Modified polyguanidine salt antibacterial and mildew-proof agent, preparation method thereof and application thereof in silicone structural sealant
An antibacterial and antifungal agent and sealant technology, which is applied in the direction of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of mold and mildew prevention time, etc., and achieve good precipitation resistance, low cost, and simple preparation process Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1
[0024] A preparation method of a modified polyguanidine salt antibacterial and antifungal agent includes the following steps:
[0025] (1) Dissolve 20 g of benzyl bromide in 20 mL of absolute ethanol and stir to obtain about 34 mL of solution A; dissolve polyhexamethylene monoguanidine phosphate in water and stir evenly to obtain polyhexamethylene mono Solution B with 20% guanidine phosphate mass fraction;
[0026] (2) Under the conditions of controlling the temperature of solution B at 50°C and controlling the stirring speed at 300 rpm, 34mL of solution A was added dropwise to 100mL of solution B within 30 minutes to produce solid insolubles;
[0027] (3) The solid insoluble matter is separated and dried in vacuum at 60° C. to obtain a modified polyguanidine salt antibacterial and antifungal agent with pendant benzene ring groups.
[0028] Applying the modified polyguanidine salt antibacterial and antifungal agent prepared in this embodiment to a silicone structural...
Example Embodiment
[0031] Example 2
[0032] A preparation method of a modified polyguanidine salt antibacterial and antifungal agent includes the following steps:
[0033] (1) Dissolve 20 g of benzyl chloride in 40 mL of absolute ethanol and stir to obtain about 58.2 mL of solution A; dissolve polyhexamethylene monoguanidine hydrochloride in water and stir to obtain polyhexamethylene Solution B with a 50% mass fraction of monoguanidine hydrochloride;
[0034] (2) Under the conditions of controlling the temperature of solution B at 80°C and controlling the stirring speed at 350 rpm, 58.2 mL of solution A was added dropwise to 250 mL of solution B within 30 minutes to produce solid insolubles;
[0035] (3) The solid insoluble matter is separated and dried in vacuum at 60° C. to obtain a modified polyguanidine salt antibacterial and antifungal agent with pendant benzene ring groups.
[0036] Applying the modified polyguanidine salt antibacterial and antifungal agent prepared in this embodiment to a silicon...
Example Embodiment
[0039] Example 3
[0040] A preparation method of a modified polyguanidine salt antibacterial and antifungal agent includes the following steps:
[0041] (1) Dissolve 30g of benzyl bromide in 20mL of absolute ethanol and stir well to obtain about 40.8mL of solution A; dissolve polyhexamethylene monoguanidine hydrochloride in water and stir well to obtain polyhexamethylene Solution B with 20% mass fraction of monoguanidine hydrochloride;
[0042] (2) Under the conditions of controlling the temperature of solution B at 80°C and controlling the stirring speed at 500 rpm, 40.8 mL of solution A was added dropwise to 100 mL of solution B within 60 minutes to produce solid insolubles;
[0043] (3) The solid insoluble matter is separated and dried in vacuum at 60° C. to obtain a modified polyguanidine salt antibacterial and antifungal agent with pendant benzene ring groups.
[0044] Applying the modified polyguanidine salt antibacterial and antifungal agent prepared in this embodiment to a sil...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap