A kind of preparation technology of circle vertical stripe coat
A preparation process and vertical stripe technology, which is applied in protective clothing, special outerwear, dyeing methods, etc., can solve the problems of expensive jacquard machines and high costs of small and medium-sized enterprises, and achieve the effects of generous patterns, reduced energy consumption, and reduced costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0019] Such as figure 1 , 2 As shown, the present invention is a preparation process of a coat with circle vertical stripes. The weight percentage of the coat is: 70% wool, 10% viscose, 10% nylon, 10% polyester; the coat The warp arrangement of the woolen is: 2A.1C.(8A.1C)*3.2A.6B.1C.(8A.1C)*2.6B; the weft arrangement of the coat is: 2A.1D.1A; the warp arrangement and The wool yarns used in the weft yarn arrangement are: A yarn is a wool yarn with a count of 10.5S and a color of A color; B yarn is a wool yarn with a count of 10.5S and a color of B color; C yarn is a wool yarn with a count of 40S and 2 Ply-jointed polyester connecting yarn; yarn D is twisted dyed A-color circle yarn with a count of 10.5S, and the front side of the fabric is shown as two-color vertical stripes of circle yarn A and B, and the front side of the technology is used as the front side of the dress; the reverse side of the technology Displayed as A-color vertical stripes, the reverse side of the craf...
Embodiment 2
[0026] The difference between Example 2 and Example 1 is that raw materials are prepared, wool fiber, viscose fiber, nylon fiber, and polyester fiber raw materials are selected according to the composition and weight percentage of the fabric, and part of the wool fiber is pretreated, including the preparation of formic acid-water solution As a pretreatment solution, the concentration of formic acid is 90%. After the preparation, the pretreatment solution is evenly sprayed on the wool fiber, and after the wool fiber is completely soaked, stand at 25°C for 1 hour, then squeeze out the pretreatment solution and wash it. , drying, the drying temperature is 75°C; then the treated wool fiber and untreated wool fiber are blended, wherein the weight ratio of the treated wool fiber to the untreated wool fiber is 1:0.5, and then The blended wool fiber and other fibers are spun into A yarn, B yarn or D yarn, and the D yarn is loop yarn.
Embodiment 3
[0028]The difference between Example 3 and Example 2 is that the pretreatment solution is evenly sprayed on the wool fiber after configuration, and after the wool fiber is completely soaked, stand at 25°C for 2 hours, then squeeze out the pretreatment solution, wash and dry Drying at a drying temperature of 80° C.; then blending the treated wool fibers with untreated wool fibers, wherein the weight ratio of the treated wool fibers to the untreated wool fibers is 1:1.