Preparation method of jute fiber mattress materials

A technology of hemp fiber and jute fiber, which is applied in the field of preparation of hemp fiber mattress materials, can solve the problems of comfort and environmental protection, antibacterial and breathable service life to be improved, and achieve the effect of comfortable mood, good ventilation and high air ion concentration

Active Publication Date: 2015-01-21
HEYE HEALTH TECH CO LTD
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the core material still needs to be improved in terms of comfort, environmental protection, antibacterial ventilation and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of jute fiber mattress materials
  • Preparation method of jute fiber mattress materials
  • Preparation method of jute fiber mattress materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Select jute fiber for use; The preparation method of jute fiber mattress material comprises the following steps:

[0058] (1) Opening: First, the jute fibers are degummed, then combed and shortened into short jute fibers, and then the short jute fibers are sent to the opener for opening;

[0059] (2) Combing into a web by airflow: the short jute fibers after opening are uniformly flowed down from the drum groove through the airflow, and the short jute fibers after opening are evenly arranged by the airflow to form as shown in Fig. figure 1 A netted semi-finished product with an S-shaped cross-section structure;

[0060] (3) Non-woven needle punching: The net-like semi-finished product is subjected to at least two spunlace treatments reinforced by water needles, and the non-woven needle-punched jute fiber semi-finished product is formed through compound entanglement;

[0061] (4) High-temperature baking: The non-woven needle-punched jute fiber semi-finished product is p...

Embodiment 2

[0080] Select jute fiber for use, and the preparation method of jute fiber mattress material may further comprise the steps:

[0081] (1) Opening: First, the jute fibers are degummed, then combed and shortened into short jute fibers, and then the short jute fibers are sent to the opener for opening;

[0082] (2) Airflow combing into a web: the opened short jute fibers are uniformly flowed down from the drum groove through the airflow, and the opened short jute fibers are evenly arranged by the airflow to form a mesh semi-finished product with an S-shaped cross-section structure;

[0083] (3) Non-woven needle punching: The net-like semi-finished product is subjected to at least two spunlace treatments reinforced by water needles, and the non-woven needle-punched jute fiber semi-finished product is formed through compound entanglement;

[0084] (4) High-temperature baking: The non-woven needle-punched jute fiber semi-finished product is placed in a high temperature of 180 °C in ...

Embodiment 3

[0105] Select jute fiber for use, and the preparation method of jute fiber mattress material may further comprise the steps:

[0106] (1) Opening: First, the jute fibers are degummed, then combed and shortened into short jute fibers, and then the short jute fibers are sent to the opener for opening;

[0107] (2) Airflow combing into a web: the opened short jute fibers are uniformly flowed down from the drum groove through the airflow, and the opened short jute fibers are evenly arranged by the airflow to form a mesh semi-finished product with an S-shaped cross-section structure;

[0108] (3) Non-woven needle punching: The net-like semi-finished product is subjected to at least two spunlace treatments reinforced by water needles, and the non-woven needle-punched jute fiber semi-finished product is formed through compound entanglement;

[0109] (4) High-temperature baking: The non-woven needle-punched jute fiber semi-finished product is placed in a high temperature of 200°C in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to preparation of fiber materials, in particular to a preparation method of jute fiber mattress materials. The method sequentially includes: opening, to be more specific, performing degumming treatments on jute fibers, carding and cutting into short jute fibers, and opening the short jute fibers in an opening machine; performing air flow carding to form nets, to be more specific, allowing the opened short jute fibers to feed evenly through a roller groove by the aid of air flows, and evenly arranging the short jute fibers to form net-shaped semi-products with S-shaped sections; non-woven needling, to be more specific, subjecting the net-shaped semi-products to spunlace reinforced by water needles at least twice, and forming non-woven needled jute fiber semi-products through composite intertwining; baking at high temperature, to be more specific, baking the non-woven needled jute fiber semi-products in up-down hot air at 180-200 DEG C in a circulating and penetration manner to make the jute fiber mattress materials. The jute fiber mattress materials prepared by the method are comfortable, environmental friendly, antibacterial, breathable and long in service life.

Description

technical field [0001] The invention relates to the preparation of a fiber material, in particular to a preparation method of a hemp fiber mattress material. [0002] Background technique [0003] Hemp fiber is a natural cellulose fiber with outstanding product characteristics, low production cost, and low requirements on production conditions. It can grow in tidal flats and low-lying places, and does not compete with grain and cotton for land. Compared with cotton fiber, its growth process requires less chemical fertilizers, The dependence on pesticides is low. [0004] CN101343815B (2012-7-4) discloses a silk hemp fiber mixed filling core material, the silk hemp fiber mixed filling core material body (2) is made of hemp fiber and silk mixed fiber, the silk hemp fiber mixed filling core material (3) The mass percent content of the hemp fiber is 20-60%. However, the core material still needs to be improved in terms of comfort and environmental protection, antibacterial ve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/485D04H1/4266D04H1/732B32B9/02B32B7/12D06M15/03D06M15/693D06M15/09D06M13/224D06M13/11D06M11/44D06M11/83D06M11/74D06M11/79D06M11/46D06M11/71D06M101/06
CPCB32B7/12B32B9/02D04H1/4266D04H1/485D04H1/732D06M11/44D06M11/46D06M11/71D06M11/74D06M11/79D06M11/83D06M13/11D06M13/224D06M15/03D06M15/09D06M15/693
Inventor 胡立江方志财李俊蔡京昊
Owner HEYE HEALTH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com