Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of microwave dielectric ceramic material and dielectric ceramic block

A technology of microwave dielectric ceramics and raw materials, applied in the field of communication, can solve the problems of heavy weight, limited performance of microwave devices, large size of metal resonators, etc.

Inactive Publication Date: 2020-07-07
ANHUI TATFOOK TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional metal resonators are bulky and heavy, limiting the performance of microwave devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of microwave dielectric ceramic material and dielectric ceramic block
  • Preparation method of microwave dielectric ceramic material and dielectric ceramic block
  • Preparation method of microwave dielectric ceramic material and dielectric ceramic block

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The following will clearly and completely describe the technical solutions in the embodiments of the present application with reference to the accompanying drawings in the embodiments of the present application. Obviously, the described embodiments are only part of the embodiments of the present application, not all of them. Based on the embodiments in this application, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the scope of protection of this application.

[0012] One aspect of the present application provides a microwave dielectric ceramic material. The microwave dielectric ceramic material includes zinc oxide, silicon dioxide and magnesium oxide. That is, the microwave dielectric ceramic material is mainly composed of the above-mentioned components, and it can be understood that the microwave dielectric ceramic may also contain a small or trace amount of other substances.

[0013] In some embodime...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a microwave dielectric ceramic material and a dielectric ceramic block. The method for preparing the microwave dielectric ceramic comprises the following steps of: providing raw materials corresponding to zinc oxide, silicon dioxide and magnesium oxide; adding an organic solvent and grinding balls, and carrying out primary ball milling; drying the slurry obtained by the primary ball milling, and calcining to obtain a ceramic body; crushing the ceramic body, adding an organic solvent and grinding balls, and carrying out secondary ball milling; drying the slurry obtained by the secondary ball milling; mixing the obtained powder with a binder to form slurry, and granulating; carrying out dry pressing molding in a mold; and removing the binder and sintering again. The microwave dielectric ceramic prepared by the method is mainly composed of zinc oxide, silicon dioxide and magnesium oxide, and has the advantages of low dielectric constant, lowloss and near-zero temperature coefficient. Therefore, the microwave dielectric ceramic material provided by the invention has improved microwave dielectric properties.

Description

technical field [0001] The present application relates to the field of communication technology, in particular to a method for manufacturing a microwave dielectric ceramic material and a dielectric ceramic block for 5G communication technology. Background technique [0002] The rapid development of microwave communication technology (such as 5G communication technology) puts forward higher requirements on the performance of microwave devices. Traditional metal resonators are bulky and heavy, which limits the performance of microwave devices. Microwave dielectric ceramics usually need to have a high dielectric constant, which can be made into various microwave devices to meet the requirements of miniaturization and low loss of filter units. [0003] The present application proposes a novel method for preparing a microwave dielectric ceramic material, and the microwave dielectric ceramic material prepared according to the method has improved microwave dielectric properties. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/453C04B35/14C04B35/626
CPCC04B35/14C04B35/453C04B35/62615C04B2235/3206C04B2235/3267C04B2235/3275C04B2235/3279C04B2235/442
Inventor 袁亮亮陆正武陈薛爱
Owner ANHUI TATFOOK TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com