A polyester ether polyol, polyurethane rigid foam technology, applied in the field of new materials, can solve the problems of use limitation, poor mold release performance, low polyester functionality, etc., achieve strength improvement, reduce thermal conductivity value, intermolecular interaction force-enhancing effect

Active Publication Date: 2019-07-05
WANHUA CHEM NINGBO RONGWEI POLYURETHANE
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the functionality of conventional polyester is too low, and the release performance is poor. Under the current trend of higher and higher requirements for release performance, the use is greatly restricted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gluconic acid initiated polyester ether polyol and application thereof in polyurethane hard foam
  • Gluconic acid initiated polyester ether polyol and application thereof in polyurethane hard foam
  • Gluconic acid initiated polyester ether polyol and application thereof in polyurethane hard foam

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A kind of preparation method of gluconic acid starting polyester ether polyol, the steps are:

[0057] 1) After mixing and dissolving 1176g of 50% mass concentration gluconic acid aqueous solution and 12g of potassium acetate, carry out nitrogen replacement, then heat to 80-90°C, then add 750g of propylene oxide at a flow rate of 750g / h, react for 1.5h, then Raise the temperature to 115°C, then carry out the aging reaction for 1h, and vacuum dehydrate at 110°C for 2h;

[0058] 2), according to the flow rate of 970g / h, add the remaining 970g of propylene oxide, continue to react at 95-105°C for 1h, then raise the temperature to 120°C for another 1h;

[0059] 3) At this time, add 100g water, 30g clay, absorb and decolorize, vacuum dehydrate and degas, filter to obtain gluconic acid starting polyester ether polyol E containing 200ppm potassium ions (existing in the form of potassium acetate), and the hydroxyl value is 460mgKOH / g, functionality is 5.5, viscosity is 35600m...

Embodiment 2

[0061] A kind of preparation method of gluconic acid starting polyester ether polyol, the steps are:

[0062] 1) After mixing and dissolving 840g of 70% mass concentration gluconic acid aqueous solution and 15g of potassium hydroxide, carry out nitrogen replacement, then heat to 90°C, then add 400g of ethylene oxide at a flow rate of 400g / h, react for 1.5h, and then heat up to 115 Then carry out aging reaction at 110°C for 1h, and vacuum dehydration at 110°C for 2h;

[0063] 2) Add the remaining 1480g of propylene oxide according to the flow rate of 800g / h, continue to react at 95-105°C for 1h, then raise the temperature to 120°C for another 1h;

[0064] 3) Add 24 grams of lactic acid and 100 g of water and stir for 0.5 h, then add 40 g of magnesium hexasilicate, absorb and remove potassium ions, vacuum dehydrate and degas, filter, and obtain gluconic acid starting polyester ether polyol F with a hydroxyl value of 410mgKOH / g, functionality 5.4, viscosity 27400mPa.s / 25℃.

Embodiment 3

[0066] A low-density and low-conductivity HFE-254 system polyurethane rigid foam, raw material composition:

[0067] The mass ratio of combined polyether to foaming agent and polyisocyanate is 100:18:140, specifically:

[0068] The composition of the combined polyether is as follows: 91.9 parts of polyether composition, 3 parts of surfactant, 3.1 parts of composite catalyst, and 2.0 parts of distilled water;

[0069] Foaming agent: 12 parts of CP (cyclopentane), 6 parts of HFE-254;

[0070] Polyisocyanate: polymerized MDI Wanhua PM-200 140 parts.

[0071] In combination polyether:

[0072] The polyether composition is composed of 51.9 parts by weight of gluconic acid starting polyester ether polyol E (prepared in Example 1): toluenediamine polyether polyol (OTDA is the starter, and the hydroxyl value is 350-450 mgKOH / g, Functionality 3.0-3.8, that is, polyether polyol B) 30 parts, glycerol polyether polyol (hydroxyl value 192mgKOH / g, functionality 2.3, namely polyether poly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

The invention provides a gluconic acid initiated polyester ether polyol and an application thereof in polyurethane hard foam. Foam prepared by using the gluconic acid initiated polyester ether polyolhas higher strength and stability, and mold release performance is good. According to the preparation method of the gluconic acid initiated polyester ether polyol, gluconic acid represented as in a formula (II) is taken as an initial raw material to carry out an addition reaction with oxidized olefin to prepare the gluconic acid initiated polyester ether polyol, wherein the oxidized olefin is oneor a combination of more selected from compounds represented as in the following formula (III), wherein R in the formula (III) is hydrogen or alkyl C<n>H<2n+1>, n is in equal to from 1 to 4, and preferably n is equal to 1.

Description

technical field [0001] The invention belongs to the field of new materials, and relates to a polyether polyol and rigid polyurethane foam, in particular to a gluconic acid starting polyester ether polyol and its preparation method and application. Background technique [0002] Polyether polyols currently used in the production of polyurethane rigid foam generally use polyether polyols with high functionality and high hydroxyl value to produce sufficient crosslinking and rigidity. The hydroxyl value of rigid polyether polyol is generally 350-650 mgKOH / g, and the average functionality is above 3. Polyethers generally use polyols or amines as initiators. Common four-functional initiators such as pentaerythritol, methyl glucoside, ethylenediamine, toluenediamine, five-functional initiators such as xylitol, diethylenetriamine, six-functional initiators such as Sorbitol, mannitol, eight-functional starters such as sucrose. [0003] Amine polyether polyols have catalytic activit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G65/28C08G18/48C08J9/14
CPCC08G18/482C08G18/4829C08G65/2609C08J9/141C08J9/143C08J2203/146C08J2203/182C08G2110/0025C08G2110/005
Inventor 王林吴晗孙兵
Owner WANHUA CHEM NINGBO RONGWEI POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap