A self-cleaning outdoor artificial stone slab and its preparation method

An artificial slate and cleaning technology, applied in the field of artificial stone, can solve the problems of difficult cleaning, low shrinkage, low water absorption, etc., and achieve the effects of less mold consumption, low shrinkage, and low water absorption

Active Publication Date: 2021-04-09
GUANGDONG GAITEQI NEW MATERIAL TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of this, the present invention overcomes at least one of the deficiencies described in the above-mentioned prior art, and provides a product with good volume stability, good self-cleaning performance, low shrinkage, no warping and deformation during use, extremely low water absorption, and durable performance. Self-cleaning outdoor artificial stone slab with good mechanical performance, good decorative effect, good stain resistance and waterproof performance and its preparation method solves the problem that traditional outdoor decorative slabs are easily polluted by outdoor organic matter and dust and are not easy to clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A self-cleaning outdoor artificial stone slab and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]A self-cleaning outdoor use of artificial slate, prefabricated by ultra-high performance mineral powder of compressive strength 100 to 150 MPa, including a raw material component of the following weight fraction: mineral active powder 80 parts of the body, a titanium dioxide, 150 parts of the cleaning bone, 4 parts of nanosoxide, 0.5 hydrophobic agents, 10 water, 2 water reducer, 4 parts of the pigment.

[0035]The mineral active powder is blended with silica ash, ore powder, glass microbead, zeolite powder, mineral active powder zeolite, zeolite, mineral active powder, zeolite, silicon ash: mineral powder: glass microbeam: zeolite powder It is 1: 0.125: 0.75: 0.15: 0.1.

[0036]The titanium dioxide is atrial titanium dioxide having a particle size of 10 to 1000 nm. On the one hand, the photocatalytic function is utilized, and most of the organic contaminants is completely oxidized and degraded into an inorganic small molecule such as water and carbon dioxide. On the other hand Its ...

Embodiment 2

[0049]In addition to the formulations of the ultra-high performance mineral powder, other conditions are in Example 1.

[0050]The ultra-high performance mineral powder includes a raw material component of the following weight parts: 100 parts of mineral active powder, 13 parts of titanium dioxide, 220 parts of the cleaning bone, 8 parts of nanosoxide, 2 hydrophilic agents, 15 parts of water, 4 water reduction agents, 10 pigments.

Embodiment 3

[0052]In addition to the formulations of the ultra-high performance mineral powder, other conditions are in Example 1.

[0053]The ultra-high performance mineral powder includes a raw material component of the following weight parts: 85 mineral active powder, 9.5 parts of titanium dioxide, from 170 of the cleaning bone, 5 parts of nanosoxide, and 0.9 hydrophobic agents. 11 parts of water, 2.5 parts of water reducer, 5.5 copies.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of artificial stone technology, and discloses a self-cleaning outdoor artificial stone slab and a preparation method thereof. The self-cleaning outdoor artificial stone slab is prefabricated from ultra-high performance mineral powder with a compressive strength of 100-150 MPa. The ultra-high-performance mineral powder includes the following raw material components in parts by weight: 80-100 parts of mineral active powder, 8-13 parts of titanium dioxide, 150-220 parts of self-cleaning aggregate, 4-8 parts of nano-silica 0.5-2 parts of water-repellent agent, 10-15 parts of water, 2-4 parts of water-reducing agent, and 4-10 parts of pigment. The artificial stone slab of the invention has good volume stability, good self-cleaning performance, low shrinkage, no warping and deformation during use, extremely low water absorption, good durability, no aging problems, good surface stain resistance, and low overall comprehensive cost. The cost is low, and it is suitable for promotion and use.

Description

Technical field[0001]The present invention relates to the field of artificial stone technology, and more particularly to a self-cleaning outdoor artificial slate and a preparation method thereof.Background technique[0002]With the material manufacturing technology and equipment, people's aesthetic and upgraded quality requirements, artificial slate has high strength, high flame retardant, high weather resistant, high-resistant, color optional, realistic color effect, good decoration effect It is suitable for the advantages of factory production, construction convenience, etc., making it the inner and outer wall decoration materials of today's high-end buildings.[0003]With the development of industrial economy, industrial waste gases, car exhaust, smog and other pollutions come one after another, and the construction of architectural stone decorative boards cannot be avoided. These pollutants are easy to form a strong adhesion on the surface of the artificial slate. It is difficult to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B38/08C04B20/10C04B14/04C04B18/02C04B111/20C04B111/27C04B111/54
CPCC04B20/1077C04B28/00C04B2111/2061C04B2111/27C04B2111/542C04B18/146C04B18/141C04B14/24C04B14/047C04B14/305C04B14/062C04B24/42C04B2103/54C04B2103/302C04B18/027C04B20/1066
Inventor 刘福财肖敏汪鹏飞黎浩黄贺明
Owner GUANGDONG GAITEQI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap