A kind of temperature-regulating textile and its production method
A technology for textiles and temperature regulation, applied in the field of textiles, can solve the problems of poor temperature regulation effect, poor temperature regulation function, hard hand feeling of fabrics, etc., and achieve the effect of improving the temperature inside the clothes, good temperature regulation effect and low drying temperature
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] The material of the textile in this embodiment is a cotton fabric, gram weight is 120 g / m. 2 .
[0034] 100 parts of MPCM30SL80 were added to the bubble tub, stirred at 1300 rpm for 2min, 1 part color cream D-501, stirred for 2 min. 6 parts of the crosslinker KH-550 was slowly added, stirred for 5 min; then 1 part of the thickener DS-J076 was added, and the mixture was stirred while the consistency was 80 dpa.s at room temperature to obtain a mixed slurry. The mixed slurry was filtered through 100 mesh filter. The slurry was extracted into the printing roll, the print roller is 80 mesh, the print magnetic rod is 10 mm, the print magnetic force is 55%, the vehicle speed is 35 m / min, dried at 150 ° C, control dry coating is 30 g / m 2 .
Embodiment 2
[0036] The material of the textile described in this embodiment is a polyester fabric, gram weight is 70 g / m. 2 .
[0037] In the 100 parts of DP-WDF345, 20 parts of tap water were added, and stirred at 1450 rpm for 5 min, 1 grade color cream D-501 was added, and stirred for 2 min. 4 parts of the crosslinker KH-550 were slowly added, stirred for 5 min; then 2 parts of thickener DS-J076 were added, and the mixture was stirred while the consistency was 50dPa.s at room temperature to obtain a mixed slurry. The mixed slurry was filtered through 100 mesh filter. The slurry is extracted in the printing roll. The print roll is 10mm, the print magnetic rod is 10 mm, the print magnetic force is 85%, the vehicle speed is 35 m / min, dried at 140 ° C, control dry coating is 20 g / m 2 .
Embodiment 3
[0039] The material of the textile in this embodiment is a polyester and a cotton mixed fabric, wherein the mass ratio of polyester and cotton is 1: 1, gram weight is 110 g / m. 2 .
[0040] In the 100 parts of DP-WDF345, 10 parts of tap water was added, and then stirred at 1500 rpm, 2 gum D-501 was added, and stirred for 2 min. 4 part of the crosslinker KH-550 was slowly added, stirred for 5 min; 1 part of the thickener DS-J076 was added, and stirred while adding until the consistency was 70 dpa.S at room temperature to obtain a mixed slurry. The mixed slurry was filtered through 100 mesh filter. The slurry was pumped into the printing roll, the printing roller was 100 mesh, the print magnetic rod was 12 mm, the print magnetic force was 65%, the vehicle speed was 40 m / min, dried at 145 ° C, control dry coating of 35 g / m 2 .
PUM
Property | Measurement | Unit |
---|---|---|
enthalpy | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com