A method for recycling and reusing porcelain bottle insulators
A treatment method and insulator technology, applied in the field of electric power equipment, can solve problems such as deformation of metal fittings, reduction of ceramic powder quality, difficulty in meeting recycling conditions, etc., to achieve the effects of easy cleaning, improved cleaning effect, and avoiding deformation
Active Publication Date: 2021-11-23
万泰智能电子科技(新沂)有限公司
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] The invention provides a method for recycling and reusing porcelain insulators, aiming to solve the following problems existing in the current recycling and reusing of porcelain insulators: cement adhesive is filled between the ceramic parts and metal fittings of porcelain insulators, and the porcelain insulators are directly After the insulator is crushed, the ceramic powder obtained by grinding is mixed with cement binder powder, which reduces the quality of the ceramic powder and is difficult to meet the recycling conditions; and the metal fittings are deformed after the broken insulators of porcelain bottles, resulting in the inclusion of ceramic parts in the metal fittings , which also adversely affects the recycling of metal fittings
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0034] The embodiments of the present invention will be described in detail below with reference to the accompanying drawings, but the present invention can be implemented in many different ways defined and covered by the claims.
[0035] Such as figure 1 As shown, this embodiment provides a method for recycling and reusing porcelain bottle insulators, including the following specific steps:
[0036] Step 1. Surface cleaning: Soak the recovered porcelain bottle insulators in deionized water to remove surface stains.
[0037] Step 2. Parts separation: separate the metal parts on the cleaned porcelain insulator from the internal ceramic parts, and clean up the cement adhesive attached to the metal parts and internal ceramic parts.
[0038] Step 3, crushing and grinding: apply external force to the separated ceramic parts to make them break and then grind to become ceramic powder.
[0039] Wherein, the process of separating the accessories described in step 2 adopts a method su...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention belongs to the technical field of electric power equipment, and specifically relates to a method for recycling and reusing porcelain bottle insulators, which includes the following specific steps: step 1, surface cleaning: soaking the recovered porcelain bottle insulators in deionized water to remove surface stains; step 2, Separation of accessories: separate the metal fittings on the cleaned porcelain insulator from the internal ceramic parts, and clean up the cement adhesive attached to the metal fittings and internal ceramic parts; step 3, crushing and grinding: the separated ceramics The parts are crushed by an external force and then ground to become ceramic powder; wherein, the process of separating the parts described in step 2 is completed with the cooperation of a porcelain bottle insulator recovery and reuse treatment device. The invention can fully clean the cement glue on the ceramic part when recycling the porcelain insulator, and can separate the metal part from the ceramic part without affecting the shape of the metal part.
Description
technical field [0001] The invention belongs to the technical field of electric power equipment, and in particular relates to a method for recycling and reusing porcelain bottle insulators. Background technique [0002] Insulators are used to support the insulators of wires, and insulators made of ceramics are called porcelain bottle insulators. The insulator bears the vertical load and the horizontal tension of the wire during operation; the insulator is also subjected to the sun, rain, climate change and corrosion of chemical substances. Therefore, the insulator has both good electrical properties and sufficient mechanical strength. Porcelain bottle insulators that have reached the end of their service life need to be recycled and reused. The current recycling and reuse method for porcelain bottle insulators is to directly crush the porcelain bottle insulators after cleaning, then crush and grind the porcelain bottle insulators, and finally recycle the ceramic powder. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): H01B15/00H01B19/00
CPCH01B15/008H01B19/00Y02W30/82
Inventor 潘春燕龚定军
Owner 万泰智能电子科技(新沂)有限公司