A kind of preparation method of three-dimensional nanostructure nickel cobalt sulfide material

A nickel-cobalt sulfide, three-dimensional nanotechnology, applied in the manufacture of hybrid/electric double layer capacitors, hybrid capacitor electrodes, etc., can solve the problems of energy storage devices limited by energy density and power balance, and achieve excellent electrochemical performance, Large specific surface area, simple and practical method

Active Publication Date: 2021-08-03
XIAMEN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there is no report on the direct use of electrospinning technology to synthesize three-dimensional hierarchical structure nanomaterials of nickel cobalt sulfide, and the positive electrode materials of energy storage devices are limited by the balance between energy density and power

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of three-dimensional nanostructure nickel cobalt sulfide material
  • A kind of preparation method of three-dimensional nanostructure nickel cobalt sulfide material
  • A kind of preparation method of three-dimensional nanostructure nickel cobalt sulfide material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] 1) Preparation of Ni-Co-S electrode with tubular fiber structure

[0063] The samples of tubular fiber structure with different vulcanization times, acetylene black and polyvinylidene fluoride (PVDF) were weighed according to the mass ratio of 8:1:1, and the weighed powder was put into an agate mortar for grinding until three Mix the powder completely, then transfer the powder to a 25mm×25mm weighing bottle, put a magnetic stirrer, and slowly add N-methylpyrrolidone (NMP) dropwise to allow the solution to completely soak the powder, then place the weighing bottle on Stir for 4 hours on a magnetic stirrer to obtain a viscous liquid. Afterwards, the viscous liquid was scraped and coated on the cleaned carbon cloth with a blade, and then dried in a vacuum drying oven to obtain a flexible electrode sheet.

[0064] The size of the above-mentioned carbon cloth is 2cm×1.5cm, and the cleaning can be performed by adding acetone, deionized water, and absolute ethanol in sequence...

Embodiment 2

[0069] 1) Preparation of Ni-Co-S electrodes with nano-petal-like structure

[0070] The samples of nano petal-like structure, acetylene black and polyvinylidene fluoride (PVDF) with different vulcanization time were weighed according to the mass ratio of 8:1:1, and the weighed powder was put into an agate mortar for grinding until three Mix the seed powder completely, then transfer the powder to a weighing bottle of 25mm×25mm, put in a magnetic stirrer, and slowly add N-methylpyrrolidone (NMP) dropwise, so that the solution completely infiltrates the powder, and then place the weighing bottle Stir for 4 h on a magnetic stirrer to obtain a viscous liquid. Afterwards, the viscous liquid was scraped and coated on the cleaned carbon cloth with a blade, and then dried in a vacuum drying oven to obtain a flexible electrode sheet.

[0071] The size of the above-mentioned carbon cloth is 2cm×1.5cm, and the cleaning can be performed by adding acetone, deionized water, and absolute eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for preparing a three-dimensional nanostructure nickel-cobalt sulfide material relates to a three-dimensional nanostructure nickel-cobalt sulfide material. Preparation of polyacrylonitrile nanofiber; preparation of Ni-Co-S tubular fiber structure; preparation of Ni-Co-S hexagonal petal-like structure. Preparation of NiCO by Electrospinning Technology 2 S 4 The three-dimensional hierarchical structure nanomaterials, which have a unique three-dimensional nanostructure, large specific surface area and excellent electrochemical performance, provide new ideas for the preparation of supercapacitor cathodes with excellent performance. With large specific surface area and excellent electrochemical performance, especially the Ni-Co-S electrode with hexagonal petal-like structure, it shows excellent performance when it is used as the positive electrode of supercapacitor. Therefore, binary nickel-cobalt sulfide nanostructures are expected to be one of the candidate materials for supercapacitor applications. The method is simple and practical and can repeat a large number of operations.

Description

technical field [0001] The invention relates to a three-dimensional nanostructure nickel-cobalt sulfide material, in particular to a preparation method of a three-dimensional nanostructure nickel-cobalt sulfide material. Background technique [0002] Supercapacitors have attracted extensive attention due to their excellent power density, good cycle stability, and environmental friendliness. Due to the low specific capacitance of carbon-based materials, the poor cycle stability of conductive polymer materials, and the low conductivity of transition metal oxide materials, transition metal sulfides have been extensively studied as novel supercapacitor materials (Wu Z, Zhu Y, Ji X. NiCo2O4-based materials for electrochemical supercapacitors [J]. JOURNAL OF MATERIALS CHEMISTRY. A, 2014, 2(36): 14759-14772). At the same time, three-dimensional nanostructured materials have also been valued for their potential applications. Therefore, in order to improve the performance of superc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/24H01G11/26H01G11/30H01G11/86
CPCH01G11/24H01G11/26H01G11/30H01G11/86Y02E60/13
Inventor 叶美丹陈星贺春锋张鑫
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap