Pure natural plant high-temperature glaze material and preparation method thereof

A high-temperature glaze and pure natural technology, applied in the field of ceramic products, can solve the problems of rare ore raw materials, unfavorable health, poor stability, etc., and achieve the effects of benefiting human health, enhancing nutritional effects, and low moisture absorption rate

Inactive Publication Date: 2019-11-22
海南丹之海文化传播有限公司
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramic glaze is an indispensable daily necessities in people's daily life. With the improvement of the quality of life, the requirements for the safety, aesthetics and practicability of ceramic products are getting higher and higher. At present, the existing ceramic glazes on the market Due to material selection and other issues, most glazes are formulated with chemical materials and fired at low temperature, which is not good for human health, and the raw materials of raw ore materials are rare, costly, and poor stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pure natural plant high-temperature glaze material and preparation method thereof
  • Pure natural plant high-temperature glaze material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A pure natural plant high-temperature glaze, comprising the following raw materials in parts by weight: 20 parts of straw ash, 10 parts of wolfberry ash, 2 parts of peach gum, 1 part of pine cone ash, 5 parts of bran ash, 20 parts of water, wherein straw ash SiO in 2 The mass percentage is 50%;

Embodiment 2

[0018] A pure natural plant high-temperature glaze, comprising the following raw materials in parts by weight: 45 parts of straw ash, 15 parts of wolfberry ash, 8 parts of peach gum, 3 parts of pine cone ash, 18 parts of bran ash, 40 parts of water, wherein straw ash SiO in 2 The mass percentage is 75%;

Embodiment 3

[0020] A pure natural plant high-temperature glaze, comprising the following raw materials in parts by weight: 35 parts of straw ash, 13 parts of wolfberry ash, 5 parts of peach gum, 2 parts of pine cone ash, 10 parts of bran ash, 35 parts of water, wherein the straw ash SiO in 2 The mass percentage is 60%;

[0021] The preparation method of a kind of pure natural plant high-temperature glaze of above-mentioned embodiment 1~3 comprises the following steps:

[0022] S1. Straw ash and Osmanthus ash are obtained by calcining rice stalks and Osmanthus at 800°C for 6 hours;

[0023] S2, pine cone ash is formed by calcining pine cones at 900°C for 6.5 hours;

[0024] S3, bran ash is made by calcining bran at 650°C for 8.5 hours;

[0025] S4. Mix and wash the above-mentioned straw ash, wolfberry ash, pine cone ash, and bran ash, pass through a 15-mesh sieve after sedimentation, add water and put it into a ball mill to mill at a speed of 90r / min for 20 hours, then pass through a 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a pure natural plant high-temperature glaze material and a preparation method thereof. Raw materials of the glaze material include, by weight, 20-45 parts of straw ash, 10-15 parts of Dicranopteris linearis ash, 2-8 parts of peach gum, 1-3 parts of pine cone ash, 5-18 parts of bran ash and 20-40 parts of water. The content of SiO2 in the straw ash is 1-3 times that of othermaterials in the straw ash. The pure natural plants are calcined at a specific temperature for a specific period of time and then subjected to high-temperature glaze firing, and the prepared glaze material is more excellent, high in hardness and strength, low in moisture absorption rate and good in visual effect. The pure natural plants are used for calcination, so that when the glaze material isused, plant materials of the glaze material can be converted into contained products, and the glaze material is beneficial to human health.

Description

technical field [0001] The invention relates to the technical field of ceramic products, in particular to a pure natural plant high-temperature glaze and a preparation method thereof. Background technique [0002] Ceramic glaze is an indispensable daily necessities in people's daily life. With the improvement of the quality of life, the requirements for the safety, aesthetics and practicability of ceramic products are getting higher and higher. However, the existing ceramic glazes on the market Due to material selection and other issues, most glazes are formulated with chemical materials and fired at low temperature, which is not good for human health. Raw ore materials are rare, costly, and poor in stability. Contents of the invention [0003] In view of this, the present invention proposes a pure natural plant high-temperature glaze and a preparation method thereof to solve the above-mentioned problems. [0004] The technical solution of the present invention is achieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 刘丹丹郑国国
Owner 海南丹之海文化传播有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com