Pre-laying self-adhesion polymer modified bituminous waterproof sheet material and preparation method thereof

A technology of modified asphalt and waterproof membrane, which is applied in the direction of textiles and paper making, which can solve the problems of poor peel strength, poor water channeling resistance, poor static load capacity, etc., and achieve good self-adhesive effect

Inactive Publication Date: 2019-08-09
富华防水科技股份有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above-mentioned waterproof membrane has good bonding performance, high and low temperature resistance, and low temperature flexibility; but it is not suitable for underground waterproofing pro...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pre-laying self-adhesion polymer modified bituminous waterproof sheet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Example 1 A pre-paved self-adhesive polymer modified asphalt waterproof membrane

[0035] The pre-paved self-adhesive polymer modified asphalt waterproofing membrane includes an isolation layer, a polyester tire base cloth, a modified asphalt layer, an anti-seepage layer, and a bottom isolation membrane;

[0036] The isolation layer is: fine sand with a thickness of 0.5 mm and a fineness of 100 mesh;

[0037] The polyester base fabric: 195g / ㎡ filament polyester base fabric, tensile strength > 500N / 5cm, thickness 1.15mm, moisture content ≤ 1.5%.

[0038] The modified asphalt layer includes the following raw material components in parts by weight:

[0039] 75 parts of No. 130 bitumen, 55 parts of No. 90 bitumen, 8 parts of wood wax oil, 8 parts of propyl paraben, 14 parts of coumarone resin, 9 parts of SBR, 5 parts of EVA, 9 parts of coal tar, xanthan gum 7 parts, 12 parts of dicyclopentadiene-based petroleum resin, 17 parts of terpene phenolic resin, 2.5 parts of sorbi...

Embodiment 2

[0044] Example 2 A pre-paved self-adhesive polymer modified bitumen waterproof membrane

[0045] The pre-paved self-adhesive polymer modified asphalt waterproofing membrane includes an isolation layer, a polyester tire base cloth, a modified asphalt layer, an anti-seepage layer, and a bottom isolation membrane;

[0046] The isolation layer is: fine sand with a thickness of 0.8 mm and a fineness of 200 mesh;

[0047] The polyester base fabric: 195g / ㎡ filament polyester base fabric, tensile strength > 500N / 5cm, thickness 1.15mm, moisture content ≤ 1.5%.

[0048] The modified asphalt layer includes the following raw material components in parts by weight:

[0049] 80 parts of No. 130 bitumen, 50 parts of No. 90 bitumen, 9 parts of wood wax oil, 7 parts of propyl paraben, 11 parts of coumarone resin, 12 parts of SBR, 5.8 parts of EVA, 7 parts of coal tar, xanthan gum 8 parts, 15 parts of dicyclopentadiene-based petroleum resin, 15 parts of terpene phenolic resin, 2 parts of sorb...

Embodiment 3

[0054] Example 3 A pre-paved self-adhesive polymer modified bitumen waterproof membrane

[0055] The pre-paved self-adhesive polymer modified asphalt waterproofing membrane includes an isolation layer, a polyester tire base cloth, a modified asphalt layer, an anti-seepage layer, and a bottom isolation membrane;

[0056] The isolation layer is: fine sand with a thickness of 0.5 mm and a fineness of 100 mesh;

[0057] The polyester base fabric: 195g / ㎡ filament polyester base fabric, tensile strength > 500N / 5cm, thickness 1.15mm, moisture content ≤ 1.5%.

[0058] The modified asphalt layer includes the following raw material components in parts by weight:

[0059] 78 parts of No. 130 bitumen, 53 parts of No. 90 bitumen, 8.4 parts of wood wax oil, 7.5 parts of propyl paraben, 13 parts of coumarone resin, 10 parts of SBR, 5.5 parts of EVA, 8 parts of coal tar, xanthan gum 7.2 parts, 13 parts of dicyclopentadiene petroleum resin, 16 parts of terpene phenolic resin, 2.3 parts of so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention provides a pre-laying self-adhesion polymer modified bituminous waterproof sheet material. The waterproof sheet material comprises a modified bitumen layer, and the modified bitumen layer is prepared from, by weight, 75-80 parts of bitumen 130, 50-55 parts of bitumen 90, 8-9 parts of wax oil, 7-8 parts of propyl p-hydroxybenzoate, 11-14 parts of coumarone resin, 9-12 parts of SBR, 5-5.8 parts of EVA, 7-9 parts of coal tar, 7-8 parts of xanthan gum, 12-15 parts of dicyclopentadiene petroleum resin, 15-17 parts of polyterpene phenolic resin, 2-2.5 parts of sorbitol, 4-5 parts of ananti-oxidant and 4-5 parts of a thickening agent. The bituminous waterproof sheet material is used for underground waterproof engineering in a cold region, the pre-laying self-adhesion effect is goodin a low-temperature environment, after the bituminous waterproof sheet material and post-cast concrete are immersed into water, the peeling strength is high, the static load capacity is high, and the water channeling resistance is high.

Description

technical field [0001] The invention relates to a pre-paved self-adhesive polymer modified asphalt waterproof coiled material and a preparation method thereof, belonging to the technical field of waterproof coiled materials. Background technique [0002] The pre-laying of waterproof membrane refers to the waterproof membrane that the structural concrete is directly poured on the waterproof membrane, and the self-adhesive layer of the membrane and the concrete have good adhesion to achieve the anti-adhesive effect of pre-laying. It includes two categories: polymer-based membranes with a self-adhesive layer on the surface and polyester tire self-adhesive membranes with modified asphalt as the main body. [0003] Pre-paved self-adhesive polymer modified bitumen waterproofing membrane itself has the function of self-adhesive, easy to construct, and easy to form a fully enclosed integral waterproof layer; in terms of material properties, its tensile force and heat resistance are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N5/00D06N3/10
CPCD06N3/10D06N5/003D06N2209/103D06N2209/1664
Inventor 隋子涛隋福胜张富刚郝振锋
Owner 富华防水科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap