A kind of aluminum powder mixing method

An aluminum powder and mixing technology, which is applied in the field of aluminum powder mixing, can solve the problems of large fluctuations in the particle size of aluminum powder, achieve uniform particle size distribution, good stability, and avoid bimodal distribution

Active Publication Date: 2022-01-11
DONGYING YINQIAO METALLIC PIGMENT CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, most of the aluminum powder production adopts conical mixing equipment with a mixing volume of 1-2 tons. When mixing and producing a single batch of aluminum powder exceeding 10 tons, it can only be carried out in a small batch of 1-2 tons. Mixed production, large particle size fluctuations between small batches of aluminum powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for mixing aluminum powder, which specifically requires obtaining aluminum powder with a specification of 23-25um, the details are as follows:

[0025] The first step is to obtain raw materials, select skeleton aluminum powder and graded aluminum powder as raw materials, wherein: the skeleton aluminum powder is aluminum powder with a median diameter of D50 and 28-30um, and the graded aluminum powder adopts a median diameter of D50 and 8- Combination of 9um aluminum powder and 3-4um aluminum powder, wherein: the concentration factor of the skeleton aluminum powder is 1.3; the concentration factor of the 8-9um aluminum powder is 1.2, and the concentration factor of the 3-4um aluminum powder is 1.3;

[0026] In terms of weight percentage, 28-30um aluminum powder: 8-9um aluminum powder: 3-4um aluminum powder is 75:20:5.

[0027] The second step, premixing, specifically: including 10 times of premixing; the premixing process is specifically to stir the raw materials...

Embodiment 2-3

[0030] Embodiment 2-3 differs from Embodiment 1 in that:

Embodiment 2

[0031] Example 2: 28-30um aluminum powder in weight percentage: 8-9um aluminum powder: 3-4um aluminum powder is 60:30:10; including 5 premixes, the raw material for a single premix is 2 tons, the total amount of 10 premixes is 20 tons. The target product obtained in Example 3 is aluminum powder of D50 and 24-24.5um, the concentration coefficient is 1.8, and the tap density reaches 1.62g / cm 3 , particle size fluctuation between batches is less than 0.65%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides an aluminum powder mixing method, comprising the following steps: the first step, obtaining raw materials, selecting skeleton aluminum powder and graded aluminum powder as raw materials; The raw materials of aluminum powder and graded aluminum powder are stirred evenly in a conical mixer to obtain premixed aluminum powder; the third step is mixing, and a certain amount of aluminum powder is taken out from the premixed aluminum powder obtained in the second step and stirred evenly get the target product. The present invention uses a variety of aluminum powders of the same specification as raw materials, selects appropriate proportions according to different requirements, and performs mixing processing according to a specific mixing process (obtaining raw materials, premixing, mixing combinations, and even including remixing) , after multiple cross-mixing treatments, the graded aluminum powder particles can be fully and evenly distributed among the skeleton aluminum powder particles, so as to achieve full filling, so that the particle size fluctuation between batches of final aluminum powder products does not exceed one thousandth Eighth, the tap density is as high as 1.65g / cm 3 .

Description

technical field [0001] The invention relates to the technical field of metal powder processing, in particular to an aluminum powder mixing method with good uniformity and high tap density. Background technique [0002] Micro-spherical aluminum powder is made by atomizing aluminum droplets or liquid strips into particles through inert high-pressure gas in the molten state. The appearance is silver-gray, and the particles are more regular spherical or nearly spherical. Due to its regular shape, smooth surface, high active aluminum content, and stable product quality, fine spherical aluminum powder is widely used in aerospace solid propellant fuel, photovoltaic solar crystalline silicon battery slurry, high-grade metallic pigments, thermal and conductive materials, fire-resistant Materials and powder metallurgy and other fields occupy an important position in national economic construction and national defense industry construction. [0003] At present, the focus of fierce com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/052
CPCB22F1/052
Inventor 刘颖俊
Owner DONGYING YINQIAO METALLIC PIGMENT CO LTD