Preparation method of CNT-SiO2/NBR material and atomization spraying gun

An atomizing spray gun, cnt-sio2 technology, applied in the field of atomizing spray gun, CNT-SiO2/NBR material preparation, can solve the problems of re-agglomeration of fillers, reduce compatibility, large water consumption, etc., achieve complete dispersion, improve dispersion performance, energy consumption and low production costs

Active Publication Date: 2019-07-09
QINGDAO UNIV OF SCI & TECH
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (1) The emulsion blending method can make CNT and other fillers more uniformly dispersed in the rubber matrix. Usually, acid and other demulsifiers are used to realize the co-precipitation of latex particles and CNT, but adding acid or other chemical reagents for flocculation and subsequent dehydration and drying process is easy Re-agglomeration of fillers will cause problems of low efficiency, long time consumption and large water consumption;
[0006] (2) Simultaneous mechanical blending method, solution blending method and melt blending method also have some unavoidable defects in the rubber composite material prepared due to technological problems;
[0007] (3) Since the multi-CNT and filler enter the gas-phase atomization spray gun when mixed, it is easy to generate group accumulation, which reduces the compatibility during the mixing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of CNT-SiO2/NBR material and atomization spraying gun
  • Preparation method of CNT-SiO2/NBR material and atomization spraying gun
  • Preparation method of CNT-SiO2/NBR material and atomization spraying gun

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] like figure 1 As shown, the present invention provides a CNT-SiO 2 / NBR composite material preparation method, is characterized in that: comprise the steps:

[0050] S100, use a ball mill to grind silicon dioxide to 100-200 meshes, place the ground silicon dioxide and deionized water in a beaker, and use a high-speed shearing machine to disperse into a silicon dioxide aqueous dispersion with a mass fraction of 25 wt%, And stirred by a stirrer to obtain 25wt% silica slurry;

[0051] S200, stirring and mixing 3 parts by mass of CNT aqueous solution and 30 parts by mass of silica slurry to form CNT-SiO 2 Mixed solution, and the dry glue mass fraction of 100 mass parts is that the centrifugal concentration nitrile latex of 60wt% adds CNT-SiO 2 In the mixture, stir the CNT-SiO with a blade stirrer 2 / NBRL mixture, complete CNT-SiO 2 Preparation of / NBRL mixture;

[0052] S300, the CNT-SiO to be prepared 2 / NBRL mixture is poured into the container tank, and the CNT-Si...

Embodiment 2

[0062] like Figure 2 to Figure 6 As shown, the present invention also provides a CNT-SiO 2 / NBR composite material ultrasonic atomization spray gun, including an assembly frame 1, and a batching bottle 2 arranged on the assembly frame 1, an air pump 3 is arranged on the assembly frame 1 located on one side of the batching bottle 2, and will be prepared The CNT / NBR mixed liquid is injected into the batching bottle 2, and the injection air pressure is provided by the air pump 3 and the pressure change in the batching bottle 2 is controlled to realize spraying under uniform pressure.

[0063] The inner side of the assembly frame 1 of the present invention is provided with a micro-movement assembly 4, and several atomizing nozzles 5 are arranged on the micro-motion assembly 4, and the left and right lateral vibrations of the atomizing nozzles are driven by the micro-motion assembly 4, thereby ensuring the stability of the atomizing nozzles 5. The spray surface moves slightly in ...

Embodiment 3

[0074] like Figure 7 , Figure 8 and Figure 9As shown, the ball mill used in the preparation of composite materials in Example 1 provided by the present invention includes a base B1 and a mounting groove B2 arranged on the base B1, and a planetary wheel B3 driven by a motor is arranged inside the mounting groove B2 , and there are at least three star wheels of the planetary wheel B3, the star wheel of the planetary wheel B3 is provided with a fixed bracket B4, the fixed bracket B4 is equipped with a grinding tank B6 through a movable hinge device B5, and a pressing rod device B7 is installed on the grinding tank B6 , the upper part of the grinding tank B6 is provided with a turntable disk B8, and the turntable disk B8 is fixedly connected to the installation groove B2 through a bracket. The opposite surfaces of B802 are provided with racks, and the top of the pressure bar device B7 is meshed between the inner disc B801 and the outer rail ring B802 through the bevel gear B1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Quality scoreaaaaaaaaaa
Quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a CNT-SiO2 / NBR material. The preparation method comprises the steps that 100, silicon dioxide is ground to be in the particle size of 100-200 meshes andthen put into a beaker with deionized water to be dispersed into silicon dioxide aqueous dispersion, stirring is conducted, and silicon dioxide slurry is obtained; 200, a CNT aqueous solution and thesilicon dioxide slurry are stirred and mixed, centrifugal concentrated nitrile butadiene rubber latex is added into a CNT-SiO2 mixed solution, stirring is conducted, and preparation of a CNT-SiO2 / NBRL mixed solution is completed; 300, the CNT-SiO2 / NBRL mixed solution is sprayed to a roller of a high-temperature open mill through a gas-phase-assisted spraying atomization gun; 400, the temperatureof the roller is adjusted, the CNT-SiO2 / NBRL mixed solution is atomized into liquid drops, dry masterbatch is obtained, and the masterbatch is scraped with a scraper blade on the roller to be collected for use; and 500, the prepared masterbatch is internally mixed on the open mill, the masterbatch, zinc oxide ZnO, stearic acid SAD, a DPG accelerant and an anti-aging agent 4020 are sequentially added to be mixed, and the CNT-SiO2 / NBR composite material is obtained. According to the preparation method, the process is simple and controllable, the principle is scientific and reasonable, the atomization uniformity and the mixing compatibility uniformity are guaranteed, and secondary dripping attachment formed through water vapor adhesion is avoided.

Description

technical field [0001] The invention relates to the field of rubber mixing, specifically a CNT-SiO 2 / NBR material preparation method and atomizing spray gun. Background technique [0002] Mixing is the first step in the rubber processing process, and it is also the most critical process. Through this process, various fillers are fully mixed with rubber, and the fillers are dispersed as uniformly as possible. The quality of the mixing result directly determines the rubber product. The performance and service life have been widely concerned by the industry. [0003] At present, the preparation methods of CNT / rubber composite materials mainly include traditional methods such as mechanical blending, solution blending, melt blending and emulsion blending. A polymethylphenylsiloxane disclosed in Chinese patent 201510770421.7 The alkane-carbon nanotube-silicone rubber composite material is carried out according to the following steps: Step 1: Mix 90-110 parts by weight of silico...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B02C21/00B02C19/06B02C19/18B29B7/00
CPCB02C21/00B02C19/06B02C19/18B29B7/002
Inventor边慧光汪传生李邵明郝国强张璐奇朱逍遥田绪东李利沈波张德伟尹凤福
OwnerQINGDAO UNIV OF SCI & TECH