A method for recovering valuable metals from oily cylinder liner honing waste by fire method
A valuable metal and cylinder liner technology, applied in the field of comprehensive utilization of solid waste resources, can solve the problems of difficult separation of valuable metal components, fine particle size, high oil content, and achieve easy control, high recovery rate, and large processing capacity. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] Cylinder liner honing waste with TFe70%, Cu2%, Mo0.5%, and oil content 10% is used as raw material, finely ground quicklime and silica are used as flux, finely ground coke powder is used as reducing agent, and lignite humic acid is used as binder Carry out batching, wherein the mass percentage of cylinder liner honing waste less than 200 mesh is 95%, and the mass percentage of quicklime, silica, and coke powder finely ground to less than 200 mesh is 99%, and the mixture CaO / SiO is adjusted 2 The mass ratio is 0.35, Al 2 o 3 The content of the compound is 15%, the amount of the reducing agent is 10%, the amount of the binder is 0.2%, and the water content of the mixture is 6%. The pellets were dried in a 120°C drying oven to obtain dry pellets; the dry pellets were isolated from the air for heating and roasting, the heating rate from room temperature to 500°C was 5°C / min, and the temperature residence time at 500°C was After 90 minutes, the gas in this section is colle...
Embodiment 2
[0031] Cylinder liner honing waste with TFe72%, Cu1.5%, Mo0.8%, and oil content of 20% is used as raw material, finely ground quicklime and silica are used as flux, finely ground coke powder is used as reducing agent, lignite humic acid is used as viscous Batching agent is used for batching, wherein the mass percentage of cylinder liner honing waste less than 200 mesh is 95%, and the mass percentage of quicklime, silica and coke powder finely ground to less than 200 mesh is 99%. Adjust the mixture CaO / SiO 2 The mass ratio is 0.45, Al2 o 3 The content of the reducing agent is 8%, the amount of the reducing agent is 5%, the amount of the binder is 0.01%, and the water content of the mixture is 3%; then the mixture is briquetted with a pair of roller briquetting machines, and the average particle size of the agglomerates is 25mm, the pellets were dried in a 120°C drying oven to obtain dry pellets; the dry pellets were isolated from the air and heated and roasted, the heating ra...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com