adhered to the bamboo veneers, so that the bonding strength of the sliding plate is increased; after the hot pressing molding, the epoxy resin adhesive film has elasticity, and the sliding plate is good in shock resistance and fracture resistance; the prepreg is formed by overlapping glass fiber nets and bamboo fibers layer by layer, so that the longitudinal performance and transverse performance of the sliding plate are good; and the prepared sliding plate is light.

Description

technical field [0001] The invention belongs to the technical field of bamboo fiber composite materials, and in particular relates to a glass fiber net reinforced bamboo fiber molded slide plate and a preparation method thereof. Background technique [0002] Canadian maple has good elasticity, moderate hardness, strong stability, not easy to deform, wear-resistant, corrosion-resistant, shock-absorbing, sound-absorbing and other excellent properties, so it is recognized as the best tree species for making skateboards. However, the growth period of Canadian maple is 50-70 years, and the price is relatively expensive, and the strength and elasticity of the skateboard made of cheap birch are lower than that of maple. [0003] With the development of science and technology and the increasing shortage of wood resources, the skateboard with bamboo as the main material has gradually become the mainstream. After years of development, bamboo has gradually become a It has become one o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B9/02B32B9/04B32B17/04C08L63/00C08L97/02C08K7/14C08J5/24
Inventor 王戈张文福程海涛谭玉林顾少华李明鹏
Owner INT CENT FOR BAMBOO & RATTAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products