Slow-rebounding coconut fiber mattress and production process thereof

A production process, the technology of elastic coconut palm, applied in the field of slow rebound coconut palm mattress and its production process, can solve the problems of poor support, bad growth, easy moisture absorption mattress bacteria, etc., to achieve good protection, support powerful effect

Inactive Publication Date: 2020-09-04
苏州椰为媒纤维制品科技有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The common slow-rebound mattresses currently on the market generally use polyurethane sponge materials as mattress materials. However, although sponge materials have good rebound effects, their support strength is poor, and the mattress is easy to absorb moisture after molding and cause damage to the inside of the mattress. Bacteria

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A slow-rebound coconut palm mattress, said slow-rebound coconut palm mattress consists of the following components in parts by mass:

[0023] 30 parts of coconut shell fiber, 30 parts of three-dimensional hollow polyester fiber, 10 parts of low melting point polyester fiber.

[0024] Wherein the three-dimensional hollow polyester fiber is composed of three-dimensional hollow polyester fibers of two specifications, one is a three-dimensional hollow polyester long fiber, and the other is a three-dimensional hollow polyester short fiber, and the length of the three-dimensional hollow polyester long fiber is 5 ~10cm, denier is 20~30 denier, the length of the three-dimensional hollow polyester staple fiber is 2~5cm, denier is 10~15 denier. The ratio between the three-dimensional hollow polyester long fibers and the three-dimensional hollow polyester short fibers is 3:1. The length of the coconut palm fiber is 5-10cm, and the length of the low-melting polyester fiber is 5-10...

Embodiment 2

[0026] A slow-rebound coconut palm mattress, said slow-rebound coconut palm mattress consists of the following components in parts by mass:

[0027] 50 parts of coconut shell fiber, 40 parts of three-dimensional hollow polyester fiber, 20 parts of low melting point polyester fiber.

[0028] Wherein the three-dimensional hollow polyester fiber is composed of three-dimensional hollow polyester fibers of two specifications, one is a three-dimensional hollow polyester long fiber, and the other is a three-dimensional hollow polyester short fiber, and the length of the three-dimensional hollow polyester long fiber is 5 ~10cm, denier is 20~30 denier, the length of the three-dimensional hollow polyester staple fiber is 2~5cm, denier is 10~15 denier. The ratio between the three-dimensional hollow polyester long fibers and the three-dimensional hollow polyester short fibers is 2:1. The length of the coconut palm fiber is 5-10cm, and the length of the low-melting polyester fiber is 5-10...

Embodiment 3

[0030] A slow-rebound coconut palm mattress, said slow-rebound coconut palm mattress consists of the following components in parts by mass:

[0031] 40 parts of coconut shell fiber, 40 parts of three-dimensional hollow polyester fiber, 15 parts of low melting point polyester fiber.

[0032] Wherein the three-dimensional hollow polyester fiber is composed of three-dimensional hollow polyester fibers of two specifications, one is a three-dimensional hollow polyester long fiber, and the other is a three-dimensional hollow polyester short fiber, and the length of the three-dimensional hollow polyester long fiber is 5 ~10cm, denier is 20~30 denier, the length of the three-dimensional hollow polyester staple fiber is 2~5cm, denier is 10~15 denier. The ratio between the three-dimensional hollow polyester long fibers and the three-dimensional hollow polyester short fibers is 3:1. The length of the coconut palm fiber is 5-10cm, and the length of the low-melting polyester fiber is 5-10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a slow-rebounding coconut fiber mattress. The slow-rebounding coconut fiber mattress is prepared from following components by mass: 30-50 parts of coconut fibers, 20-40 parts of three-dimensional hollow polyester fibers and 10-20 parts of low-melting-point polyester fibers. After the raw materials are mixed, opened, webbed, needled, baked, cooled and shaped and the like, the finished slow-rebounding coconut fiber mattress is manufactured. In this way, the slow-rebounding coconut fiber mattress has the beneficial effects of a common slow-rebounding mattress and a coconutfiber mattress, and is refreshing, transparent and free of moisture absorption while achieving a good protection effect on vertebrae of the human body, and bacterium breeding is not easily caused.

Description

technical field [0001] The invention relates to the field of coconut palm products, in particular to a slow-rebound coconut palm mattress and a production process thereof. Background technique [0002] The slow-rebound mattress can provide comfortable support and hardness while being able to sense and remember the curve of the human body when in use. It can be perfectly shaped according to the ups and downs of the human body, and protects the natural bending of the neck, waist and legs. All parts of the human body are in a stress-free state, promoting blood circulation and relieving physical fatigue. Due to the above-mentioned various advantages, slow rebound mattresses, as a kind of high-end mattresses, have developed faster and faster in recent years. The common slow-rebound mattresses currently on the market generally use polyurethane sponge materials as mattress materials. However, although sponge materials have good rebound effects, their support strength is poor, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/485D04H1/4391D04H1/541D04H1/55D04H1/4258A47C27/12
CPCA47C27/122D04H1/4258D04H1/4391D04H1/485D04H1/541D04H1/55
Inventor 张光林
Owner 苏州椰为媒纤维制品科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com