Antique blue brick with Taihu silt as main raw material and firing method thereof

A technology of antique blue bricks, the main raw material, applied in the field of antique blue bricks, to achieve the effect of improving work efficiency and stabilizing product quality

Active Publication Date: 2021-11-23
武汉纳士德热能科技设备有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In terms of the preparation of antique blue bricks, there is no method for using Taihu Lake silt as the main raw material to prepare antique blue bricks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antique blue brick with Taihu silt as main raw material and firing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of archaize green with Taihu silt as the main raw material, the raw materials are calculated by mass percentage: 50wt% of Taihu silt, 18wt% of ordinary clay powder, 2wt% of waste float glass powder, 4wt% of coal powder, 1.2wt% of waste rubber powder , pig iron powder 0.8wt%, steel slag particles 16wt%, and discarded green bricks 8wt%.

[0042] The above-mentioned preparation method of antique green bricks with Taihu Lake silt as the main raw material, the preparation process includes batching, molding, drying, loading and firing process, the process of firing steps is as follows: the kiln car with brick adobe obtained after loading The car machine is pushed into the kiln, and it belongs to the preheating section of the tunnel kiln from the kiln head to the high temperature insulation section. Firing section, the holding temperature range of the firing section is 980°C, the flame atmosphere of the firing section is a weak oxidizing flame, and the holding time rang...

Embodiment 2

[0045] A kind of archaize green with Taihu silt as the main raw material, its raw materials are calculated by mass percentage: 57.5wt% of Taihu silt, 16wt% of kaolin powder, 2.1wt% of waste float glass powder, 3wt% of coal powder, 0.8wt of waste rubber powder %, pig iron powder 0.6wt%, steel slag particles 12wt%, and discarded green bricks 8wt%.

[0046] The above-mentioned preparation method of antique green bricks with Taihu Lake silt as the main raw material, the preparation process includes batching, molding, drying, loading and firing process, the process of firing steps is as follows: the kiln car with brick adobe obtained after loading The turning machine is pushed into the kiln, and it belongs to the preheating section of the tunnel kiln from the kiln head to the high-temperature insulation section. Firing section, the holding temperature range of the firing section is 1050°C, the flame atmosphere of the firing section is a weak oxidizing flame, and the holding time ra...

Embodiment 3

[0049] A kind of archaize blue that takes Taihu silt as main raw material, and its raw material is counted by mass percent: Taihu silt 60wt%, montmorillonite powder 15wt%, waste float glass powder 2wt%, coal powder 3wt%, waste rubber powder 0.8wt% , pig iron powder 0.6wt%, steel slag particles 10wt%, and discarded green bricks 8.6wt%.

[0050] The above-mentioned preparation method of antique green bricks with Taihu Lake silt as the main raw material, the preparation process includes batching, molding, drying, loading and firing process, the process of firing steps is as follows: the kiln car with brick adobe obtained after loading The car machine is pushed into the kiln, and the section from the kiln head to the high-temperature insulation section belongs to the preheating section of the tunnel kiln. The temperature rise rate range of the preheating section is 1.2°C / min, and it takes 15 hours to heat up; Firing section, the holding temperature range of the firing section is 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antique green brick with Taihu silt as the main raw material, and the raw materials are Taihu silt, clay powder, waste float glass powder, coal powder, waste rubber powder, pig iron powder, steel slag particles and discarded green bricks ; Its preparation process is characterized in that the firing steps are as follows: the heating rate of the preheating section is 1 ~ 1.2 o C / min, it takes 13.5~20 hours to heat up; after the preheating section ends, it enters the high temperature firing section of the tunnel kiln, and the holding temperature of the firing section is 980~1090 oC , the flame atmosphere in the firing section is a weak oxidizing flame, and the holding time is 4 to 8 hours; o Within the temperature of C, the pressure of water vaporization to form saturated water vapor is controlled at 60‑120 Pa, and the cooling rate of this temperature range is 0.5~1.1 o C / min; temperature below 450 o C, enter the cooling section, the cooling medium in this stage is air, and the cooling rate is 0.5~1.2 o C / min. The average flexural strength of the antique blue brick prepared by the invention is 18-20 MPa, the average compressive strength is 20-24 MPa, and the impact resistance is 1.1-1.8 MPa.

Description

technical field [0001] The invention relates to an antique blue brick with Taihu Lake silt as the main raw material and a firing method thereof in a tunnel kiln, belonging to the technical field of antique blue bricks. Background technique [0002] The ancient buildings in our country have a long history and rich cultural connotations. The buildings featuring ancient blue tiles and blue bricks are even more unique, with their unique performance and aesthetic value. Green brick belongs to fired brick, which is a common building material. Because of its special production process and simple color, it is favored by people. The traditional sintering of blue tiles and blue bricks is generally sintered in small coal kilns or downdraft kilns. Small coal kilns are gradually eliminated due to heavy pollution, while downdraft kilns have the disadvantages of difficult operation, difficult temperature control, and low output. [0003] With the strengthening of environmental protection ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/132C04B33/138C04B33/24C04B33/32
CPCC04B33/13C04B33/132C04B33/1321C04B33/1324C04B33/138C04B33/24C04B33/32C04B2235/6562C04B2235/6567Y02P40/60
Inventor 牛汉新何峰
Owner 武汉纳士德热能科技设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap