Primer for light-transmitting ceramic tiles and preparation method thereof

A technology of ceramic tiles and primer, which is applied in the field of ceramics, can solve the problems that the primer does not have light transmission, blocks light irradiation, and affects the appearance of light-transmitting bricks, so as to improve the suspension performance, eliminate the impact, and improve the aesthetics. Effect

Active Publication Date: 2022-02-01
FOSHAN OCEANO CERAMICS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But for light-transmitting ceramic tiles, this type of primer is not translucent and will block the light. When this type of primer is coated on the bottom of the ceramic tile, it will be exposed to light when it is irradiated by light. The surface of the ceramic tiles presents back lines, which seriously affect the appearance of the transparent tiles. Since the primer has been stuck to the ceramic tiles during the firing process, it is very troublesome to remove it. Therefore, it is necessary to check the composition of the primer. Improvement, so as not to affect the beauty of ceramic tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Primer for light-transmitting ceramic tiles and preparation method thereof
  • Primer for light-transmitting ceramic tiles and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A primer for light-transmitting ceramic tiles, the raw materials and the added mass parts of the primer for light-transmitting ceramic tiles are: 30 parts of clay, 70 parts of anorthite and 0.5 parts of surfactant, wherein the surfactant It is made by mixing sodium polycarboxylate and sodium tripolyphosphate at a weight ratio of 1:1, and the content of iron oxide and titanium oxide in the clay is 0.45%.

[0022] A method for preparing a primer for light-transmitting ceramic tiles, wherein the specific operating steps are:

[0023] (1) Take by weighing 30 parts of clay, 70 parts of anorthite and 0.5 part of surfactant, place in a ball mill, then add a certain amount of water, mix and ball mill to obtain a slurry,

[0024] (2) The obtained slurry is discharged, and then iron removal treatment is carried out through an iron removal tank equipped with iron removal rods to obtain a base slurry for light-transmitting ceramic tiles, wherein the solid phase content of the slurr...

Embodiment 2

[0026] A primer for light-transmitting ceramic tiles, the raw materials and the added mass parts of the primer for light-transmitting ceramic tiles are: 10 parts of clay, 90 parts of anorthite and 2 parts of surfactant, wherein the surfactant It is made by mixing sodium polycarboxylate and sodium tripolyphosphate at a weight ratio of 3:1, and the content of iron oxide and titanium oxide in the clay is 0.35%.

[0027] A method for preparing a primer for light-transmitting ceramic tiles, wherein the specific operating steps are:

[0028] (1) Take by weighing 10 parts of clay, 90 parts of anorthite and 2 parts of surfactant, place in a ball mill, then add a certain amount of water, mix and ball mill to obtain a slurry,

[0029] (2) The obtained slurry is discharged, and then iron removal treatment is carried out through an iron removal tank equipped with iron removal rods to obtain a base slurry for light-transmitting ceramic tiles, wherein the solid phase content of the slurry i...

Embodiment 3

[0031] A primer for light-transmitting ceramic tiles, the raw materials and the added mass parts of the primer for light-transmitting ceramic tiles are: 20 parts of clay, 80 parts of anorthite and 1.5 parts of surfactant, wherein the surfactant It is made by mixing sodium polycarboxylate and sodium tripolyphosphate at a weight ratio of 2:1, and the content of iron oxide and titanium oxide in the clay is 0.48%.

[0032] A method for preparing a primer for light-transmitting ceramic tiles, wherein the specific operating steps are:

[0033] (1) Take by weighing 20 parts of clay, 80 parts of anorthite and 1.5 parts of surfactant, place in a ball mill, then add a certain amount of water, mix and ball mill to obtain a slurry,

[0034] (2) The obtained slurry is discharged, and then iron removal treatment is carried out through an iron removal tank equipped with iron removal rods to obtain a base slurry for light-transmitting ceramic tiles, wherein the solid phase content of the slur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present disclosure provides a primer for light-transmitting ceramic tiles. The raw materials of the primer for light-transmitting ceramic tiles include: clay, anorthite and a surfactant. The primer for light-transmitting ceramic tiles not only has good high temperature resistance, but also can effectively eliminate the influence of traditional primers on the surface of light-transmitting ceramic tiles, improving the aesthetics of transparent ceramics.

Description

technical field [0001] The disclosure relates to the technical field of ceramics, in particular to a primer for light-transmitting ceramic tiles and a preparation method thereof. Background technique [0002] As a decorative material, architectural ceramics are favored by consumers due to their rich and beautiful surface patterns and good wear resistance. A series of products such as leather pattern, imitation cloth pattern, imitation natural marble, imitation jade, etc. Among them, imitation jade products have put forward higher requirements for the preparation process of ceramic tiles, and jade products themselves are a kind of light-transmitting Products, while traditional ceramic tiles show non-transparent characteristics due to crystal phase, pores and impurities, so it is necessary to adjust the structure of the product, adjust the crystal phase of ceramic tile products, improve internal pores and reduce impurities. Influence, so as to improve the light transmission p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/87C04B35/195
CPCC04B41/87C04B41/5037C04B35/195C04B2235/349C04B2235/447C04B41/5024C04B41/5015C04B41/4884
Inventor 柯善军蒙臻明王妹妹
Owner FOSHAN OCEANO CERAMICS