Corrosion-resistant surface treatment method for coil housing and corrosion-resistant coil housing

A technology for surface treatment and shell surface, which is applied to the device for coating liquid on the surface, metal material coating process, coating and other directions, which can solve problems such as affecting the service life of the workpiece, incomplete removal of pollutants, and corrosion and rusting of products. , to achieve the effect of prolonging the service life, convenient loading and unloading operations, and easy operation.

Active Publication Date: 2022-01-25
SUZHOU CHUANGRUI MACHINERY & ELECTRICAL TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Regardless of the process, the pollutants on the surface of the workpiece are often not completely removed, and the residual pollutants are likely to cause premature corrosion and rust of the product
[0006] At the same time, the existing workpieces are not subjected to other surface treatment after cleaning, and the workpieces are vulnerable to the intrusion of water and other liquids to cause corrosion, and their corrosion resistance is poor, which seriously affects the service life of the workpieces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion-resistant surface treatment method for coil housing and corrosion-resistant coil housing
  • Corrosion-resistant surface treatment method for coil housing and corrosion-resistant coil housing
  • Corrosion-resistant surface treatment method for coil housing and corrosion-resistant coil housing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] Objects, advantages and features of the present invention will be illustrated and explained by the following non-limiting description of preferred embodiments. These embodiments are only typical examples of applying the technical solutions of the present invention, and all technical solutions formed by adopting equivalent replacements or equivalent transformations fall within the protection scope of the present invention.

[0044] In the description of the scheme, it should be noted that the terms "center", "upper", "lower", "left", "right", "front", "rear", "vertical", "horizontal", " The orientation or positional relationship indicated by "inner", "outer", etc. is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of description and simplification of description, rather than indicating or implying that the device or element referred to must have a specific orientation , constructed and operated in a particular or...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
poweraaaaaaaaaa
poweraaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-corrosion surface treatment method of a coil shell and a corrosion-resistant coil shell, wherein the surface treatment method includes the following steps: S100, cleaning the coil shell; S200, performing plasma cleaning on the cleaned coil shell; S300, performing plasma cleaning on the coil shell; A solid corrosion-resistant film is formed on the surface of the cleaned coil shell through vapor deposition, and the contact angle of liquid on the surface of the solid corrosion-resistant film is greater than 90°. The method is exquisite in design and simple in process. The surface of the workpiece can be cleaned by plasma through the vapor deposition system, thereby ensuring the cleanliness of the surface of the workpiece, and at the same time improving the surface activity of the workpiece, further forming a solid corrosion-resistant film on the surface of the workpiece, and making the solid corrosion-resistant film Maintaining hydrophobicity can effectively avoid the intrusion of liquid, greatly improve the corrosion resistance of the workpiece, and prolong the service life of the workpiece, especially suitable for the treatment of workpieces with high surface anti-corrosion requirements.

Description

technical field [0001] The invention relates to the field of coil shell processing, in particular to an anti-corrosion surface treatment method for a coil shell and a corrosion-resistant coil shell. Background technique [0002] At present, for the finished coil casing (coil casing for automobile turbocharger), it usually needs to be cleaned before packaging. [0003] One of the feasible cleaning processes includes the following process: ultrasonic cleaning-rinsing-industrial oven drying. [0004] Another feasible cleaning process includes the following processes: automatic spray cleaning - ultrasonic cleaning - spray rinsing - high pressure wind cutting water. [0005] Regardless of the process, the pollutants on the surface of the workpiece are often not completely removed, and the residual pollutants are likely to cause premature corrosion and rust of the product. [0006] At the same time, the existing workpieces are not subjected to other surface treatment after clean...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C16/50C23C16/02C23C16/458C23F15/00B05D1/00
CPCC23F15/00C23C16/50C23C16/0245C23C16/458B05D1/62
Inventor 刘鑫培朱小刚柳慧敏
Owner SUZHOU CHUANGRUI MACHINERY & ELECTRICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products