Formula of nylon hose material

A nylon and hose technology, applied in the field of preparation and production of polymer materials, can solve the problems of limited supply, high price, limited output, etc., and achieve the effects of good dimensional stability, good low temperature flexibility, and stable extrusion molding.

Inactive Publication Date: 2020-04-14
WUXI YINDA NYLON
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nylon 11 and Nylon 12 have not yet been industrialized in China, and the supply is limited and the price is high. However, long-carbon-chain diamine, one...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula of nylon hose material
  • Formula of nylon hose material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The formula is as follows: 100 parts of copolymerized nylon PA610 / 613 (where PA613 accounts for 10% of the copolymerized nylon), 10 parts of plasticizer N-butylbenzenesulfonamide, 10 parts of impact modifier EPDM-g-MA, antioxidant 1681.5 parts, antioxidant 1098 1.5 parts.

[0018] Add the copolymerized nylon PA610 / 613, antioxidant, and impact modifier EPDM-g-MA into the high mixer according to the ratio required by the formula, and stir for 8 minutes under the condition of 400r / min. After the materials are completely mixed, pass The feeder is fed into the twin-screw extruder at a constant speed, and the plasticizer is fed in at a calculated speed through the liquid feeding port reserved in the extruder with a liquid metering pump to ensure that the ratio meets the formula requirements. All materials are melted and mixed uniformly by twin-screws, then extruded, cooled, granulated, dried and packaged to obtain the final product.

[0019] The mechanical properties of the ...

Embodiment 2

[0021] The formula is as follows: 100 parts of copolymerized nylon PA610 / 613 (where PA613 accounts for 15% of the copolymerized nylon), 10 parts of plasticizer N-butylbenzenesulfonamide, 15 parts of impact modifier EPDM-g-MA, antioxidant 1682 parts, antioxidant 1098 2 parts.

[0022] Add the copolymerized nylon PA610 / 613, antioxidant, and impact modifier EPDM-g-MA into the high mixer according to the ratio required by the formula, and stir for 8 minutes under the condition of 400r / min. After the materials are completely mixed, pass The feeder is fed into the twin-screw extruder at a constant speed, and the plasticizer is fed in at a calculated speed through the liquid feeding port reserved in the extruder with a liquid metering pump to ensure that the ratio meets the formula requirements. All materials are melted and mixed uniformly by twin-screws, then extruded, cooled, granulated, dried and packaged to obtain the final product.

[0023] The mechanical properties of the prep...

Embodiment 3

[0025] The formula is as follows: 100 parts of copolymerized nylon PA612 / 613 (where PA613 accounts for 10% of the copolymerized nylon), 10 parts of plasticizer N-butylbenzenesulfonamide, 15 parts of impact modifier SEBS-g-MA, antioxidant 168 2 parts, antioxidant 1098 2 parts.

[0026] Add the copolymerized nylon PA612 / 613, antioxidant, and impact modifier SEBS-g-MA into the high mixer according to the proportion required by the formula, and stir for 8 minutes under the condition of 400r / min. After the materials are completely mixed, pass The feeder is fed into the twin-screw extruder at a constant speed, and the plasticizer is fed in at a calculated speed through the liquid feeding port reserved in the extruder with a liquid metering pump to ensure that the ratio meets the formula requirements. All materials are melted and mixed uniformly by twin-screws, then extruded, cooled, granulated, dried and packaged to obtain the final product.

[0027] The mechanical properties of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a formula of a nylon hose material, wherein the nylon hose material at least takes a polyamide resin, a plasticizer and an impact modifier as production raw materials, the polyamide resin is obtained by copolymerizing short-chain odd-even nylon and short-chain even-even nylon, the plasticizer is one or a combination comprising a plurality of materials selected from higher alcohol, hydroxybenzoate, aromatic sulfonamide and phenol, and the impact modifier is one or a combination comprising a plurality of materials selected from polyolefin, an olefin copolymer and an elastomer. According to the invention, the nylon hose material has the characteristics of low price, high strength, good low-temperature flexibility, oil resistance, good dimensional stability, stable extrusion molding and the like compared with the long carbon chain nylon hose, and completely meets the requirements of the nylon hose for vehicles.

Description

technical field [0001] The invention relates to a formula of nylon hose material, which belongs to the field of preparation and production of polymer materials. Background technique [0002] Nylon hoses are widely used in the automotive industry. Nylon hose is mainly made of long carbon chain nylon as the matrix resin, which is toughened and modified. In foreign countries, nylon 11 and nylon 12 are used as the main raw materials. In recent years, nylon hose materials with long carbon chain nylon 1012 and nylon 1010 as the main raw materials have been developed in China. Nylon 11 and nylon 12 have not yet been industrialized in China, their supply is limited, and their prices are high. However, long-carbon-chain diamines, one of the main raw materials for domestic long-carbon-chain nylon, are mainly derived from castor oil, with limited production and high prices. Contents of the invention [0003] The present invention discovers a formula of nylon hose material, which us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L51/04C08L51/00C08K5/435
CPCC08L77/06C08L2203/18C08L2205/025C08L2205/03C08L51/04C08K5/435C08L51/006
Inventor 沈俊毅陈尚标胡瑞莉殷炼伟
Owner WUXI YINDA NYLON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap