A kind of cotton pulp production process for manufacturing cellulose nitrate

A cellulose nitrate ester and production process technology, applied in multi-stage pulping process, fiber raw material treatment, papermaking, etc., can solve the problems of cumbersome cooking process and bleaching process, difficult to treat highly polluted wastewater, and maximize product benefits, etc., to achieve The degree of polymerization is stable, the content of methyl fiber is high, and the strength is good.

Active Publication Date: 2022-04-19
山东银鹰股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the existing bleaching process of ordinary cotton pulp production, sodium hypochlorite and chlorine gas are used for multi-stage bleaching of cotton pulp, which causes damage to fibers and reduces fiber strength
And the COD of cooking black liquor is about 45000mg / L, there is a problem of highly polluted wastewater that is difficult to treat
[0005] Chinese patent, application number CN200810016759.3 discloses a title "a cotton pulp production method", in which cotton linters are used as raw materials to produce nitrated cotton pulp, but the cooking process and bleaching process are too cumbersome , which is not conducive to the control of the overall body and the maximization of product benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] In the embodiment of the present invention, a kind of cotton pulp production process for manufacturing cellulose nitrate, the process comprises the following steps:

[0037] (1) Material selection, cotton opening, and dry impurity removal: select 100% second-class cotton linters with a first-level maturity of 79-81%, use a cotton opener to tear the linters, and use an impurity remover to select After removing impurities, it is sent to screw press and impregnation through cyclone separator.

[0038] (2) Alkali preparation and impregnation: prepare lye at room temperature, control the temperature of lye at 15°C, the concentration of lye: 42g / L, the amount of lye: 17800L / ball, the ratio of lye (water to sodium hydroxide Proportion) 1:3.6, and then through the screw extrusion of the screw conveyor, the prepared lye and cotton linters are fully infiltrated and mixed. After the mixing is completed, they are transported to the cooking process by the screw conveyor.

[0039] (...

Embodiment 2

[0057] A kind of cotton pulp production process for manufacturing cellulose nitrate, the process comprises the following steps:

[0058] (1) Material selection, cotton opening, and dry impurity removal: select 100% second-class cotton linters with a first-level maturity of 79-81%, use a cotton opener to tear the linters, and use an impurity remover to select After removing impurities, it is sent to screw press and impregnation through cyclone separator.

[0059] (2) Alkali blending and impregnation: Alkali blending at room temperature, the temperature is controlled at 25°C, the concentration of alkali blending: 44g / L, the amount of alkali blending: 18000L / ball, the ratio of alkali liquid: 1:3.8, through screw extrusion, and cotton short The velvet is fully infiltrated and mixed, and conveyed to the cooking process by a screw.

[0060] (3) Injection aid: the aid is H 2 o 2 Specific additives, in the process of filling the ball with H 2 o 2 The standard H with the amount of...

Embodiment 3

[0075] A kind of cotton pulp production process for manufacturing cellulose nitrate, the process comprises the following steps:

[0076] (1) Material selection, cotton opening, and dry impurity removal: select 100% second-class cotton linters with a first-level maturity of 79-81%, use a cotton opener to tear the linters, and use an impurity remover to select After removing impurities, it is sent to screw press and impregnation through cyclone separator.

[0077] (2) Alkali blending and impregnation: Alkali blending at room temperature, the temperature is controlled at 35°C, the concentration of alkali blending: 46g / L, the amount of alkali blending: 18200L / ball, the ratio of alkali liquid: 1:4, through screw extrusion, and cotton short The velvet is fully infiltrated and mixed, and conveyed to the cooking process by a screw.

[0078] (3) Injection aid: the aid is H 2 o 2 Specific additives, in the process of filling the ball with H 2 o 2 The standard H with the amount of 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
whitenessaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of cotton pulp for manufacturing cellulose nitrate. The cotton pulp has the following indicators: polymerization degree 930-980; whiteness ≥ 88%; iron content ≤ 15ppm; ash content ≤ 0.08%; fiber Length 23-32%; A fiber ≥ 97.5%; moisture 6-9%; small dust ≤ 15mm² / 500g; Class B dust ≤ 2mm² / 500g, the cotton pulp for cellulose nitrate prepared by the above method in the present invention, High fibrous degree, good strength, high methyl fiber content, stable polymerization degree, less dust, can be better used in new pharmaceutical fillers ~ microcrystalline cellulose and explosive nitrocellulose, advanced nitro paint and architectural coatings, etc. industry production.

Description

technical field [0001] The present invention relates to a production process of cotton pulp, in particular to a production process of cotton pulp for the manufacture of cellulose nitrate, which is used for the production of various colored celluloid, film, nitro lacquer flakes and explosives, and various spray paints. , typing stencil, varnish, bottle cover, etc., belonging to the technical field of cotton pulp. Background technique [0002] In recent years, in the domestic and foreign markets, explosives with strong explosive force and strong action have been manufactured and used as vasodilators in medicine. They are made into 0.3% nitroglycerin tablets and administered sublingually. The effect is rapid and short-lived, and the effect is extremely strong. . Therefore, the demand for nitrocellulose products is also increasing, which provides a favorable condition for the research and development of this variety of cotton pulp. [0003] my country is a big cotton producing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21C3/26D21C7/00D21D1/02D21D1/30
CPCD21C3/26D21C7/00D21D1/02D21D1/30
Inventor 陈忠国曹知朋马伟良唐逢郑春友吕兴华李宗臻孙海龙
Owner 山东银鹰股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com