A kind of preparation method of carboxylated carbon nanotube modified pentaerythritol acrolein resin

A technology of pentaerythritol acrolein resin and carboxylated carbon, which is applied in the field of energetic material preparation, can solve the problems of lack of active groups, poor dispersion, lack of interface interaction, etc., and achieve improved section elongation, section elongation, and Improves the effect of fiber toughening effect

Active Publication Date: 2022-05-03
INST OF CHEM MATERIAL CHINA ACADEMY OF ENG PHYSICS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Carbon nanotubes are a kind of nanofiber material with excellent performance. However, there are certain difficulties in directly using carbon nanotubes to modify 123 resin. First, carbon nanotubes are nanomaterials and are easy to agglomerate, so they have poor dispersion in 123 resin. , the surface of carbon nanotubes lacks active groups and lacks strong interfacial interaction with the matrix, which is not conducive to improving the mechanical properties of the matrix material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of carboxylated carbon nanotube modified pentaerythritol acrolein resin
  • A kind of preparation method of carboxylated carbon nanotube modified pentaerythritol acrolein resin
  • A kind of preparation method of carboxylated carbon nanotube modified pentaerythritol acrolein resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] First weigh 0.02g of carboxylated CNTs, and use an agate grinding rod to crush and grind the CNTs; weigh 50g of 123 resin, then mix the ground CNTs with 123 resin, and initially stir evenly; Ultrasonic dispersion treatment for 30 minutes; mechanical stirring method was used again for 15 minutes; next, 0.9 mL of DES was added to the mixture, stirred evenly, and then poured into a mold; finally, it was placed in a 60°C oven and cured for 8 hours to prepare the Carboxylated CNTs modified 123 resin samples.

Embodiment 2

[0034] Weigh 0.04g of carboxylated CNTs, crush and grind the CNTs with an agate grinding rod; weigh 100g of 123 resin, then mix the ground CNTs with 123 resin, and initially stir evenly; then use an ultrasonic instrument to ultrasonicate the mixture Disperse for 30 minutes; again use mechanical stirring for 15 minutes; then add 1.8mL of DES to the mixture, stir evenly, and then pour it into a mold; finally put it in a 60°C oven and cure it for 8 hours to prepare carboxyl NaCNTs modified 123 resin samples.

Embodiment 3

[0036] Weigh 0.03g of carboxylated CNTs, crush and grind the CNTs with an agate grinding rod; weigh 100g of 123 resin, then mix the ground CNTs with 123 resin, and initially stir evenly; then use an ultrasonic instrument to ultrasonicate the mixture Disperse for 30 minutes; again use mechanical stirring for 15 minutes; then add 1.8mL of DES to the mixture, stir evenly, and then pour it into a mold; finally place it in a 60°C oven and cure for 8 hours to prepare 0.03 wt% carboxylated CNTs modified 123 resin samples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of pentaerythritol acrolein resin modified by carboxylated carbon nanotubes, which belongs to the technical field of energetic materials. The method comprises the following steps: step 1: crushing and grinding the carboxylated carbon nanotubes with an agate grinding rod; step 2: mixing the carboxylated carbon nanotubes ground in step 1 with pentaerythritol acrolein resin, And preliminarily stir evenly; Step 3: then adopt ultrasonic instrument to carry out ultrasonic dispersion treatment to the mixture that obtains in step 2; Step 4: adopt the method for mechanical stirring again to stir the mixture after dispersion treatment in step 3; Step 5: then Next, add diethyl sulfate to the mixture obtained in step 4, and stir evenly, and then pour it into a mold; step 6: place the mixture obtained in step 5 in an oven, and cure it to prepare carboxylated carbon nano Tube modified pentaerythritol acrolein resin.

Description

technical field [0001] The invention belongs to the field of energetic material preparation, and in particular relates to a preparation method of pentaerythritol acrolein resin modified by carboxylated carbon nanotubes. Background technique [0002] Pentaerythritol acrolein resin (also known as 123 resin) is used as the adhesive for many thermosetting explosive parts that require high shape stability. 123 resin is an adhesive prepolymer formed by chemical crosslinking of pentaerythritol and acrolein in the presence of an acid catalyst. It is a transparent viscous liquid resin. Polymerization achieves curing. The catalyst is generally selected from diethyl sulfate within an appropriate acid value range (acid value less than 1%). The cured 123 resin is a highly transparent and non-porous hard resin with good mechanical properties, heat resistance, and chemical corrosion resistance. plastic. This also endows polymer bonded explosives (PBX) with good mechanical properties, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L29/00C08K3/04C08K9/04C08J3/20
CPCC08J3/203C08J2329/00C08K3/041C08K9/04
Inventor 刘涛郑保辉谢虓肖春黄川
Owner INST OF CHEM MATERIAL CHINA ACADEMY OF ENG PHYSICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.