A moisture-crosslinked organic silicon anti-wrinkle and non-ironing finishing solution and its preparation method and application

A technology of non-iron finishing and silicone, which is applied in fiber treatment, plant fiber, and fiber that affects crease behavior, etc. It can solve the problems of reduced hand feeling comfort and reduced strength, so as to ensure safety, environmental protection and whiteness , the effect of convenient operation

Active Publication Date: 2021-10-22
上海氟聚化学产品股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, the anti-wrinkle and non-ironing finishing is made of padding resin, which is baked at high temperature, which is likely to cause a decrease in strength and a decrease in hand comfort.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A moisture-crosslinked organic silicon anti-wrinkle and non-ironing finishing solution and its preparation method and application
  • A moisture-crosslinked organic silicon anti-wrinkle and non-ironing finishing solution and its preparation method and application
  • A moisture-crosslinked organic silicon anti-wrinkle and non-ironing finishing solution and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A moisture-crosslinked silicone anti-wrinkle and non-ironing finishing liquid, each rising tide cross-linked silicone anti-wrinkle and non-ironing finishing liquid is made of the following components:

[0034] Anti-shrinkage and anti-wrinkle resin NBD: 200g / L, catalyst CS-300: 100g / L, penetrant JFC: 2g / L, hydrophilic silicone softener SS 6179-1: 40g / L, self-crosslinking silicone finishing agent SS 6186: 30g / L, silicone crosslinking agent SS 6175: 10g / L, and the rest is deionized water.

[0035] A preparation method of the moisture-crosslinked organosilicon anti-wrinkle and non-ironing finishing solution, comprising the following steps:

[0036] According to the ratio, under normal temperature conditions, add anti-shrinkage and anti-wrinkle resin NBD, catalyst CS-300, penetrating agent JFC, hydrophilic silicone softener SS 6179-1, self-crosslinking silicone finishing agent SS 6186, organic Add deionized water to the silicon cross-linking agent SS 6175, stir and set the ...

Embodiment 2

[0040] A moisture-crosslinked silicone anti-wrinkle and non-ironing finishing liquid, each rising tide cross-linked silicone anti-wrinkle and non-ironing finishing liquid is made of the following components:

[0041] Anti-shrinkage and anti-wrinkle resin NBD: 230g / L, catalyst CS-300: 105g / L, penetrant JFC: 2g / L, hydrophilic silicone softener SS 6179-1: 40g / L, self-crosslinking silicone finishing agent SS 6186: 30g / L, silicone crosslinking agent SS 6175: 10g / L, and the rest is deionized water.

[0042] A preparation method of the moisture-crosslinked organosilicon anti-wrinkle and non-ironing finishing solution, comprising the following steps:

[0043] According to the ratio, under normal temperature conditions, add anti-shrinkage and anti-wrinkle resin NBD, catalyst CS-300, penetrating agent JFC, hydrophilic silicone softener SS 6179-1, self-crosslinking silicone finishing agent SS 6186, organic Add deionized water to the silicon cross-linking agent SS 6175, stir and set the ...

Embodiment 3

[0047] A moisture-crosslinked silicone anti-wrinkle and non-ironing finishing liquid, each rising tide cross-linked silicone anti-wrinkle and non-ironing finishing liquid is made of the following components:

[0048] Anti-shrink and anti-wrinkle resin NBD: 200g / L, catalyst CS-300: 100g / L, penetrant JFC: 2g / L, hydrophilic silicone softener SS 6179-1: 30g / L, self-crosslinking silicone finishing agent SS 6186: 45g / L, silicone crosslinking agent SS 6175: 15g / L, and the rest is deionized water.

[0049] A preparation method of the moisture-crosslinked organosilicon anti-wrinkle and non-ironing finishing solution, comprising the following steps:

[0050] According to the ratio, under normal temperature conditions, add anti-shrinkage and anti-wrinkle resin NBD, catalyst CS-300, penetrating agent JFC, hydrophilic silicone softener SS 6179-1, self-crosslinking silicone finishing agent SS 6186, organic Add deionized water to the silicon cross-linking agent SS 6175, stir and set the vol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a moisture-crosslinked silicone anti-wrinkle and non-ironing finishing liquid. Each rising tide cross-linked organic silicon anti-wrinkle and non-ironing finishing liquid is made of the following components by weight: anti-shrinkage and anti-wrinkle resin: 200‑260 parts, catalyst: 100‑130 parts, penetrating agent: 1‑2 parts, hydrophilic silicone softener: 20‑50 parts, self-crosslinking silicone finishing agent: 30‑60 parts, silicone crosslinking agent: 10‑ 20 parts, the rest is deionized water. Using the moisture-crosslinked silicone anti-wrinkle and non-ironing finishing solution of the present invention to carry out non-ironing finishing on pure cotton woven fabrics not only realizes the non-ironing finishing of the fabric, but also ensures the physical properties such as whiteness, strength, and hand feeling of the fabric. The finishing solution does not contain formaldehyde, thus ensuring the safety and environmental protection of the finished fabric.

Description

technical field [0001] The invention belongs to the technical field of textile printing and dyeing, and in particular relates to a moisture-crosslinked organosilicon anti-wrinkle and non-ironing finishing liquid and a preparation method and application thereof. Background technique [0002] Cotton, a natural fiber fabric, has natural comfort, so it is more and more favored by people. But cotton fabrics, especially woven fabrics, tend to wrinkle and shrink after washing. In order to improve this shortcoming, it is very important to carry out anti-wrinkle and non-ironing finishing on cotton fabrics. Generally, anti-wrinkle and non-ironing finishing uses padding resin, which is baked at high temperature, which is likely to cause a decrease in strength and a decrease in hand comfort. Contents of the invention [0003] The first object of the present invention is to provide a moisture-crosslinked silicone anti-wrinkle and easy-care finishing solution. [0004] The second obj...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/00D06M15/643D06M15/53D06M101/06
CPCD06M15/00D06M15/53D06M15/643D06M15/6436D06M2101/06D06M2200/20
Inventor 张玉杨坡曹华斌
Owner 上海氟聚化学产品股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More