An epoxy-based long-lasting fluorescent anti-skid adhesive and its preparation method

A technology of long epoxy-based and long afterglow materials, applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve problems such as poor water resistance, and achieve the effect of high afterglow brightness, long duration and good stability

Active Publication Date: 2021-08-17
江苏大力士云石护理材料有限公司
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the above technical solution, epoxy resin is used as the main resin of the anti-slip glue, and the rare earth silicate-based long-lasting afterglow material and the rare-earth aluminate-based long-lasting afterglow material are dispersed in it. After the epoxy resin is cured, the rare-earth aluminate-based long-lasting Material coating, forming a protective layer, overcomes the problem of poor water resistance of rare earth aluminate-based long-lasting materials, thus giving it better stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An epoxy-based long-lasting fluorescent anti-skid adhesive and its preparation method
  • An epoxy-based long-lasting fluorescent anti-skid adhesive and its preparation method
  • An epoxy-based long-lasting fluorescent anti-skid adhesive and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] This embodiment provides an epoxy-based long-lasting fluorescent anti-slip adhesive, including A component and B component, in parts by weight, the A component includes 100 parts of epoxy resin, rare earth silicate-based long-lasting material Sr 2 MgSi 2 o 7 :Eu 2+ , Dy 3+ 5 parts, rare earth aluminate based long afterglow material SrAl 2 o 4 :Eu 2+ , Dy 3+ 10 parts, 60 parts of high permeability silica powder, 40 parts of quartz sand, 8 parts of polyisoprene, 8 parts of SBS, 4 parts of ABS and 5 parts of fumed silica; the B component includes 100 parts of epoxy resin curing agent 3 parts, 3 parts of vinyl silane, 40 parts of high permeability silica powder, 30 parts of quartz sand and 8 parts of fumed silica.

[0032] This embodiment also provides the preparation method of the above-mentioned fluorescent anti-slip glue: put the above-mentioned raw materials of component A into a stirred tank, and stir at a high speed of not less than 1500r / min under a negativ...

experiment example 1

[0050] Take 20 g of the raw material in Comparative Example 1 and place it in a 35mm petri dish, numbered A.

[0051] Take the raw materials in Example 1, and the preparation method is to put the raw materials of component A into a stirred tank, and in a negative pressure state with a vacuum degree of 0.08MPa, stir at a high speed of 1500r / min until uniform, and the stirring time is 20 minutes, and then pass Three-roller machine, the speed ratio of the slow, medium and fast rollers of the three-roller machine is 1:3:9, the speed of the slow roller is controlled at 30r / min, and the roller gap is adjusted to 0.015mm. Put the raw materials of component B into the stirring tank, and stir them at a high speed of 1500r / min under the negative pressure of vacuum degree of 0.08MPa until uniform, and the stirring time is 20 minutes. Mix 10g of component A and 10g of component B and put it in a 35mm Petri dish, numbered B.

[0052] Take the raw materials in Example 1, and the preparatio...

experiment example 2

[0061] Take the epoxy-based epoxy-based long-lasting fluorescent anti-skid rubber raw material provided in Examples 1-17, and the preparation method is to put the A-component raw material into a stirred tank, and under a negative pressure state with a vacuum degree of 0.08MPa, the rotation speed is 1500r / min high-speed stirring until uniform, the stirring time is 20 minutes, and then through the three-roller machine, the speed ratio of the slow, medium and fast rollers of the three-roller machine is 1:3:9, the speed of the slow roller is controlled at 30r / min, the gap between the rollers Adjust it to 0.015 mm; put the raw materials of component B into the stirring tank, and stir at a speed of 1500r / min at a high speed under a negative pressure of 0.08MPa until uniform, and the stirring time is 20 minutes. Perform the following performance tests:

[0062] Refer to the test method of GB 24264-2009 "Adhesives for Facing Stone" and the test method of the People's Republic of Chin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an epoxy-based long-lasting fluorescent anti-slip adhesive and a preparation method thereof. The fluorescent anti-slip adhesive includes components A and B, and the component A includes epoxy resin, long-lasting materials and fillers. The B component includes an epoxy resin curing agent, wherein the long afterglow material is obtained by mixing a rare earth silicate based long afterglow material and a rare earth aluminate based long afterglow material in a weight ratio of 1:3 to 3:1. The fluorescent anti-slip adhesive of the invention overcomes the problem of poor water resistance of rare earth aluminate-based long-lasting materials, has good stability, has good fluorescent effect, and has high afterglow brightness and long duration.

Description

technical field [0001] The invention relates to the field of anti-slip adhesives, in particular to an epoxy-based long-lasting fluorescent anti-slip adhesive and a preparation method thereof. Background technique [0002] For the sake of safety, anti-slip products and fluorescent indicators are usually installed in corridors, stairwells or places with low light, especially at night, in the event of power failure or building fire, the two work together to protect people's lives. The anti-slip products on the market today are mainly anti-slip strips, anti-slip tapes and anti-slip rubber, and the cost of various fluorescent indicators on the market is relatively high, and the installation method is cumbersome. The two must be used at the same time to play the role of maximum security, but currently there is no product on the market that combines the functions of fluorescent indicators and anti-skid. [0003] In addition, the most widely used fluorescent materials at present ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J11/04
CPCC09J11/04C09J163/00C08K13/02C08K3/34C08K3/24
Inventor 杜昆文杜昆武邱国峰毛攀峰周哲熊善高王莉亚
Owner 江苏大力士云石护理材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com