High-strength-and-toughness and corrosion-resistance magnesium alloy and preparation method thereof

A magnesium alloy and corrosion-resistant technology, which is applied in the field of high-strength and corrosion-resistant magnesium alloy and its preparation, can solve the problems of low corrosion rate, difficult plastic processing, poor deformation ability of magnesium alloy, etc., and achieve uniform corrosion, good corrosion resistance, Good corrosion resistance effect

Active Publication Date: 2019-08-20
珠海中科先进技术研究院有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The embodiments of the present invention solve the problem by providing a high-strength, toughness and corrosion-resistant magnesium alloy, which contains 1.0-8.0% of Zn, 0.1-5.0% of Nd, 0.1-5.0% of Ca, 0.1-4.0% of Zr and the balance of Mg. In the prior art, the deformation ability of magnesium alloy at room temperature is poor, and it is difficult to plastically process when it is used to prepare the stent. While achieving the ideal support effect of the alloy, it can also be degraded uniformly in the body and has better corrosion resistance. , and the corrosion is relatively uniform, and the corrosion rate is as low as 0.18mm / year

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength-and-toughness and corrosion-resistance magnesium alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] This example provides a high-strength and toughness corrosion-resistant magnesium alloy, which includes the following components in mass percentage:

[0077] Zn 1.0%, Nd 0.1%, Ca 0.1%, Zr 0.1%, the balance is Mg, the total amount of impurity elements in this alloy is <0.05%.

Embodiment 2

[0079] This example provides a high-strength and toughness corrosion-resistant magnesium alloy, which includes the following components in mass percentage:

[0080] Zn 8.0%, Nd 5.0%, Ca 5.0%, Zr 4.0%, the balance is Mg, the total amount of impurity elements in this alloy is <0.05%.

Embodiment 3

[0082] This example provides a high-strength and toughness corrosion-resistant magnesium alloy, which includes the following components in mass percentage:

[0083] Zn 4.0%, Nd 2.5%, Ca 2.5%, Zr 2.0%, the balance is Mg, the total amount of impurity elements in this alloy is <0.05%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The embodiment of the invention provides high-strength-and-toughness and corrosion-resistance magnesium alloy and a preparation method thereof. The alloy solves the problems in the prior art that thedeformation capability of the magnesium alloy is poorer and the plasticity processing is difficult when the magnesium alloy is used for preparing stents, the stents can be uniformly degraded in the body while the ideal supporting effect of alloy is achieved, better corrosion resistant performance is achieved, the corrosion-resistance rate is significantly reduced, and the corrosion is more uniform.

Description

technical field [0001] The invention belongs to the technical field of material preparation, and in particular relates to a high-strength and toughness corrosion-resistant magnesium alloy and a preparation method thereof. Background technique [0002] According to the survey report of the World Health Organization, nearly 18 million people die of cardiovascular diseases every year, and this number is expected to increase to 24 million by 2030. It can be seen that cardiovascular disease has become the leading cause of death in the world, and vascular stent implantation is the most effective clinical treatment for cardiovascular disease. [0003] The vascular stents currently used clinically are mainly made of inert metal materials such as 316L stainless steel, nickel-titanium alloy, and cobalt-chromium alloy. The elastic recoil reduces the restenosis rate of blood vessels. However, these inert metal stents act as foreign bodies after implantation, which can lead to excessiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C23/00C22C23/04C22C1/03C22F1/06
CPCC22C1/03C22C23/00C22C23/04C22F1/06
Inventor 马国睿吴锋
Owner 珠海中科先进技术研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com