Antibacterial agent composition and application
A technology of composition and antibacterial agent, which is applied in the field of antibacterial agent preparation, achieves the effects of environmental protection biocompatibility, improvement of mechanical properties and antibacterial properties, and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0018] Embodiment 1: antibacterial agent is to escherichia coli bacteriostatic bactericidal effect
[0019] 1, the chitosan preparation method of loaded nitrogen, iodine-doped carbon dot comprises the following steps:
[0020] Preparation of chitosan nanoparticles: Dissolve 1 part of chitosan in 100 parts of 1% acetic acid solution, add (v / v) 0.4% Tween-20 aqueous solution, and mix (w / v) 0.04 % sodium tripolyphosphate aqueous solution was added dropwise in the above solution, the pH was adjusted to 5.0, stirred for 10min, which was chitosan nanoparticles;
[0021] Preparation of iodine nitrogen doped carbon dots: Weigh 1 part of iodixanol, add 100 parts of ultrapure water, mix and dissolve, add 0.3 parts of ethylenediamine, ultrasonicate for 10 minutes, and transfer to a polytetrafluoroethylene reactor, at 180 ° C Heating for 8 hours, after natural cooling, filter with a pore size of 0.22 μm filter membrane, and then use a dialysis bag with a molecular weight cut-off of 3...
Embodiment 2
[0031] Embodiment 2: antibacterial agent is to staphylococcus aureus bacteriostatic bactericidal effect
[0032] 1, the chitosan preparation method of loaded nitrogen, iodine-doped carbon dot comprises the following steps:
[0033] Preparation of chitosan nanoparticles: Weigh 3 parts of chitosan and dissolve in 300 parts of 1% acetic acid solution, add (v / v) 0.6% Tween-20 aqueous solution, and mix (w / v) 0.06 % sodium tripolyphosphate aqueous solution was added dropwise to the above solution, the pH was adjusted to 5.0, and stirred for 15 min to form chitosan nanoparticles;
[0034] Preparation of iodine nitrogen doped carbon dots: Weigh 2 parts of iodixanol, add 120 parts of ultrapure water, mix and dissolve, add 0.5 parts of ethylenediamine, sonicate for 15 min, and transfer to a polytetrafluoroethylene reactor, at 180 Heating at ℃ for 10 h, after natural cooling, first filter with a filter membrane with a pore size of 0.22 μm, and then use a dialysis bag with a molecula...
Embodiment 3
[0045] Embodiment 3: antibacterial agent is used in tipping paper for cigarette
[0046] 1, the chitosan preparation method of loaded nitrogen, iodine-doped carbon dot comprises the following steps:
[0047] Preparation of chitosan nanoparticles: Weigh 5 parts of chitosan and dissolve in 500 parts of 1% acetic acid solution, add (v / v) 0.8% Tween-20 aqueous solution, and mix (w / v) 0.08 % sodium tripolyphosphate aqueous solution is added dropwise in the above-mentioned solution, pH is adjusted to 5.0, stirs 20min, namely chitosan nano-particle;
[0048] Preparation of carbon dots doped with iodine nitrogen: Weigh 3 parts of iodixanol, add 150 parts of ultrapure water, mix and dissolve, add 1 part of ethylenediamine, sonicate for 20 minutes, and transfer to a polytetrafluoroethylene reactor, at 180 ° C Heating for 12 hours, after natural cooling, filter with a filter membrane with a pore size of 0.22 μm, and then perform dialysis treatment with a dialysis bag with a molecula...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap